Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ | H38 | ||
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H38 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 140.0 MPa Show Material materials with Bending Fatigue Strength of 140.0 MPa | H38 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Dureza Brinell | 77.0 [-] Show Material materials with Dureza Brinell of 77.0 [-] | H38 | AA Standards | ||
77.0 [-] Show Material materials with Dureza Brinell of 77.0 [-] | H38 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 25 % Show Material materials with Elongación of 25 % | H38 | Elongation in 50 mm | |
-80 °C | 18 % Show Material materials with Elongación of 18 % | H38 | Elongation in 50 mm | ||
2.0 % Show Material materials with Elongación of 2.0 % | H38 | AA Standards, ASTM B209 | A50 | ||
3.0 % Show Material materials with Elongación of 3.0 % | H38 | AA Standards, ASTM B209 | A50 | ||
4.0 % Show Material materials with Elongación of 4.0 % | H38 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
5.9 % Show Material materials with Elongación of 5.9 % | H38 | ||||
7.0 % Show Material materials with Elongación of 7.0 % | H38 | AA Standards | A50 | ||
7.0 % Show Material materials with Elongación of 7.0 % | H38 | AA Standards | A100 | ||
0 °C | 15 % Show Material materials with Elongación of 15 % | H38 | Elongation in 50 mm | ||
24 °C | 14 % Show Material materials with Elongación of 14 % | H38 | Elongation in 50 mm | ||
100 °C | 16 % Show Material materials with Elongación of 16 % | H38 | Elongation in 50 mm | ||
150 °C | 24 % Show Material materials with Elongación of 24 % | H38 | Elongation in 50 mm | ||
205 °C | 45 % Show Material materials with Elongación of 45 % | H38 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongación of 80 % | H38 | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Elongación of 110 % | H38 | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Elongación of 130 % | H38 | Elongation in 50 mm | ||
Límite elástico | -196 °C | 303 MPa Show Material materials with Límite elástico of 303 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 262 MPa Show Material materials with Límite elástico of 262 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 255 MPa Show Material materials with Límite elástico of 255 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
215.0 MPa Show Material materials with Límite elástico of 215.0 MPa | H38 | AA Standards, ASTM B210, ASTM B483 | RP02 | ||
220.0 MPa Show Material materials with Límite elástico of 220.0 MPa | H38 | AA Standards, ASTM B209, ASTM B313 | RP02 | ||
250.0 MPa Show Material materials with Límite elástico of 250.0 MPa | H38 | ||||
255.0 MPa Show Material materials with Límite elástico of 255.0 MPa | H38 | AA Standards | RP02 | ||
24 °C | 255 MPa Show Material materials with Límite elástico of 255 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 248 MPa Show Material materials with Límite elástico of 248 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 193 MPa Show Material materials with Límite elástico of 193 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | H38 | |||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
70 GPa Show Material materials with Módulo elástico of 70 GPa | H38 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Resistencia a la fatiga | 140 MPa Show Material materials with Resistencia a la fatiga of 140 MPa | H38 | for 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 415 MPa Show Material materials with Resistencia a la tracción of 415 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 303 MPa Show Material materials with Resistencia a la tracción of 303 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
270.0 MPa Show Material materials with Resistencia a la tracción of 270.0 MPa | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |||
290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | H38 | AA Standards | |||
0 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
300.0 MPa Show Material materials with Resistencia a la tracción of 300.0 MPa | H38 | ||||
24 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 275 MPa Show Material materials with Resistencia a la tracción of 275 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 235 MPa Show Material materials with Resistencia a la tracción of 235 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 172 MPa Show Material materials with Resistencia a la tracción of 172 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Resistencia a la tracción of 83 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 165.0 MPa Show Material materials with Resistencia al cizallamiento of 165.0 MPa | H38 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H38 | |||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H38 | |||
20 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
Conductividad térmica | 138 W/(m·K) Show Material materials with Conductividad térmica of 138 W/(m·K) | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
140.0 W/(m·K) Show Material materials with Conductividad térmica of 140.0 W/(m·K) | H38 | ||||
Temperatura de fusión | 605.0 - 650.0 °C Show Material materials with Temperatura de fusión of 605.0 - 650.0 °C | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
610.0 °C Show Material materials with Temperatura de fusión of 610.0 °C | H38 | ||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 20000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 S/m | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
20300000 S/m Show Material materials with Conductividad eléctrica of 20300000 S/m | H38 | Unstated/Typical value | ||
Resistividad eléctrica | 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 5e-08 Ω·m | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
Specific Electrical conductivity | 35.0 % IACS Show Material materials with Specific Electrical conductivity of 35.0 % IACS | H38 | Unstated value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 95.8 - 97.7 % Show Material materials with Aluminio of 95.8 - 97.7 % | H38 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Cromo | 0.15 - 0.35 % Show Material materials with Cromo of 0.15 - 0.35 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
0.4 % Show Material materials with Hierro of 0.4 % | H38 | ||
Magnesio | 2.2 - 2.8 % Show Material materials with Magnesio of 2.2 - 2.8 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H38 | |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |