Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.64 g/cm³ Show Material materials with Densidad of 2.64 g/cm³ | O | AA Standards, ASTM B211, ASTM B316 |
2.64 g/cm³ Show Material materials with Densidad of 2.64 g/cm³ | O | ||
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | O |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 140.0 MPa Show Material materials with Bending Fatigue Strength of 140.0 MPa | O | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Dureza Brinell | 65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-] | O | AA Standards | ||
65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-] | O | 500 kg load, 10 mm ball | |||
Elongación | 18.0 % Show Material materials with Elongación of 18.0 % | O | AA Standards, ASTM B211 | A100 | |
20.0 % Show Material materials with Elongación of 20.0 % | O | AA Standards, ASTM B211 | A50 | ||
31.0 % Show Material materials with Elongación of 31.0 % | O | ||||
32.0 % Show Material materials with Elongación of 32.0 % | O | AA Standards | A100 | ||
24 °C | 35 % Show Material materials with Elongación of 35 % | O | Elongation in 50 mm | ||
149 °C | 55 % Show Material materials with Elongación of 55 % | O | Elongation in 50 mm | ||
204 °C | 65 % Show Material materials with Elongación of 65 % | O | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongación of 80 % | O | Elongation in 50 mm | ||
316 °C | 100 % Show Material materials with Elongación of 100 % | O | Elongation in 50 mm | ||
371 °C | 130 % Show Material materials with Elongación of 130 % | O | Elongation in 50 mm | ||
Límite elástico | 110.0 MPa Show Material materials with Límite elástico of 110.0 MPa | O | |||
150.0 MPa Show Material materials with Límite elástico of 150.0 MPa | O | AA Standards | RP02 | ||
24 °C | 150 MPa Show Material materials with Límite elástico of 150 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 117 MPa Show Material materials with Límite elástico of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 69 MPa Show Material materials with Límite elástico of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 48 MPa Show Material materials with Límite elástico of 48 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 28 MPa Show Material materials with Límite elástico of 28 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | O | |||
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | O | AA Standards, ASTM B211, ASTM B316 | ||
71 GPa Show Material materials with Módulo elástico of 71 GPa | O | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Resistencia a la fatiga | 138 MPa Show Material materials with Resistencia a la fatiga of 138 MPa | O | for 5x10⁸ cycles | ||
Resistencia a la tracción | 290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | O | AA Standards | ||
320.0 MPa Show Material materials with Resistencia a la tracción of 320.0 MPa | O | AA Standards, ASTM B211, ASTM B316 | |||
24 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
149 °C | 214 MPa Show Material materials with Resistencia a la tracción of 214 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
204 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
316 °C | 76 MPa Show Material materials with Resistencia a la tracción of 76 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
371 °C | 41 MPa Show Material materials with Resistencia a la tracción of 41 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 179.0 MPa Show Material materials with Resistencia al cizallamiento of 179.0 MPa | O |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 910.0 J/(kg·K) Show Material materials with Calor específico of 910.0 J/(kg·K) | O | |||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | O | |||
20 °C | 2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K | O | AA Standards, ASTM B211, ASTM B316 | ||
100 °C | 2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K | O | AA Standards, ASTM B211, ASTM B316 | ||
Conductividad térmica | 109.0 - 117.0 W/(m·K) Show Material materials with Conductividad térmica of 109.0 - 117.0 W/(m·K) | O | AA Standards, ASTM B211, ASTM B316 | ||
120.0 W/(m·K) Show Material materials with Conductividad térmica of 120.0 W/(m·K) | O | ||||
20 °C | 120 W/(m·K) Show Material materials with Conductividad térmica of 120 W/(m·K) | O | unstated value | ||
Temperatura de fusión | 565.0 - 640.0 °C Show Material materials with Temperatura de fusión of 565.0 - 640.0 °C | O | AA Standards, ASTM B211, ASTM B316 | ||
570.0 °C Show Material materials with Temperatura de fusión of 570.0 °C | O | ||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 16000000.0 - 17000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 17000000.0 S/m | O | AA Standards, ASTM B211, ASTM B316 | |
17000000 S/m Show Material materials with Conductividad eléctrica of 17000000 S/m | O | Typical value | ||
Resistividad eléctrica | 5.88e-08 - 6.25e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.88e-08 - 6.25e-08 Ω·m | O | AA Standards, ASTM B211, ASTM B316 | |
5.8999999999999986e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.8999999999999986e-08 Ω·m | O | Typical value | ||
Specific Electrical conductivity | 29.0 % IACS Show Material materials with Specific Electrical conductivity of 29.0 % IACS | O | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 93.0 - 95.4 % Show Material materials with Aluminio of 93.0 - 95.4 % | O | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | O | AA Standards, ASTM B211, ASTM B316 |
Cromo | 0.05 - 0.2 % Show Material materials with Cromo of 0.05 - 0.2 % | O | AA Standards, ASTM B211, ASTM B316 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | O | AA Standards, ASTM B211, ASTM B316 |
0.4 % Show Material materials with Hierro of 0.4 % | O | ||
Magnesio | 4.5 - 5.6 % Show Material materials with Magnesio of 4.5 - 5.6 % | O | AA Standards, ASTM B211, ASTM B316 |
Manganeso | 0.05 - 0.2 % Show Material materials with Manganeso of 0.05 - 0.2 % | O | AA Standards, ASTM B211, ASTM B316 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | O | |
Silicona | 0.3 % Show Material materials with Silicona of 0.3 % | O | AA Standards, ASTM B211, ASTM B316 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | O | AA Standards, ASTM B211, ASTM B316 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392) | |
| General machinability | General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392) | |
| Workability | general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392) | |