Propiedades
General
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | T651 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Dureza Brinell | 95.0 [-] Show Material materials with Dureza Brinell of 95.0 [-] | T651 | AA Standards | ||
95.0 [-] Show Material materials with Dureza Brinell of 95.0 [-] | T651 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 22 % Show Material materials with Elongación of 22 % | T651 | Elongation in 50 mm | |
-80 °C | 18 % Show Material materials with Elongación of 18 % | T651 | Elongation in 50 mm | ||
5.0 % Show Material materials with Elongación of 5.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Elongación of 7.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
8.0 % Show Material materials with Elongación of 8.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
9.0 % Show Material materials with Elongación of 9.0 % | T651 | AA Standards, ASTM B211 | A100 | ||
10.0 % Show Material materials with Elongación of 10.0 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | A50 | ||
11.0 % Show Material materials with Elongación of 11.0 % | T651 | ||||
12.0 % Show Material materials with Elongación of 12.0 % | T651 | AA Standards | A50 | ||
15.0 % Show Material materials with Elongación of 15.0 % | T651 | AA Standards | A100 | ||
0 °C | 17 % Show Material materials with Elongación of 17 % | T651 | Elongation in 50 mm | ||
24 °C | 17 % Show Material materials with Elongación of 17 % | T651 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Elongación of 18 % | T651 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Elongación of 20 % | T651 | Elongation in 50 mm | ||
205 °C | 28 % Show Material materials with Elongación of 28 % | T651 | Elongation in 50 mm | ||
260 °C | 60 % Show Material materials with Elongación of 60 % | T651 | Elongation in 50 mm | ||
315 °C | 85 % Show Material materials with Elongación of 85 % | T651 | Elongation in 50 mm | ||
370 °C | 95 % Show Material materials with Elongación of 95 % | T651 | Elongation in 50 mm | ||
Límite elástico | -196 °C | 324 MPa Show Material materials with Límite elástico of 324 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 290 MPa Show Material materials with Límite elástico of 290 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 283 MPa Show Material materials with Límite elástico of 283 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
240.0 MPa Show Material materials with Límite elástico of 240.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | RP02 | ||
270.0 MPa Show Material materials with Límite elástico of 270.0 MPa | T651 | ||||
275.0 MPa Show Material materials with Límite elástico of 275.0 MPa | T651 | AA Standards | RP02 | ||
24 °C | 276 MPa Show Material materials with Límite elástico of 276 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 262 MPa Show Material materials with Límite elástico of 262 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 214 MPa Show Material materials with Límite elástico of 214 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 103 MPa Show Material materials with Límite elástico of 103 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 34 MPa Show Material materials with Límite elástico of 34 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 19 MPa Show Material materials with Límite elástico of 19 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 12 MPa Show Material materials with Límite elástico of 12 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Módulo de compresión | 69.7 MPa Show Material materials with Módulo de compresión of 69.7 MPa | T651 | |||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | ||
Plane-Strain Fracture Toughnes | -196 °C | 41.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 41.6 MPa·√m | T651 | For plate in T-L direction | |
24 °C | 29.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 29.1 MPa·√m | T651 | For plate in T-L direction | ||
Resistencia a la tracción | -195 °C | 415 MPa Show Material materials with Resistencia a la tracción of 415 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 338 MPa Show Material materials with Resistencia a la tracción of 338 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa | T651 | AA Standards, ASTM B209 | |||
290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |||
310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T651 | AA Standards | |||
320.0 MPa Show Material materials with Resistencia a la tracción of 320.0 MPa | T651 | ||||
0 °C | 325 MPa Show Material materials with Resistencia a la tracción of 325 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 310 MPa Show Material materials with Resistencia a la tracción of 310 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 290 MPa Show Material materials with Resistencia a la tracción of 290 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 235 MPa Show Material materials with Resistencia a la tracción of 235 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 130 MPa Show Material materials with Resistencia a la tracción of 130 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 32 MPa Show Material materials with Resistencia a la tracción of 32 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 21 MPa Show Material materials with Resistencia a la tracción of 21 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 207.0 MPa Show Material materials with Resistencia al cizallamiento of 207.0 MPa | T651 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | T651 | ||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | T651 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
100 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
Conductividad térmica | 155.0 - 180.0 W/(m·K) Show Material materials with Conductividad térmica of 155.0 - 180.0 W/(m·K) | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
170.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 W/(m·K) | T651 | |||
Temperatura de fusión | 580.0 - 650.0 °C Show Material materials with Temperatura de fusión of 580.0 - 650.0 °C | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
580.0 °C Show Material materials with Temperatura de fusión of 580.0 °C | T651 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 23000000.0 - 27000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 27000000.0 S/m | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Resistividad eléctrica | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.7e-08 - 4.35e-08 Ω·m | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 95.9 - 98.6 % Show Material materials with Aluminio of 95.9 - 98.6 % | T651 | |
Cobre | 0.15 - 0.4 % Show Material materials with Cobre of 0.15 - 0.4 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Cromo | 0.04 - 0.35 % Show Material materials with Cromo of 0.04 - 0.35 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
0.7 % Show Material materials with Hierro of 0.7 % | T651 | ||
Magnesio | 0.8 - 1.2 % Show Material materials with Magnesio of 0.8 - 1.2 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Manganeso | 0.15 % Show Material materials with Manganeso of 0.15 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T651 | |
Silicona | 0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
| Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) | |