Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.64 g/cm³ Show Material materials with Densidad of 2.64 g/cm³ | H18 | AA Standards, ASTM B211 |
2.64 g/cm³ Show Material materials with Densidad of 2.64 g/cm³ | H18 | ||
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H18 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 150.0 MPa Show Material materials with Bending Fatigue Strength of 150.0 MPa | H18 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Dureza Brinell | 105.0 [-] Show Material materials with Dureza Brinell of 105.0 [-] | H18 | AA Standards | ||
105.0 [-] Show Material materials with Dureza Brinell of 105.0 [-] | H18 | 500 kg load, 10 mm ball | |||
Elongación | 9.0 % Show Material materials with Elongación of 9.0 % | H18 | AA Standards | A100 | |
9.7 % Show Material materials with Elongación of 9.7 % | H18 | ||||
24 °C | 15 % Show Material materials with Elongación of 15 % | H18 | Elongation in 50 mm | ||
149 °C | 30 % Show Material materials with Elongación of 30 % | H18 | Elongation in 50 mm | ||
204 °C | 50 % Show Material materials with Elongación of 50 % | H18 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongación of 80 % | H18 | Elongation in 50 mm | ||
316 °C | 100 % Show Material materials with Elongación of 100 % | H18 | Elongation in 50 mm | ||
Límite elástico | 405.0 MPa Show Material materials with Límite elástico of 405.0 MPa | H18 | AA Standards | RP02 | |
410.0 MPa Show Material materials with Límite elástico of 410.0 MPa | H18 | ||||
24 °C | 345 MPa Show Material materials with Límite elástico of 345 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 214 MPa Show Material materials with Límite elástico of 214 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 124 MPa Show Material materials with Límite elástico of 124 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 69 MPa Show Material materials with Límite elástico of 69 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 48 MPa Show Material materials with Límite elástico of 48 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | H18 | |||
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | H18 | AA Standards, ASTM B211 | ||
71 GPa Show Material materials with Módulo elástico of 71 GPa | H18 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Resistencia a la fatiga | 152 MPa Show Material materials with Resistencia a la fatiga of 152 MPa | H18 | for 5x10⁸ cycles | ||
Resistencia a la tracción | 400.0 MPa Show Material materials with Resistencia a la tracción of 400.0 MPa | H18 | AA Standards, ASTM B211 | ||
435.0 MPa Show Material materials with Resistencia a la tracción of 435.0 MPa | H18 | AA Standards | |||
440.0 MPa Show Material materials with Resistencia a la tracción of 440.0 MPa | H18 | ||||
24 °C | 414 MPa Show Material materials with Resistencia a la tracción of 414 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
149 °C | 262 MPa Show Material materials with Resistencia a la tracción of 262 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
204 °C | 179 MPa Show Material materials with Resistencia a la tracción of 179 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
316 °C | 76 MPa Show Material materials with Resistencia a la tracción of 76 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 234.0 MPa Show Material materials with Resistencia al cizallamiento of 234.0 MPa | H18 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 910.0 J/(kg·K) Show Material materials with Calor específico of 910.0 J/(kg·K) | H18 | |||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H18 | |||
20 °C | 2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K | H18 | AA Standards, ASTM B211 | ||
100 °C | 2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K | H18 | AA Standards, ASTM B211 | ||
Conductividad térmica | 109.0 - 117.0 W/(m·K) Show Material materials with Conductividad térmica of 109.0 - 117.0 W/(m·K) | H18 | AA Standards, ASTM B211 | ||
Temperatura de fusión | 565.0 - 640.0 °C Show Material materials with Temperatura de fusión of 565.0 - 640.0 °C | H18 | AA Standards, ASTM B211 | ||
570.0 °C Show Material materials with Temperatura de fusión of 570.0 °C | H18 | ||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 16000000.0 - 17000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 17000000.0 S/m | H18 | AA Standards, ASTM B211 |
Resistividad eléctrica | 5.88e-08 - 6.25e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.88e-08 - 6.25e-08 Ω·m | H18 | AA Standards, ASTM B211 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 93.0 - 95.4 % Show Material materials with Aluminio of 93.0 - 95.4 % | H18 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H18 | AA Standards, ASTM B211 |
Cromo | 0.05 - 0.2 % Show Material materials with Cromo of 0.05 - 0.2 % | H18 | AA Standards, ASTM B211 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H18 | AA Standards, ASTM B211 |
0.4 % Show Material materials with Hierro of 0.4 % | H18 | ||
Magnesio | 4.5 - 5.6 % Show Material materials with Magnesio of 4.5 - 5.6 % | H18 | AA Standards, ASTM B211 |
Manganeso | 0.05 - 0.2 % Show Material materials with Manganeso of 0.05 - 0.2 % | H18 | AA Standards, ASTM B211 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H18 | |
Silicona | 0.3 % Show Material materials with Silicona of 0.3 % | H18 | AA Standards, ASTM B211 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H18 | AA Standards, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392) | |
| General machinability | General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392) | |
| Workability | general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392) | |