Property | Value | Condition |
---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H116 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 160.0 MPa Show Material materials with Bending Fatigue Strength of 160.0 MPa | H116 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Elongación | 13.0 % Show Material materials with Elongación of 13.0 % | H116 | ||
14.0 % Show Material materials with Elongación of 14.0 % | H116 | AA Standards | A100 | |
Límite elástico | 230.0 MPa Show Material materials with Límite elástico of 230.0 MPa | H116 | AA Standards | RP02 |
230.0 MPa Show Material materials with Límite elástico of 230.0 MPa | H116 | |||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | H116 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Resistencia a la tracción | 315.0 MPa Show Material materials with Resistencia a la tracción of 315.0 MPa | H116 | AA Standards | |
330.0 MPa Show Material materials with Resistencia a la tracción of 330.0 MPa | H116 |
Aplicaciones térmicas
Property | Value | Condition | Comment |
---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H116 | |
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H116 | |
Conductividad térmica | 120.0 W/(m·K) Show Material materials with Conductividad térmica of 120.0 W/(m·K) | H116 | |
Temperatura de fusión | 580.0 °C Show Material materials with Temperatura de fusión of 580.0 °C | H116 | |
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
Property | Value | Comment |
---|---|---|
Conductividad eléctrica | 18000000.0 - 31000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Resistividad eléctrica | 3.3e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 92.4 - 95.6 % Show Material materials with Aluminio of 92.4 - 95.6 % | H116 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H116 | AA Standards |
Cromo | 0.05 - 0.25 % Show Material materials with Cromo of 0.05 - 0.25 % | H116 | AA Standards |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H116 | AA Standards |
0.4 % Show Material materials with Hierro of 0.4 % | H116 | ||
Magnesio | 4.0 - 4.9 % Show Material materials with Magnesio of 4.0 - 4.9 % | H116 | AA Standards |
Manganeso | 0.4 - 1.0 % Show Material materials with Manganeso of 0.4 - 1.0 % | H116 | AA Standards |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H116 | |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | H116 | AA Standards |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | H116 | AA Standards |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H116 | AA Standards |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor | |
Workability | general (condition): acceptable (O), poor(H321, H116, H111) |