Propiedades
General
| Property | Value | Condition |
|---|---|---|
Densidad | 2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³ | H34 |
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H34 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Dureza Brinell | 81.0 [-] Show Material materials with Dureza Brinell of 81.0 [-] | H34 | AA Standards | ||
81.0 [-] Show Material materials with Dureza Brinell of 81.0 [-] | H34 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 30 % Show Material materials with Elongación of 30 % | H34 | Elongation in 50 mm | |
-80 °C | 21 % Show Material materials with Elongación of 21 % | H34 | Elongation in 50 mm | ||
4.0 % Show Material materials with Elongación of 4.0 % | H34 | AA Standards, ASTM B209 | A50 | ||
4.0 % Show Material materials with Elongación of 4.0 % | H34 | AA Standards, ASTM B234 | A100 | ||
5.0 % Show Material materials with Elongación of 5.0 % | H34 | AA Standards, ASTM B209 | A50 | ||
6.0 % Show Material materials with Elongación of 6.0 % | H34 | AA Standards, ASTM B209, ASTM B547 | A50 | ||
6.0 % Show Material materials with Elongación of 6.0 % | H34 | AA Standards, ASTM B234 | A100 | ||
7.3 % Show Material materials with Elongación of 7.3 % | H34 | ||||
9.0 % Show Material materials with Elongación of 9.0 % | H34 | AA Standards, ASTM B209 | A100 | ||
10.0 % Show Material materials with Elongación of 10.0 % | H34 | AA Standards, ASTM B209, ASTM B547 | A50 | ||
0 °C | 18 % Show Material materials with Elongación of 18 % | H34 | Elongation in 50 mm | ||
24 °C | 16 % Show Material materials with Elongación of 16 % | H34 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Elongación of 18 % | H34 | Elongation in 50 mm | ||
150 °C | 32 % Show Material materials with Elongación of 32 % | H34 | Elongation in 50 mm | ||
205 °C | 45 % Show Material materials with Elongación of 45 % | H34 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongación of 80 % | H34 | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Elongación of 110 % | H34 | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Elongación of 130 % | H34 | Elongation in 50 mm | ||
Límite elástico | -196 °C | 285 MPa Show Material materials with Límite elástico of 285 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 250 MPa Show Material materials with Límite elástico of 250 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 240 MPa Show Material materials with Límite elástico of 240 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200.0 MPa Show Material materials with Límite elástico of 200.0 MPa | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 | RP02 | ||
240.0 MPa Show Material materials with Límite elástico of 240.0 MPa | H34 | AA Standards | RP02 | ||
240.0 MPa Show Material materials with Límite elástico of 240.0 MPa | H34 | ||||
24 °C | 240 MPa Show Material materials with Límite elástico of 240 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 235 MPa Show Material materials with Límite elástico of 235 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 195 MPa Show Material materials with Límite elástico of 195 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 130 MPa Show Material materials with Límite elástico of 130 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 75 MPa Show Material materials with Límite elástico of 75 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 29 MPa Show Material materials with Límite elástico of 29 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Módulo de compresión | 71.0 MPa Show Material materials with Módulo de compresión of 71.0 MPa | H34 | |||
Módulo elástico | 70 GPa Show Material materials with Módulo elástico of 70 GPa | H34 | |||
71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | H34 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Resistencia a la tracción | -195 °C | 435 MPa Show Material materials with Resistencia a la tracción of 435 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 317 MPa Show Material materials with Resistencia a la tracción of 317 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
270.0 - 325.0 MPa Show Material materials with Resistencia a la tracción of 270.0 - 325.0 MPa | H34 | AA Standards, ASTM B209, ASTM B547 | |||
270.0 MPa Show Material materials with Resistencia a la tracción of 270.0 MPa | H34 | AA Standards, ASTM B234 | |||
300.0 MPa Show Material materials with Resistencia a la tracción of 300.0 MPa | H34 | ||||
0 °C | 303 MPa Show Material materials with Resistencia a la tracción of 303 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
305.0 MPa Show Material materials with Resistencia a la tracción of 305.0 MPa | H34 | AA Standards | |||
24 °C | 303 MPa Show Material materials with Resistencia a la tracción of 303 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 295 MPa Show Material materials with Resistencia a la tracción of 295 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 235 MPa Show Material materials with Resistencia a la tracción of 235 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 117 MPa Show Material materials with Resistencia a la tracción of 117 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 74 MPa Show Material materials with Resistencia a la tracción of 74 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 179.0 MPa Show Material materials with Resistencia al cizallamiento of 179.0 MPa | H34 |
Aplicaciones térmicas
| Property | Value | Condition | Comment |
|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H34 | |
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H34 | |
Conductividad térmica | 130.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 W/(m·K) | H34 | |
Temperatura de fusión | 600.0 °C Show Material materials with Temperatura de fusión of 600.0 °C | H34 | |
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Comment |
|---|---|---|
Conductividad eléctrica | 18000000.0 - 31000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Resistividad eléctrica | 3.3e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 94.5 - 97.1 % Show Material materials with Aluminio of 94.5 - 97.1 % | H34 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Cromo | 0.05 - 0.2 % Show Material materials with Cromo of 0.05 - 0.2 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
0.4 % Show Material materials with Hierro of 0.4 % | H34 | ||
Magnesio | 2.4 - 3.0 % Show Material materials with Magnesio of 2.4 - 3.0 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Manganeso | 0.5 - 1.0 % Show Material materials with Manganeso of 0.5 - 1.0 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H34 | |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Titanio | 0.2 % Show Material materials with Titanio of 0.2 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H111), sufficient (H34) | |
| Workability | general (condition): good (O), acceptable (H32, H34, H111) | |