Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ | H34 | ||
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H34 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | H34 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Dureza Brinell | 68.0 [-] Show Material materials with Dureza Brinell of 68.0 [-] | H34 | AA Standards | ||
68.0 [-] Show Material materials with Dureza Brinell of 68.0 [-] | H34 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 28 % Show Material materials with Elongación of 28 % | H34 | Elongation in 50 mm | |
-80 °C | 21 % Show Material materials with Elongación of 21 % | H34 | Elongation in 50 mm | ||
3.0 % Show Material materials with Elongación of 3.0 % | H34 | AA Standards, ASTM B209 | A50 | ||
4.0 % Show Material materials with Elongación of 4.0 % | H34 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
6.0 % Show Material materials with Elongación of 6.0 % | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
9.0 % Show Material materials with Elongación of 9.0 % | H34 | AA Standards, ASTM B209 | A100 | ||
9.1 % Show Material materials with Elongación of 9.1 % | H34 | ||||
10.0 % Show Material materials with Elongación of 10.0 % | H34 | AA Standards, ASTM B209, ASTM B547 | A50 | ||
12.0 % Show Material materials with Elongación of 12.0 % | H34 | AA Standards | A100 | ||
0 °C | 18 % Show Material materials with Elongación of 18 % | H34 | Elongation in 50 mm | ||
24 °C | 16 % Show Material materials with Elongación of 16 % | H34 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Elongación of 18 % | H34 | Elongation in 50 mm | ||
150 °C | 27 % Show Material materials with Elongación of 27 % | H34 | Elongation in 50 mm | ||
205 °C | 45 % Show Material materials with Elongación of 45 % | H34 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongación of 80 % | H34 | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Elongación of 110 % | H34 | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Elongación of 130 % | H34 | Elongation in 50 mm | ||
Límite elástico | -196 °C | 248 MPa Show Material materials with Límite elástico of 248 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 221 MPa Show Material materials with Límite elástico of 221 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 214 MPa Show Material materials with Límite elástico of 214 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
180.0 MPa Show Material materials with Límite elástico of 180.0 MPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | RP02 | ||
210.0 MPa Show Material materials with Límite elástico of 210.0 MPa | H34 | ||||
215.0 MPa Show Material materials with Límite elástico of 215.0 MPa | H34 | AA Standards | RP02 | ||
24 °C | 214 MPa Show Material materials with Límite elástico of 214 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 214 MPa Show Material materials with Límite elástico of 214 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 186 MPa Show Material materials with Límite elástico of 186 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 103 MPa Show Material materials with Límite elástico of 103 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 52 MPa Show Material materials with Límite elástico of 52 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 38 MPa Show Material materials with Límite elástico of 38 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 21 MPa Show Material materials with Límite elástico of 21 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | H34 | |||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
70 GPa Show Material materials with Módulo elástico of 70 GPa | H34 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Resistencia a la fatiga | 125 MPa Show Material materials with Resistencia a la fatiga of 125 MPa | H34 | for 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 380 MPa Show Material materials with Resistencia a la tracción of 380 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 275 MPa Show Material materials with Resistencia a la tracción of 275 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
235.0 - 285.0 MPa Show Material materials with Resistencia a la tracción of 235.0 - 285.0 MPa | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
235.0 MPa Show Material materials with Resistencia a la tracción of 235.0 MPa | H34 | AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |||
260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | H34 | AA Standards | |||
0 °C | 262 MPa Show Material materials with Resistencia a la tracción of 262 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 262 MPa Show Material materials with Resistencia a la tracción of 262 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 262 MPa Show Material materials with Resistencia a la tracción of 262 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 207 MPa Show Material materials with Resistencia a la tracción of 207 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 165 MPa Show Material materials with Resistencia a la tracción of 165 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Resistencia a la tracción of 83 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 145.0 MPa Show Material materials with Resistencia al cizallamiento of 145.0 MPa | H34 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H34 | |||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H34 | |||
20 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
Conductividad térmica | 138 W/(m·K) Show Material materials with Conductividad térmica of 138 W/(m·K) | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
140.0 W/(m·K) Show Material materials with Conductividad térmica of 140.0 W/(m·K) | H34 | ||||
Temperatura de fusión | 605.0 - 650.0 °C Show Material materials with Temperatura de fusión of 605.0 - 650.0 °C | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
610.0 °C Show Material materials with Temperatura de fusión of 610.0 °C | H34 | ||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 20000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 S/m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Resistividad eléctrica | 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 5e-08 Ω·m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 95.8 - 97.7 % Show Material materials with Aluminio of 95.8 - 97.7 % | H34 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Cromo | 0.15 - 0.35 % Show Material materials with Cromo of 0.15 - 0.35 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
0.4 % Show Material materials with Hierro of 0.4 % | H34 | ||
Magnesio | 2.2 - 2.8 % Show Material materials with Magnesio of 2.2 - 2.8 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H34 | |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |