Propiedades
General
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 MPa | T1 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Dureza Brinell | 42.0 [-] Show Material materials with Dureza Brinell of 42.0 [-] | T1 | AA Standards | ||
42.0 [-] Show Material materials with Dureza Brinell of 42.0 [-] | T1 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 44 % Show Material materials with Elongación of 44 % | T1 | Elongation in 50 mm | |
-80 °C | 36 % Show Material materials with Elongación of 36 % | T1 | Elongation in 50 mm | ||
10.0 % Show Material materials with Elongación of 10.0 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | A100 | ||
12.0 % Show Material materials with Elongación of 12.0 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | A50 | ||
16.0 % Show Material materials with Elongación of 16.0 % | T1 | ||||
20.0 % Show Material materials with Elongación of 20.0 % | T1 | AA Standards | A50 | ||
0 °C | 34 % Show Material materials with Elongación of 34 % | T1 | Elongation in 50 mm | ||
24 °C | 33 % Show Material materials with Elongación of 33 % | T1 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Elongación of 18 % | T1 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Elongación of 20 % | T1 | Elongation in 50 mm | ||
205 °C | 40 % Show Material materials with Elongación of 40 % | T1 | Elongation in 50 mm | ||
260 °C | 75 % Show Material materials with Elongación of 75 % | T1 | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongación of 80 % | T1 | Elongation in 50 mm | ||
370 °C | 105 % Show Material materials with Elongación of 105 % | T1 | Elongation in 50 mm | ||
Límite elástico | -196 °C | 110 MPa Show Material materials with Límite elástico of 110 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 103 MPa Show Material materials with Límite elástico of 103 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 97 MPa Show Material materials with Límite elástico of 97 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
55.0 MPa Show Material materials with Límite elástico of 55.0 MPa | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | RP02 | ||
60.0 MPa Show Material materials with Límite elástico of 60.0 MPa | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | RP02 | ||
78.0 MPa Show Material materials with Límite elástico of 78.0 MPa | T1 | ||||
90.0 MPa Show Material materials with Límite elástico of 90.0 MPa | T1 | AA Standards | RP02 | ||
24 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 97 MPa Show Material materials with Límite elástico of 97 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 103 MPa Show Material materials with Límite elástico of 103 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 45 MPa Show Material materials with Límite elástico of 45 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 24 MPa Show Material materials with Límite elástico of 24 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 17 MPa Show Material materials with Límite elástico of 17 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 14 MPa Show Material materials with Límite elástico of 14 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Módulo de compresión | 69.7 MPa Show Material materials with Módulo de compresión of 69.7 MPa | T1 | |||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | ||
69 GPa Show Material materials with Módulo elástico of 69 GPa | T1 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |||
Resistencia a la fatiga | 62 MPa Show Material materials with Resistencia a la fatiga of 62 MPa | T1 | fo 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 235 MPa Show Material materials with Resistencia a la tracción of 235 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
110.0 MPa Show Material materials with Resistencia a la tracción of 110.0 MPa | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |||
115.0 MPa Show Material materials with Resistencia a la tracción of 115.0 MPa | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |||
140.0 MPa Show Material materials with Resistencia a la tracción of 140.0 MPa | T1 | ||||
150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa | T1 | AA Standards | |||
0 °C | 165 MPa Show Material materials with Resistencia a la tracción of 165 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 152 MPa Show Material materials with Resistencia a la tracción of 152 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 145 MPa Show Material materials with Resistencia a la tracción of 145 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 62 MPa Show Material materials with Resistencia a la tracción of 62 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 31 MPa Show Material materials with Resistencia a la tracción of 31 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 22 MPa Show Material materials with Resistencia a la tracción of 22 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 16 MPa Show Material materials with Resistencia a la tracción of 16 MPa | T1 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 97.0 MPa Show Material materials with Resistencia al cizallamiento of 97.0 MPa | T1 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | T1 | ||
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T1 | ||
20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
Conductividad térmica | 193.0 - 218.0 W/(m·K) Show Material materials with Conductividad térmica of 193.0 - 218.0 W/(m·K) | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
200.0 W/(m·K) Show Material materials with Conductividad térmica of 200.0 W/(m·K) | T1 | |||
Temperatura de fusión | 615.0 - 655.0 °C Show Material materials with Temperatura de fusión of 615.0 - 655.0 °C | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
620.0 °C Show Material materials with Temperatura de fusión of 620.0 °C | T1 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 29000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 29000000.0 - 34000000.0 S/m | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
29000000 S/m Show Material materials with Conductividad eléctrica of 29000000 S/m | T1 | Typical value | ||
Resistividad eléctrica | 2.94e-08 - 3.45e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.94e-08 - 3.45e-08 Ω·m | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
3.4e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.4e-08 Ω·m | T1 | Typical value | ||
Specific Electrical conductivity | 50.0 % IACS Show Material materials with Specific Electrical conductivity of 50.0 % IACS | T1 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 97.5 - 99.4 % Show Material materials with Aluminio of 97.5 - 99.4 % | T1 | |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Hierro | 0.35 % Show Material materials with Hierro of 0.35 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
0.35 % Show Material materials with Hierro of 0.35 % | T1 | ||
Magnesio | 0.45 - 0.9 % Show Material materials with Magnesio of 0.45 - 0.9 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T1 | |
Silicona | 0.2 - 0.6 % Show Material materials with Silicona of 0.2 - 0.6 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Titanio | 0.1 % Show Material materials with Titanio of 0.1 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T1 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (T1, T4), sufficient (T5, T452, T6, T83, T831, T832) | |
| Workability | general (condition): acceptable (T1, T4, T5, T452), poor(T6, T83, T831, T832) | |