Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ | O | ||
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | O |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | O | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Dureza Brinell | 47.0 [-] Show Material materials with Dureza Brinell of 47.0 [-] | O | AA Standards | ||
47.0 [-] Show Material materials with Dureza Brinell of 47.0 [-] | O | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 46 % Show Material materials with Elongación of 46 % | O | Elongation in 50 mm | |
-80 °C | 35 % Show Material materials with Elongación of 35 % | O | Elongation in 50 mm | ||
13.0 % Show Material materials with Elongación of 13.0 % | O | AA Standards, ASTM B209 | A50 | ||
15.0 % Show Material materials with Elongación of 15.0 % | O | AA Standards, ASTM B209 | A50 | ||
16.0 % Show Material materials with Elongación of 16.0 % | O | AA Standards, ASTM B209 | A100 | ||
17.0 % Show Material materials with Elongación of 17.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
18.0 % Show Material materials with Elongación of 18.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
19.0 % Show Material materials with Elongación of 19.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
22.0 % Show Material materials with Elongación of 22.0 % | O | AA Standards, ASTM B211 | A100 | ||
23.0 % Show Material materials with Elongación of 23.0 % | O | ||||
25.0 % Show Material materials with Elongación of 25.0 % | O | AA Standards, ASTM B211 | A50 | ||
27.0 % Show Material materials with Elongación of 27.0 % | O | AA Standards | A100 | ||
0 °C | 32 % Show Material materials with Elongación of 32 % | O | Elongation in 50 mm | ||
24 °C | 30 % Show Material materials with Elongación of 30 % | O | Elongation in 50 mm | ||
100 °C | 36 % Show Material materials with Elongación of 36 % | O | Elongation in 50 mm | ||
150 °C | 50 % Show Material materials with Elongación of 50 % | O | Elongation in 50 mm | ||
205 °C | 60 % Show Material materials with Elongación of 60 % | O | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongación of 80 % | O | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Elongación of 110 % | O | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Elongación of 130 % | O | Elongation in 50 mm | ||
Límite elástico | -196 °C | 110 MPa Show Material materials with Límite elástico of 110 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
65.0 MPa Show Material materials with Límite elástico of 65.0 MPa | O | AA Standards, ASTM B209, ASTM B211, ASTM B313, ASTM B547 | RP02 | ||
70.0 MPa Show Material materials with Límite elástico of 70.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B483 | RP02 | ||
80.0 MPa Show Material materials with Límite elástico of 80.0 MPa | O | ||||
90.0 MPa Show Material materials with Límite elástico of 90.0 MPa | O | AA Standards | RP02 | ||
24 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 76 MPa Show Material materials with Límite elástico of 76 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 52 MPa Show Material materials with Límite elástico of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 38 MPa Show Material materials with Límite elástico of 38 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 21 MPa Show Material materials with Límite elástico of 21 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | O | |||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
70 GPa Show Material materials with Módulo elástico of 70 GPa | O | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Resistencia a la fatiga | 110 MPa Show Material materials with Resistencia a la fatiga of 110 MPa | O | for 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 303 MPa Show Material materials with Resistencia a la tracción of 303 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 200 MPa Show Material materials with Resistencia a la tracción of 200 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
170.0 - 215.0 MPa Show Material materials with Resistencia a la tracción of 170.0 - 215.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
170.0 - 240.0 MPa Show Material materials with Resistencia a la tracción of 170.0 - 240.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241 | |||
170.0 - 220.0 MPa Show Material materials with Resistencia a la tracción of 170.0 - 220.0 MPa | O | AA Standards, ASTM B211 | |||
170.0 MPa Show Material materials with Resistencia a la tracción of 170.0 MPa | O | AA Standards, ASTM B483 | |||
190.0 MPa Show Material materials with Resistencia a la tracción of 190.0 MPa | O | ||||
0 °C | 193 MPa Show Material materials with Resistencia a la tracción of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
195.0 MPa Show Material materials with Resistencia a la tracción of 195.0 MPa | O | AA Standards | |||
220.0 MPa Show Material materials with Resistencia a la tracción of 220.0 MPa | O | AA Standards, ASTM B316 | |||
24 °C | 193 MPa Show Material materials with Resistencia a la tracción of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 193 MPa Show Material materials with Resistencia a la tracción of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 160 MPa Show Material materials with Resistencia a la tracción of 160 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 117 MPa Show Material materials with Resistencia a la tracción of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Resistencia a la tracción of 83 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 125.0 MPa Show Material materials with Resistencia al cizallamiento of 125.0 MPa | O |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | O | |||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | O | |||
20 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
Conductividad térmica | 138 W/(m·K) Show Material materials with Conductividad térmica of 138 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
140.0 W/(m·K) Show Material materials with Conductividad térmica of 140.0 W/(m·K) | O | ||||
Temperatura de fusión | 605.0 - 650.0 °C Show Material materials with Temperatura de fusión of 605.0 - 650.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
610.0 °C Show Material materials with Temperatura de fusión of 610.0 °C | O | ||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 20000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
20300000 S/m Show Material materials with Conductividad eléctrica of 20300000 S/m | O | Unstated/Typical value, Typical/derived value | ||
Resistividad eléctrica | 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 5e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
Specific Electrical conductivity | 35.0 % IACS Show Material materials with Specific Electrical conductivity of 35.0 % IACS | O | Unstated value, Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 95.8 - 97.7 % Show Material materials with Aluminio of 95.8 - 97.7 % | O | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Cromo | 0.15 - 0.35 % Show Material materials with Cromo of 0.15 - 0.35 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
0.4 % Show Material materials with Hierro of 0.4 % | O | ||
Magnesio | 2.2 - 2.8 % Show Material materials with Magnesio of 2.2 - 2.8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | O | |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |