General
Property | Value | Condition | Related Standards |
---|---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H113 | |
2.705 g/cm³ Show Material materials with Densidad of 2.705 g/cm³ | H113 | AA Standards, ASTM B210, ASTM B483 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Límite elástico | 15.0 MPa Show Material materials with Límite elástico of 15.0 MPa | H113 | AA Standards, ASTM B210, ASTM B483 | RP02 |
17.0 MPa Show Material materials with Límite elástico of 17.0 MPa | H113 | |||
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H113 | AA Standards, ASTM B210, ASTM B483 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Resistencia a la tracción | 60.0 MPa Show Material materials with Resistencia a la tracción of 60.0 MPa | H113 | AA Standards, ASTM B210, ASTM B483 | |
69.0 MPa Show Material materials with Resistencia a la tracción of 69.0 MPa | H113 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H113 | ||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H113 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | H113 | AA Standards, ASTM B210, ASTM B483 | |
100 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | H113 | AA Standards, ASTM B210, ASTM B483 | |
Conductividad térmica | 230.0 - 234.0 W/(m·K) Show Material materials with Conductividad térmica of 230.0 - 234.0 W/(m·K) | H113 | AA Standards, ASTM B210, ASTM B483 | |
230.0 W/(m·K) Show Material materials with Conductividad térmica of 230.0 W/(m·K) | H113 | |||
Temperatura de fusión | 645.0 - 655.0 °C Show Material materials with Temperatura de fusión of 645.0 - 655.0 °C | H113 | AA Standards, ASTM B210, ASTM B483 | |
650.0 °C Show Material materials with Temperatura de fusión of 650.0 °C | H113 |
Eléctrico
Property | Value | Condition | Related Standards |
---|---|---|---|
Conductividad eléctrica | 35000000.0 - 36000000.0 S/m Show Material materials with Conductividad eléctrica of 35000000.0 - 36000000.0 S/m | H113 | AA Standards, ASTM B210, ASTM B483 |
Resistividad eléctrica | 2.78e-08 - 2.86e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.78e-08 - 2.86e-08 Ω·m | H113 | AA Standards, ASTM B210, ASTM B483 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 99.6 % Show Material materials with Aluminio of 99.6 % | H113 | AA Standards, ASTM B210, ASTM B483 |
99.6 - 100.0 % Show Material materials with Aluminio of 99.6 - 100.0 % | H113 | ||
Cobre | 0.05 % Show Material materials with Cobre of 0.05 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Hierro | 0.35 % Show Material materials with Hierro of 0.35 % | H113 | AA Standards, ASTM B210, ASTM B483 |
0.35 % Show Material materials with Hierro of 0.35 % | H113 | ||
Magnesio | 0.03 % Show Material materials with Magnesio of 0.03 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Manganeso | 0.03 % Show Material materials with Manganeso of 0.03 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Titanio | 0.03 % Show Material materials with Titanio of 0.03 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Vanadio | 0.05 % Show Material materials with Vanadio of 0.05 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) |