Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³ | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³ | O | ||
2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | O |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | O | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Dureza Brinell | 45.0 [-] Show Material materials with Dureza Brinell of 45.0 [-] | O | AA Standards | ||
45.0 [-] Show Material materials with Dureza Brinell of 45.0 [-] | O | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 38 % Show Material materials with Elongación of 38 % | O | Elongation in 50 mm | |
-80 °C | 30 % Show Material materials with Elongación of 30 % | O | Elongation in 50 mm | ||
9.0 % Show Material materials with Elongación of 9.0 % | O | AA Standards, ASTM B209 | A50 | ||
12.0 % Show Material materials with Elongación of 12.0 % | O | AA Standards, ASTM B209 | A50 | ||
14.0 % Show Material materials with Elongación of 14.0 % | O | AA Standards, ASTM B209 | A100 | ||
15.0 % Show Material materials with Elongación of 15.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
16.0 % Show Material materials with Elongación of 16.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
18.0 % Show Material materials with Elongación of 18.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
18.0 % Show Material materials with Elongación of 18.0 % | O | ||||
20.0 % Show Material materials with Elongación of 20.0 % | O | AA Standards | A50 | ||
22.0 % Show Material materials with Elongación of 22.0 % | O | AA Standards | A100 | ||
0 °C | 26 % Show Material materials with Elongación of 26 % | O | Elongation in 50 mm | ||
24 °C | 25 % Show Material materials with Elongación of 25 % | O | Elongation in 50 mm | ||
100 °C | 25 % Show Material materials with Elongación of 25 % | O | Elongation in 50 mm | ||
150 °C | 35 % Show Material materials with Elongación of 35 % | O | Elongation in 50 mm | ||
205 °C | 55 % Show Material materials with Elongación of 55 % | O | Elongation in 50 mm | ||
260 °C | 70 % Show Material materials with Elongación of 70 % | O | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongación of 80 % | O | Elongation in 50 mm | ||
370 °C | 90 % Show Material materials with Elongación of 90 % | O | Elongation in 50 mm | ||
Límite elástico | -200 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 80 MPa Show Material materials with Límite elástico of 80 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 69 MPa Show Material materials with Límite elástico of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
60.0 MPa Show Material materials with Límite elástico of 60.0 MPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | RP02 | ||
69.0 MPa Show Material materials with Límite elástico of 69.0 MPa | O | ||||
70.0 MPa Show Material materials with Límite elástico of 70.0 MPa | O | AA Standards | RP02 | ||
25 °C | 69 MPa Show Material materials with Límite elástico of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 69 MPa Show Material materials with Límite elástico of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 65 MPa Show Material materials with Límite elástico of 65 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 34 MPa Show Material materials with Límite elástico of 34 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 9 MPa Show Material materials with Límite elástico of 9 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 GPa | O | |||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
69 GPa Show Material materials with Módulo elástico of 69 GPa | O | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Resistencia a la fatiga | 14 MPa Show Material materials with Resistencia a la fatiga of 14 MPa | O | for 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 193 MPa Show Material materials with Resistencia a la tracción of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150.0 - 200.0 MPa Show Material materials with Resistencia a la tracción of 150.0 - 200.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
160.0 - 200.0 MPa Show Material materials with Resistencia a la tracción of 160.0 - 200.0 MPa | O | AA Standards, ASTM B221 | |||
170.0 MPa Show Material materials with Resistencia a la tracción of 170.0 MPa | O | ||||
180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | O | AA Standards | |||
0 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 97 MPa Show Material materials with Resistencia a la tracción of 97 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 70 MPa Show Material materials with Resistencia a la tracción of 70 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 110.0 MPa Show Material materials with Resistencia al cizallamiento of 110.0 MPa | O |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 890.0 J/(kg·K) Show Material materials with Calor específico of 890.0 J/(kg·K) | O | ||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | O | ||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
Conductividad térmica | 160.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 W/(m·K) | O | ||
163 W/(m·K) Show Material materials with Conductividad térmica of 163 W/(m·K) | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
Temperatura de fusión | 630.0 - 655.0 °C Show Material materials with Temperatura de fusión of 630.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
630.0 °C Show Material materials with Temperatura de fusión of 630.0 °C | O |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 24000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 S/m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
24000000 S/m Show Material materials with Conductividad eléctrica of 24000000 S/m | O | Typical/derived value | ||
Resistividad eléctrica | 4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.17e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
Specific Electrical conductivity | 42.0 % IACS Show Material materials with Specific Electrical conductivity of 42.0 % IACS | O | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 95.6 - 98.2 % Show Material materials with Aluminio of 95.6 - 98.2 % | O | |
Cobre | 0.25 % Show Material materials with Cobre of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
0.7 % Show Material materials with Hierro of 0.7 % | O | ||
Magnesio | 0.8 - 1.3 % Show Material materials with Magnesio of 0.8 - 1.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Manganeso | 1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | O | |
Silicona | 0.3 % Show Material materials with Silicona of 0.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |