Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.73 g/cm³ Show Material materials with Densidad of 2.73 g/cm³ | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
2.73 g/cm³ Show Material materials with Densidad of 2.73 g/cm³ | H14 | ||
2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | H14 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 MPa | H14 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Dureza Brinell | 40.0 [-] Show Material materials with Dureza Brinell of 40.0 [-] | H14 | AA Standards | ||
40.0 [-] Show Material materials with Dureza Brinell of 40.0 [-] | H14 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 30 % Show Material materials with Elongación of 30 % | H14 | Elongation in 50 mm | |
-80 °C | 18 % Show Material materials with Elongación of 18 % | H14 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongación of 1.0 % | H14 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Elongación of 2.0 % | H14 | AA Standards, ASTM B209 | A50 | ||
3.0 % Show Material materials with Elongación of 3.0 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B234, ASTM B313 | A50 | ||
3.0 % Show Material materials with Elongación of 3.0 % | H14 | AA Standards, ASTM B234 | A100 | ||
4.0 % Show Material materials with Elongación of 4.0 % | H14 | AA Standards, ASTM B210 | A50 | ||
4.0 % Show Material materials with Elongación of 4.0 % | H14 | AA Standards, ASTM B234 | A100 | ||
5.0 % Show Material materials with Elongación of 5.0 % | H14 | AA Standards, ASTM B209, ASTM B234, ASTM B313, ASTM B547 | A50 | ||
7.0 % Show Material materials with Elongación of 7.0 % | H14 | AA Standards, ASTM B209 | A100 | ||
7.5 % Show Material materials with Elongación of 7.5 % | H14 | ||||
8.0 % Show Material materials with Elongación of 8.0 % | H14 | AA Standards, ASTM B209, ASTM B234, ASTM B547 | A50 | ||
14.0 % Show Material materials with Elongación of 14.0 % | H14 | AA Standards | A100 | ||
0 °C | 16 % Show Material materials with Elongación of 16 % | H14 | Elongation in 50 mm | ||
24 °C | 16 % Show Material materials with Elongación of 16 % | H14 | Elongation in 50 mm | ||
100 °C | 16 % Show Material materials with Elongación of 16 % | H14 | Elongation in 50 mm | ||
150 °C | 16 % Show Material materials with Elongación of 16 % | H14 | Elongation in 50 mm | ||
205 °C | 20 % Show Material materials with Elongación of 20 % | H14 | Elongation in 50 mm | ||
260 °C | 60 % Show Material materials with Elongación of 60 % | H14 | Elongation in 50 mm | ||
315 °C | 70 % Show Material materials with Elongación of 70 % | H14 | Elongation in 50 mm | ||
370 °C | 70 % Show Material materials with Elongación of 70 % | H14 | Elongation in 50 mm | ||
Límite elástico | -200 °C | 170 MPa Show Material materials with Límite elástico of 170 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 155 MPa Show Material materials with Límite elástico of 155 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 145 MPa Show Material materials with Límite elástico of 145 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
115.0 MPa Show Material materials with Límite elástico of 115.0 MPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | RP02 | ||
130.0 MPa Show Material materials with Límite elástico of 130.0 MPa | H14 | ||||
145.0 MPa Show Material materials with Límite elástico of 145.0 MPa | H14 | AA Standards | RP02 | ||
25 °C | 145 MPa Show Material materials with Límite elástico of 145 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 130 MPa Show Material materials with Límite elástico of 130 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 17 MPa Show Material materials with Límite elástico of 17 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 12 MPa Show Material materials with Límite elástico of 12 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 GPa | H14 | |||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
69 GPa Show Material materials with Módulo elástico of 69 GPa | H14 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Resistencia a la fatiga | 62 MPa Show Material materials with Resistencia a la fatiga of 62 MPa | H14 | for 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 240 MPa Show Material materials with Resistencia a la tracción of 240 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 165 MPa Show Material materials with Resistencia a la tracción of 165 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
140.0 - 180.0 MPa Show Material materials with Resistencia a la tracción of 140.0 - 180.0 MPa | H14 | AA Standards, ASTM B209, ASTM B313, ASTM B316, ASTM B547 | |||
140.0 MPa Show Material materials with Resistencia a la tracción of 140.0 MPa | H14 | AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |||
150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa | H14 | AA Standards | |||
0 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
160.0 MPa Show Material materials with Resistencia a la tracción of 160.0 MPa | H14 | ||||
24 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 145 MPa Show Material materials with Resistencia a la tracción of 145 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 125 MPa Show Material materials with Resistencia a la tracción of 125 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 97 MPa Show Material materials with Resistencia a la tracción of 97 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 28 MPa Show Material materials with Resistencia a la tracción of 28 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 19 MPa Show Material materials with Resistencia a la tracción of 19 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 97.0 MPa Show Material materials with Resistencia al cizallamiento of 97.0 MPa | H14 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 890.0 J/(kg·K) Show Material materials with Calor específico of 890.0 J/(kg·K) | H14 | ||
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | H14 | ||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
Conductividad térmica | 159.0 - 193.0 W/(m·K) Show Material materials with Conductividad térmica of 159.0 - 193.0 W/(m·K) | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
180.0 W/(m·K) Show Material materials with Conductividad térmica of 180.0 W/(m·K) | H14 | |||
Temperatura de fusión | 640.0 - 655.0 °C Show Material materials with Temperatura de fusión of 640.0 - 655.0 °C | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
640.0 °C Show Material materials with Temperatura de fusión of 640.0 °C | H14 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 24000000.0 - 29000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 - 29000000.0 S/m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
24000000 S/m Show Material materials with Conductividad eléctrica of 24000000 S/m | H14 | Typical value | ||
Resistividad eléctrica | 3.45e-08 - 4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.45e-08 - 4.17e-08 Ω·m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
4.2e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.2e-08 Ω·m | H14 | Typical value | ||
Specific Electrical conductivity | 41.0 % IACS Show Material materials with Specific Electrical conductivity of 41.0 % IACS | H14 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 96.8 - 99.0 % Show Material materials with Aluminio of 96.8 - 99.0 % | H14 | |
Cobre | 0.05 - 0.2 % Show Material materials with Cobre of 0.05 - 0.2 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
0.7 % Show Material materials with Hierro of 0.7 % | H14 | ||
Manganeso | 1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H14 | |
Silicona | 0.6 % Show Material materials with Silicona of 0.6 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H25) | |
| Workability | general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18) | |