Propiedades
General
| Property | Value | Condition |
|---|---|---|
Densidad | 2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³ | H111 |
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H111 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Dureza Brinell | 70.0 [-] Show Material materials with Dureza Brinell of 70.0 [-] | H111 | AA Standards | |
70.0 [-] Show Material materials with Dureza Brinell of 70.0 [-] | H111 | 500 kg load, 10 mm ball | ||
Elongación | 10.0 % Show Material materials with Elongación of 10.0 % | H111 | AA Standards, ASTM B221, ASTM B241 | A100 |
12.0 % Show Material materials with Elongación of 12.0 % | H111 | AA Standards, ASTM B221, ASTM B241 | A50 | |
14.0 % Show Material materials with Elongación of 14.0 % | H111 | AA Standards | A50 | |
14 % Show Material materials with Elongación of 14 % | H111 | |||
15.0 % Show Material materials with Elongación of 15.0 % | H111 | |||
Límite elástico | 130.0 MPa Show Material materials with Límite elástico of 130.0 MPa | H111 | AA Standards, ASTM B221, ASTM B241 | RP02 |
140.0 MPa Show Material materials with Límite elástico of 140.0 MPa | H111 | |||
180.0 MPa Show Material materials with Límite elástico of 180.0 MPa | H111 | AA Standards | RP02 | |
180 MPa Show Material materials with Límite elástico of 180 MPa | H111 | RP02 | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Módulo de compresión | 71.0 MPa Show Material materials with Módulo de compresión of 71.0 MPa | H111 | ||
Módulo elástico | 70 GPa Show Material materials with Módulo elástico of 70 GPa | H111 | ||
71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | H111 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Resistencia a la tracción | 230.0 MPa Show Material materials with Resistencia a la tracción of 230.0 MPa | H111 | AA Standards, ASTM B221, ASTM B241 | |
250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | H111 | |||
260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | H111 | AA Standards | ||
260 MPa Show Material materials with Resistencia a la tracción of 260 MPa | H111 | |||
Resistencia al cizallamiento | 159.0 MPa Show Material materials with Resistencia al cizallamiento of 159.0 MPa | H111 |
Aplicaciones térmicas
| Property | Value | Condition | Comment |
|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H111 | |
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H111 | |
Conductividad térmica | 130.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 W/(m·K) | H111 | |
Temperatura de fusión | 600.0 °C Show Material materials with Temperatura de fusión of 600.0 °C | H111 | |
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Comment |
|---|---|---|
Conductividad eléctrica | 18000000.0 - 31000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Resistividad eléctrica | 3.3e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 94.5 - 97.1 % Show Material materials with Aluminio of 94.5 - 97.1 % | H111 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H111 | AA Standards, ASTM B221, ASTM B241 |
Cromo | 0.05 - 0.2 % Show Material materials with Cromo of 0.05 - 0.2 % | H111 | AA Standards, ASTM B221, ASTM B241 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H111 | AA Standards, ASTM B221, ASTM B241 |
0.4 % Show Material materials with Hierro of 0.4 % | H111 | ||
Magnesio | 2.4 - 3.0 % Show Material materials with Magnesio of 2.4 - 3.0 % | H111 | AA Standards, ASTM B221, ASTM B241 |
Manganeso | 0.5 - 1.0 % Show Material materials with Manganeso of 0.5 - 1.0 % | H111 | AA Standards, ASTM B221, ASTM B241 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H111 | |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241 |
Titanio | 0.2 % Show Material materials with Titanio of 0.2 % | H111 | AA Standards, ASTM B221, ASTM B241 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H111), sufficient (H34) | |
| Workability | general (condition): good (O), acceptable (H32, H34, H111) | |