Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³ | H38 | AA Standards, ASTM B209, ASTM B313 |
2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³ | H38 | ||
2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | H38 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | H38 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Dureza Brinell | 77.0 [-] Show Material materials with Dureza Brinell of 77.0 [-] | H38 | AA Standards | ||
77.0 [-] Show Material materials with Dureza Brinell of 77.0 [-] | H38 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 20 % Show Material materials with Elongación of 20 % | H38 | Elongation in 50 mm | |
-80 °C | 10 % Show Material materials with Elongación of 10 % | H38 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongación of 1.0 % | H38 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Elongación of 2.0 % | H38 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
3.8 % Show Material materials with Elongación of 3.8 % | H38 | ||||
4.0 % Show Material materials with Elongación of 4.0 % | H38 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
5.0 % Show Material materials with Elongación of 5.0 % | H38 | AA Standards | A50 | ||
5.0 % Show Material materials with Elongación of 5.0 % | H38 | AA Standards | A100 | ||
0 °C | 7 % Show Material materials with Elongación of 7 % | H38 | Elongation in 50 mm | ||
24 °C | 6 % Show Material materials with Elongación of 6 % | H38 | Elongation in 50 mm | ||
100 °C | 7 % Show Material materials with Elongación of 7 % | H38 | Elongation in 50 mm | ||
150 °C | 15 % Show Material materials with Elongación of 15 % | H38 | Elongation in 50 mm | ||
205 °C | 30 % Show Material materials with Elongación of 30 % | H38 | Elongation in 50 mm | ||
260 °C | 50 % Show Material materials with Elongación of 50 % | H38 | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongación of 80 % | H38 | Elongation in 50 mm | ||
370 °C | 90 % Show Material materials with Elongación of 90 % | H38 | Elongation in 50 mm | ||
Límite elástico | -200 °C | 295 MPa Show Material materials with Límite elástico of 295 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 267 MPa Show Material materials with Límite elástico of 267 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 245 MPa Show Material materials with Límite elástico of 245 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
215.0 MPa Show Material materials with Límite elástico of 215.0 MPa | H38 | AA Standards, ASTM B209, ASTM B313 | RP02 | ||
250.0 MPa Show Material materials with Límite elástico of 250.0 MPa | H38 | AA Standards | RP02 | ||
250.0 MPa Show Material materials with Límite elástico of 250.0 MPa | H38 | ||||
25 °C | 245 MPa Show Material materials with Límite elástico of 245 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 245 MPa Show Material materials with Límite elástico of 245 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 105 MPa Show Material materials with Límite elástico of 105 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 34 MPa Show Material materials with Límite elástico of 34 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 19 MPa Show Material materials with Límite elástico of 19 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 GPa | H38 | |||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H38 | AA Standards, ASTM B209, ASTM B313 | ||
69 GPa Show Material materials with Módulo elástico of 69 GPa | H38 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Resistencia a la fatiga | 16 MPa Show Material materials with Resistencia a la fatiga of 16 MPa | H38 | for 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 400 MPa Show Material materials with Resistencia a la tracción of 400 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 303 MPa Show Material materials with Resistencia a la tracción of 303 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | H38 | AA Standards, ASTM B209, ASTM B313 | |||
285.0 MPa Show Material materials with Resistencia a la tracción of 285.0 MPa | H38 | AA Standards | |||
290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | H38 | ||||
0 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 283 MPa Show Material materials with Resistencia a la tracción of 283 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 275 MPa Show Material materials with Resistencia a la tracción of 275 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 215 MPa Show Material materials with Resistencia a la tracción of 215 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Resistencia a la tracción of 83 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 145.0 MPa Show Material materials with Resistencia al cizallamiento of 145.0 MPa | H38 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 890.0 J/(kg·K) Show Material materials with Calor específico of 890.0 J/(kg·K) | H38 | ||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H38 | ||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B313 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B313 | |
Conductividad térmica | 160.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 W/(m·K) | H38 | ||
163 W/(m·K) Show Material materials with Conductividad térmica of 163 W/(m·K) | H38 | AA Standards, ASTM B209, ASTM B313 | ||
Temperatura de fusión | 630.0 - 655.0 °C Show Material materials with Temperatura de fusión of 630.0 - 655.0 °C | H38 | AA Standards, ASTM B209, ASTM B313 | |
630.0 °C Show Material materials with Temperatura de fusión of 630.0 °C | H38 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 24000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 S/m | H38 | AA Standards, ASTM B209, ASTM B313 |
Resistividad eléctrica | 4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.17e-08 Ω·m | H38 | AA Standards, ASTM B209, ASTM B313 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 95.6 - 98.2 % Show Material materials with Aluminio of 95.6 - 98.2 % | H38 | |
Cobre | 0.25 % Show Material materials with Cobre of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | H38 | AA Standards, ASTM B209, ASTM B313 |
0.7 % Show Material materials with Hierro of 0.7 % | H38 | ||
Magnesio | 0.8 - 1.3 % Show Material materials with Magnesio of 0.8 - 1.3 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Manganeso | 1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H38 | |
Silicona | 0.3 % Show Material materials with Silicona of 0.3 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |