Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.64 g/cm³ Show Material materials with Densidad of 2.64 g/cm³ | H32 | AA Standards, ASTM B211, ASTM B316 |
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H32 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | H32 | AA Standards, ASTM B211, ASTM B316 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Resistencia a la tracción | 300.0 MPa Show Material materials with Resistencia a la tracción of 300.0 MPa | H32 | AA Standards, ASTM B211 | |
300.0 - 360.0 MPa Show Material materials with Resistencia a la tracción of 300.0 - 360.0 MPa | H32 | AA Standards, ASTM B316 | ||
350.0 MPa Show Material materials with Resistencia a la tracción of 350.0 MPa | H32 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 910.0 J/(kg·K) Show Material materials with Calor específico of 910.0 J/(kg·K) | H32 | |||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H32 | |||
20 °C | 2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K | H32 | AA Standards, ASTM B211, ASTM B316 | ||
100 °C | 2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K | H32 | AA Standards, ASTM B211, ASTM B316 | ||
Conductividad térmica | 109.0 - 117.0 W/(m·K) Show Material materials with Conductividad térmica of 109.0 - 117.0 W/(m·K) | H32 | AA Standards, ASTM B211, ASTM B316 | ||
Temperatura de fusión | 565.0 - 640.0 °C Show Material materials with Temperatura de fusión of 565.0 - 640.0 °C | H32 | AA Standards, ASTM B211, ASTM B316 | ||
570.0 °C Show Material materials with Temperatura de fusión of 570.0 °C | H32 | ||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 16000000.0 - 17000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 17000000.0 S/m | H32 | AA Standards, ASTM B211, ASTM B316 |
Resistividad eléctrica | 5.88e-08 - 6.25e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.88e-08 - 6.25e-08 Ω·m | H32 | AA Standards, ASTM B211, ASTM B316 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 93.0 - 95.4 % Show Material materials with Aluminio of 93.0 - 95.4 % | H32 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Cromo | 0.05 - 0.2 % Show Material materials with Cromo of 0.05 - 0.2 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H32 | AA Standards, ASTM B211, ASTM B316 |
0.4 % Show Material materials with Hierro of 0.4 % | H32 | ||
Magnesio | 4.5 - 5.6 % Show Material materials with Magnesio of 4.5 - 5.6 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Manganeso | 0.05 - 0.2 % Show Material materials with Manganeso of 0.05 - 0.2 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H32 | |
Silicona | 0.3 % Show Material materials with Silicona of 0.3 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392) | |
| General machinability | General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392) | |
| Workability | general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392) | |