Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³ | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³ | O | ||
2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | O |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Dureza Brinell | 62.0 [-] Show Material materials with Dureza Brinell of 62.0 [-] | O | AA Standards | ||
62.0 [-] Show Material materials with Dureza Brinell of 62.0 [-] | O | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 39 % Show Material materials with Elongación of 39 % | O | Elongation in 50 mm | |
-80 °C | 30 % Show Material materials with Elongación of 30 % | O | Elongation in 50 mm | ||
12.0 % Show Material materials with Elongación of 12.0 % | O | AA Standards, ASTM B209 | A50 | ||
12.0 % Show Material materials with Elongación of 12.0 % | O | AA Standards, ASTM B221, ASTM B241 | A100 | ||
13.0 % Show Material materials with Elongación of 13.0 % | O | AA Standards, ASTM B209 | A50 | ||
14.0 % Show Material materials with Elongación of 14.0 % | O | AA Standards, ASTM B221, ASTM B241 | A50 | ||
16.0 % Show Material materials with Elongación of 16.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
16.0 % Show Material materials with Elongación of 16.0 % | O | AA Standards, ASTM B209 | A100 | ||
18.0 % Show Material materials with Elongación of 18.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
18.0 % Show Material materials with Elongación of 18.0 % | O | ||||
22.0 % Show Material materials with Elongación of 22.0 % | O | AA Standards | A50 | ||
0 °C | 27 % Show Material materials with Elongación of 27 % | O | Elongation in 50 mm | ||
24 °C | 25 % Show Material materials with Elongación of 25 % | O | Elongation in 50 mm | ||
100 °C | 31 % Show Material materials with Elongación of 31 % | O | Elongation in 50 mm | ||
150 °C | 50 % Show Material materials with Elongación of 50 % | O | Elongation in 50 mm | ||
205 °C | 60 % Show Material materials with Elongación of 60 % | O | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongación of 80 % | O | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Elongación of 110 % | O | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Elongación of 130 % | O | Elongation in 50 mm | ||
Límite elástico | -196 °C | 130 MPa Show Material materials with Límite elástico of 130 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 115 MPa Show Material materials with Límite elástico of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 115 MPa Show Material materials with Límite elástico of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
85.0 MPa Show Material materials with Límite elástico of 85.0 MPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | RP02 | ||
100.0 MPa Show Material materials with Límite elástico of 100.0 MPa | O | ||||
115.0 MPa Show Material materials with Límite elástico of 115.0 MPa | O | AA Standards | RP02 | ||
24 °C | 115 MPa Show Material materials with Límite elástico of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 115 MPa Show Material materials with Límite elástico of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 110 MPa Show Material materials with Límite elástico of 110 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 105 MPa Show Material materials with Límite elástico of 105 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 75 MPa Show Material materials with Límite elástico of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 29 MPa Show Material materials with Límite elástico of 29 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Módulo de compresión | 71.0 MPa Show Material materials with Módulo de compresión of 71.0 MPa | O | |||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
70 GPa Show Material materials with Módulo elástico of 70 GPa | O | ||||
71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | O | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Resistencia a la tracción | -195 °C | 372 MPa Show Material materials with Resistencia a la tracción of 372 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 255 MPa Show Material materials with Resistencia a la tracción of 255 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
215.0 - 285.0 MPa Show Material materials with Resistencia a la tracción of 215.0 - 285.0 MPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |||
240.0 MPa Show Material materials with Resistencia a la tracción of 240.0 MPa | O | ||||
0 °C | 248 MPa Show Material materials with Resistencia a la tracción of 248 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | O | AA Standards | |||
24 °C | 248 MPa Show Material materials with Resistencia a la tracción of 248 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 248 MPa Show Material materials with Resistencia a la tracción of 248 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 200 MPa Show Material materials with Resistencia a la tracción of 200 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 117 MPa Show Material materials with Resistencia a la tracción of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 75 MPa Show Material materials with Resistencia a la tracción of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 159.0 MPa Show Material materials with Resistencia al cizallamiento of 159.0 MPa | O |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | O | |||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | O | |||
20 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
100 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
Conductividad térmica | 130.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 W/(m·K) | O | |||
134 W/(m·K) Show Material materials with Conductividad térmica of 134 W/(m·K) | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |||
Temperatura de fusión | 600.0 - 645.0 °C Show Material materials with Temperatura de fusión of 600.0 - 645.0 °C | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
600.0 °C Show Material materials with Temperatura de fusión of 600.0 °C | O | ||||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 20000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 S/m | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Resistividad eléctrica | 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 5e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 94.5 - 97.1 % Show Material materials with Aluminio of 94.5 - 97.1 % | O | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Cromo | 0.05 - 0.2 % Show Material materials with Cromo of 0.05 - 0.2 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
0.4 % Show Material materials with Hierro of 0.4 % | O | ||
Magnesio | 2.4 - 3.0 % Show Material materials with Magnesio of 2.4 - 3.0 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Manganeso | 0.5 - 1.0 % Show Material materials with Manganeso of 0.5 - 1.0 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | O | |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Titanio | 0.2 % Show Material materials with Titanio of 0.2 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H111), sufficient (H34) | |
| Workability | general (condition): good (O), acceptable (H32, H34, H111) | |