AA Standards Grade 3004 H34

View suppliers (23)

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Suppliers with similar grades

ALUDIUM

FABRICANTE

Information and services

Quantity:

One truck load – Specialty products on request.

Additional services:

Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training

AMS METAL LOGO

PROCESSOR AND DISTRIBUTOR

AA METALS INC.

PROCESSOR AND DISTRIBUTOR

There are 20 other suppliers for this grade.

Preview all suppliers

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Value	Condition	Related Standards
Densidad	2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
	2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³	H34
	2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³	H34

Mecánica

Property	Temperature	Value	Condition	Related Standards	Comment
Bending Fatigue Strength		105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa	H34	AA Standards
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]			Typical for Wrought 3000 Series Aluminium
Dureza Brinell		63.0 [-] Show Material materials with Dureza Brinell of 63.0 [-]	H34	AA Standards
		63.0 [-] Show Material materials with Dureza Brinell of 63.0 [-]	H34		500 kg load, 10 mm ball
Elongación	-195 °C	26 % Show Material materials with Elongación of 26 %	H34		Elongation in 50 mm
	-80 °C	16 % Show Material materials with Elongación of 16 %	H34		Elongation in 50 mm
		1.0 % Show Material materials with Elongación of 1.0 %	H34	AA Standards, ASTM B209	A50
		2.0 % Show Material materials with Elongación of 2.0 %	H34	AA Standards, ASTM B209	A50
		3.0 % Show Material materials with Elongación of 3.0 %	H34	AA Standards, ASTM B209, ASTM B313	A50
		4.0 % Show Material materials with Elongación of 4.0 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547	A50
		4.0 % Show Material materials with Elongación of 4.0 %	H34	AA Standards, ASTM B209	A100
		5.0 % Show Material materials with Elongación of 5.0 %	H34	AA Standards, ASTM B209, ASTM B547	A50
		7.1 % Show Material materials with Elongación of 7.1 %	H34
		9.0 % Show Material materials with Elongación of 9.0 %	H34	AA Standards	A50
		10.0 % Show Material materials with Elongación of 10.0 %	H34	AA Standards	A100
	0 °C	13 % Show Material materials with Elongación of 13 %	H34		Elongation in 50 mm
	24 °C	12 % Show Material materials with Elongación of 12 %	H34		Elongation in 50 mm
	100 °C	13 % Show Material materials with Elongación of 13 %	H34		Elongation in 50 mm
	150 °C	22 % Show Material materials with Elongación of 22 %	H34		Elongation in 50 mm
	205 °C	35 % Show Material materials with Elongación of 35 %	H34		Elongation in 50 mm
	260 °C	55 % Show Material materials with Elongación of 55 %	H34		Elongation in 50 mm
	315 °C	80 % Show Material materials with Elongación of 80 %	H34		Elongation in 50 mm
	370 °C	90 % Show Material materials with Elongación of 90 %	H34		Elongation in 50 mm
Límite elástico	-200 °C	235 MPa Show Material materials with Límite elástico of 235 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	-100 °C	212 MPa Show Material materials with Límite elástico of 212 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	-30 °C	200 MPa Show Material materials with Límite elástico of 200 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
		170.0 MPa Show Material materials with Límite elástico of 170.0 MPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547	RP02
		200.0 MPa Show Material materials with Límite elástico of 200.0 MPa	H34	AA Standards	RP02
		200.0 MPa Show Material materials with Límite elástico of 200.0 MPa	H34
	25 °C	200 MPa Show Material materials with Límite elástico of 200 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	100 °C	200 MPa Show Material materials with Límite elástico of 200 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	200 °C	105 MPa Show Material materials with Límite elástico of 105 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	300 °C	34 MPa Show Material materials with Límite elástico of 34 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	400 °C	19 MPa Show Material materials with Límite elástico of 19 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
Módulo de cizallamiento		25.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 GPa	H34
Módulo elástico		69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
		69 GPa Show Material materials with Módulo elástico of 69 GPa	H34
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m			Typical for Wrought 3000 Series Aluminium
Resistencia a la fatiga		15 MPa Show Material materials with Resistencia a la fatiga of 15 MPa	H34		for 5x10⁸ cycles
Resistencia a la tracción	-195 °C	360 MPa Show Material materials with Resistencia a la tracción of 360 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	-80 °C	262 MPa Show Material materials with Resistencia a la tracción of 262 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
		220.0 - 265.0 MPa Show Material materials with Resistencia a la tracción of 220.0 - 265.0 MPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
		240.0 MPa Show Material materials with Resistencia a la tracción of 240.0 MPa	H34	AA Standards
	0 °C	248 MPa Show Material materials with Resistencia a la tracción of 248 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	24 °C	240 MPa Show Material materials with Resistencia a la tracción of 240 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	100 °C	235 MPa Show Material materials with Resistencia a la tracción of 235 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	150 °C	193 MPa Show Material materials with Resistencia a la tracción of 193 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	205 °C	145 MPa Show Material materials with Resistencia a la tracción of 145 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	260 °C	97 MPa Show Material materials with Resistencia a la tracción of 97 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	315 °C	52 MPa Show Material materials with Resistencia a la tracción of 52 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	370 °C	35 MPa Show Material materials with Resistencia a la tracción of 35 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
Resistencia al cizallamiento		125.0 MPa Show Material materials with Resistencia al cizallamiento of 125.0 MPa	H34

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards
Calor específico		890.0 J/(kg·K) Show Material materials with Calor específico of 890.0 J/(kg·K)	H34
Coeficiente de dilatación térmica		2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K	H34
	20 °C	2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
	100 °C	2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Conductividad térmica		160.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 W/(m·K)	H34
		163 W/(m·K) Show Material materials with Conductividad térmica of 163 W/(m·K)	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Temperatura de fusión		630.0 - 655.0 °C Show Material materials with Temperatura de fusión of 630.0 - 655.0 °C	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
		630.0 °C Show Material materials with Temperatura de fusión of 630.0 °C	H34

Eléctrico

Property	Value	Condition	Related Standards
Conductividad eléctrica	24000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 S/m	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Resistividad eléctrica	4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.17e-08 Ω·m	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547

Chemical properties

Property	Value	Condition	Related Standards
Aluminio	95.6 - 98.2 % Show Material materials with Aluminio of 95.6 - 98.2 %	H34
Cobre	0.25 % Show Material materials with Cobre of 0.25 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Hierro	0.70 % Show Material materials with Hierro of 0.70 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
	0.7 % Show Material materials with Hierro of 0.7 %	H34
Magnesio	0.8 - 1.3 % Show Material materials with Magnesio of 0.8 - 1.3 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Manganeso	1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Otro	0.15 % Show Material materials with Otro of 0.15 %	H34
Silicona	0.3 % Show Material materials with Silicona of 0.3 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Zinc	0.25 % Show Material materials with Zinc of 0.25 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547

Technological properties

Property
Brazing	general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen
Corrosion properties	Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere
General machinability	General: poor (O, H32), sufficient (H34, H36, H38)
Workability	general (condition): good (O), acceptable (H32, H34), poor(H36, H38)

Looking for suppliers of this material? Click to see 23 supplier of AA Standards Grade 3004 H34 on Matmatch