General
Property | Value | Condition | Related Standards |
---|---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | T89 | AA Standards, ASTM B211 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Elongación | 14.0 % Show Material materials with Elongación of 14.0 % | T89 | ||
Límite elástico | 325.0 MPa Show Material materials with Límite elástico of 325.0 MPa | T89 | AA Standards, ASTM B211 | RP02 |
370.0 MPa Show Material materials with Límite elástico of 370.0 MPa | T89 | |||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | T89 | AA Standards, ASTM B211 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Resistencia a la tracción | 370.0 MPa Show Material materials with Resistencia a la tracción of 370.0 MPa | T89 | AA Standards, ASTM B211 | |
430.0 MPa Show Material materials with Resistencia a la tracción of 430.0 MPa | T89 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | T89 | ||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | T89 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | T89 | AA Standards, ASTM B211 | |
100 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | T89 | AA Standards, ASTM B211 | |
Conductividad térmica | 155.0 - 180.0 W/(m·K) Show Material materials with Conductividad térmica of 155.0 - 180.0 W/(m·K) | T89 | AA Standards, ASTM B211 | |
170.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 W/(m·K) | T89 | |||
Temperatura de fusión | 580.0 - 650.0 °C Show Material materials with Temperatura de fusión of 580.0 - 650.0 °C | T89 | AA Standards, ASTM B211 | |
580.0 °C Show Material materials with Temperatura de fusión of 580.0 °C | T89 |
Eléctrico
Property | Value | Condition | Related Standards |
---|---|---|---|
Conductividad eléctrica | 23000000.0 - 27000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 27000000.0 S/m | T89 | AA Standards, ASTM B211 |
Resistividad eléctrica | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.7e-08 - 4.35e-08 Ω·m | T89 | AA Standards, ASTM B211 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 95.9 - 98.6 % Show Material materials with Aluminio of 95.9 - 98.6 % | T89 | |
Cobre | 0.15 - 0.4 % Show Material materials with Cobre of 0.15 - 0.4 % | T89 | AA Standards, ASTM B211 |
Cromo | 0.04 - 0.35 % Show Material materials with Cromo of 0.04 - 0.35 % | T89 | AA Standards, ASTM B211 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T89 | AA Standards, ASTM B211 |
0.7 % Show Material materials with Hierro of 0.7 % | T89 | ||
Magnesio | 0.8 - 1.2 % Show Material materials with Magnesio of 0.8 - 1.2 % | T89 | AA Standards, ASTM B211 |
Manganeso | 0.15 % Show Material materials with Manganeso of 0.15 % | T89 | AA Standards, ASTM B211 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T89 | |
Silicona | 0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 % | T89 | AA Standards, ASTM B211 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T89 | AA Standards, ASTM B211 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T89 | AA Standards, ASTM B211 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) |