Propiedades
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Densidad | 2.65 g/cm³ Show Material materials with Densidad of 2.65 g/cm³ | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet |
2.66 g/cm³ Show Material materials with Densidad of 2.66 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
2.66 g/cm³ Show Material materials with Densidad of 2.66 g/cm³ | O | |||
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | O |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Dureza Brinell | 75.0 [-] Show Material materials with Dureza Brinell of 75.0 [-] | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | ||
Elongación | -195 °C | 36 % Show Material materials with Elongación of 36 % | O | Elongation in 50 mm | ||
-80 °C | 30 % Show Material materials with Elongación of 30 % | O | Elongation in 50 mm | |||
10.0 % Show Material materials with Elongación of 10.0 % | O | AA Standards, ASTM B209 | A100 | |||
12.0 % Show Material materials with Elongación of 12.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | A100 | |||
14.0 % Show Material materials with Elongación of 14.0 % | O | AA Standards, ASTM B209 | A100 | |||
14.0 % Show Material materials with Elongación of 14.0 % | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | A50 | |||
16.0 % Show Material materials with Elongación of 16.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | |||
16.0 % Show Material materials with Elongación of 16.0 % | O | |||||
20.0 % Show Material materials with Elongación of 20.0 % | O | AA Standards | A100 | |||
0 °C | 27 % Show Material materials with Elongación of 27 % | O | Elongation in 50 mm | |||
24 °C | 25 % Show Material materials with Elongación of 25 % | O | Elongation in 50 mm | |||
100 °C | 36 % Show Material materials with Elongación of 36 % | O | Elongation in 50 mm | |||
150 °C | 50 % Show Material materials with Elongación of 50 % | O | Elongation in 50 mm | |||
205 °C | 60 % Show Material materials with Elongación of 60 % | O | Elongation in 50 mm | |||
260 °C | 80 % Show Material materials with Elongación of 80 % | O | Elongation in 50 mm | |||
315 °C | 110 % Show Material materials with Elongación of 110 % | O | Elongation in 50 mm | |||
370 °C | 130 % Show Material materials with Elongación of 130 % | O | Elongation in 50 mm | |||
Límite elástico | -195 °C | 165 MPa Show Material materials with Límite elástico of 165 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 145 MPa Show Material materials with Límite elástico of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-30 °C | 145 MPa Show Material materials with Límite elástico of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100.0 MPa Show Material materials with Límite elástico of 100.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
105.0 MPa Show Material materials with Límite elástico of 105.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
110.0 MPa Show Material materials with Límite elástico of 110.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | RP02 | |||
115.0 - 200.0 MPa Show Material materials with Límite elástico of 115.0 - 200.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
115.0 MPa Show Material materials with Límite elástico of 115.0 MPa | O | AA Standards, ASTM B547 | RP02 | |||
125.0 - 200.0 MPa Show Material materials with Límite elástico of 125.0 - 200.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
125.0 MPa Show Material materials with Límite elástico of 125.0 MPa | O | AA Standards, ASTM B547 | RP02 | |||
140.0 MPa Show Material materials with Límite elástico of 140.0 MPa | O | |||||
145.0 MPa Show Material materials with Límite elástico of 145.0 MPa | O | AA Standards | RP02 | |||
25 °C | 145 MPa Show Material materials with Límite elástico of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 145 MPa Show Material materials with Límite elástico of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
150 °C | 130 MPa Show Material materials with Límite elástico of 130 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
205 °C | 115 MPa Show Material materials with Límite elástico of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 75 MPa Show Material materials with Límite elástico of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
315 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
Módulo de cizallamiento | 26.4 GPa Show Material materials with Módulo de cizallamiento of 26.4 GPa | O | ||||
Módulo de compresión | 71.7 MPa Show Material materials with Módulo de compresión of 71.7 MPa | O | ||||
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
71 GPa Show Material materials with Módulo elástico of 71 GPa | O | |||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Resistencia a la fatiga | 160 MPa Show Material materials with Resistencia a la fatiga of 160 MPa | O | for 5x10⁸ cycles | |||
Resistencia a la tracción | -195 °C | 407 MPa Show Material materials with Resistencia a la tracción of 407 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 295 MPa Show Material materials with Resistencia a la tracción of 295 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
125.0 MPa Show Material materials with Resistencia a la tracción of 125.0 MPa | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |||
250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | O | AA Standards, ASTM B209 | ||||
255.0 MPa Show Material materials with Resistencia a la tracción of 255.0 MPa | O | AA Standards, ASTM B209 | ||||
260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | O | AA Standards, ASTM B209 | ||||
270.0 - 345.0 MPa Show Material materials with Resistencia a la tracción of 270.0 - 345.0 MPa | O | AA Standards, ASTM B209, ASTM B547 | ||||
270.0 - 350.0 MPa Show Material materials with Resistencia a la tracción of 270.0 - 350.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | ||||
275.0 - 350.0 MPa Show Material materials with Resistencia a la tracción of 275.0 - 350.0 MPa | O | AA Standards, ASTM B209, ASTM B547 | ||||
290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | O | AA Standards | ||||
0 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
300.0 MPa Show Material materials with Resistencia a la tracción of 300.0 MPa | O | |||||
24 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 275 MPa Show Material materials with Resistencia a la tracción of 275 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 215 MPa Show Material materials with Resistencia a la tracción of 215 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 117 MPa Show Material materials with Resistencia a la tracción of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 75 MPa Show Material materials with Resistencia a la tracción of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
Resistencia al cizallamiento | 172.0 MPa Show Material materials with Resistencia al cizallamiento of 172.0 MPa | O |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | O | ||||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | O | ||||
20 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
100 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
Conductividad térmica | 117.0 W/(m·K) Show Material materials with Conductividad térmica of 117.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
120.0 W/(m·K) Show Material materials with Conductividad térmica of 120.0 W/(m·K) | O | |||||
121.0 W/(m·K) Show Material materials with Conductividad térmica of 121.0 W/(m·K) | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |||
Temperatura de fusión | 570.0 °C Show Material materials with Temperatura de fusión of 570.0 °C | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | ||
580.0 - 640.0 °C Show Material materials with Temperatura de fusión of 580.0 - 640.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||||
580.0 °C Show Material materials with Temperatura de fusión of 580.0 °C | O | |||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Conductividad eléctrica | 17000000.0 S/m Show Material materials with Conductividad eléctrica of 17000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
17000000 S/m Show Material materials with Conductividad eléctrica of 17000000 S/m | O | Typical value | |||
Resistividad eléctrica | 5.8e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.8e-08 Ω·m | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
5.88e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.88e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
6e-08 Ω·m Show Material materials with Resistividad eléctrica of 6e-08 Ω·m | O | Typical value | |||
Specific Electrical conductivity | 29.0 % IACS Show Material materials with Specific Electrical conductivity of 29.0 % IACS | O | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Aluminio | 92.4 - 95.6 % Show Material materials with Aluminio of 92.4 - 95.6 % | O | |||
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | Typical |
Cromo | 0.05 - 0.25 % Show Material materials with Cromo of 0.05 - 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
0.4 % Show Material materials with Hierro of 0.4 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | ||
Magnesio | 4.0 - 4.9 % Show Material materials with Magnesio of 4.0 - 4.9 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Manganeso | 0.4 - 1.0 % Show Material materials with Manganeso of 0.4 - 1.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | Total |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Titanio | 0.05 - 0.25 % Show Material materials with Titanio of 0.05 - 0.25 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
0.15 % Show Material materials with Titanio of 0.15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Ship building, Rail cars, Vehicle bodies, Tip truck bodies, Mine skips and cages, Pressure vessels | |
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor | |
| Soldering general | Poor | |
| Welding | When welding 5083 to itself or another alloy from the same sub-group, the recommended filler metal is 5183. Other suitable fillers are 5356 and 5556. Gas: Average; Arc: Excellent; Resistance: Excellent | |
| Workability | general (condition): acceptable (O), poor(H321, H116, H111) | |