Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.78 g/cm³ Show Material materials with Densidad of 2.78 g/cm³ | T53 | AA Standards, ASTM B221 |
2.78 g/cm³ Show Material materials with Densidad of 2.78 g/cm³ | T53 | ||
2.9 g/cm³ Show Material materials with Densidad of 2.9 g/cm³ | T53 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | |||
Elongación | -269 °C | 16 % Show Material materials with Elongación of 16 % | T53 | Elongation in 50 mm | |
-196 °C | 16 % Show Material materials with Elongación of 16 % | T53 | Elongation in 50 mm | ||
-80 °C | 13 % Show Material materials with Elongación of 13 % | T53 | Elongation in 50 mm | ||
-28 °C | 14 % Show Material materials with Elongación of 14 % | T53 | Elongation in 50 mm | ||
9.0 % Show Material materials with Elongación of 9.0 % | T53 | AA Standards, ASTM B221 | A100 | ||
10.0 % Show Material materials with Elongación of 10.0 % | T53 | AA Standards, ASTM B221 | A50 | ||
10.0 % Show Material materials with Elongación of 10.0 % | T53 | ||||
24 °C | 15 % Show Material materials with Elongación of 15 % | T53 | Elongation in 50 mm | ||
100 °C | 20 % Show Material materials with Elongación of 20 % | T53 | Elongation in 50 mm | ||
149 °C | 35 % Show Material materials with Elongación of 35 % | T53 | Elongation in 50 mm | ||
204 °C | 60 % Show Material materials with Elongación of 60 % | T53 | Elongation in 50 mm | ||
Límite elástico | -269 °C | 483 MPa Show Material materials with Límite elástico of 483 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-196 °C | 421 MPa Show Material materials with Límite elástico of 421 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 379 MPa Show Material materials with Límite elástico of 379 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 359 MPa Show Material materials with Límite elástico of 359 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
305.0 MPa Show Material materials with Límite elástico of 305.0 MPa | T53 | AA Standards, ASTM B221 | RP02 | ||
350.0 MPa Show Material materials with Límite elástico of 350.0 MPa | T53 | ||||
24 °C | 345 MPa Show Material materials with Límite elástico of 345 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 283 MPa Show Material materials with Límite elástico of 283 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 145 MPa Show Material materials with Límite elástico of 145 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 83 MPa Show Material materials with Límite elástico of 83 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 26.9 GPa Show Material materials with Módulo de cizallamiento of 26.9 GPa | T53 | |||
Módulo de compresión | 72.4 MPa Show Material materials with Módulo de compresión of 72.4 MPa | T53 | |||
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | T53 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | |||
Resistencia a la fatiga | 231 MPa Show Material materials with Resistencia a la fatiga of 231 MPa | T53 | fo 5x10⁸ cycles | ||
Resistencia a la tracción | -269 °C | 641 MPa Show Material materials with Resistencia a la tracción of 641 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-196 °C | 538 MPa Show Material materials with Resistencia a la tracción of 538 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 441 MPa Show Material materials with Resistencia a la tracción of 441 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-28 °C | 421 MPa Show Material materials with Resistencia a la tracción of 421 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
345.0 MPa Show Material materials with Resistencia a la tracción of 345.0 MPa | T53 | AA Standards, ASTM B221 | |||
400.0 MPa Show Material materials with Resistencia a la tracción of 400.0 MPa | T53 | ||||
24 °C | 392 MPa Show Material materials with Resistencia a la tracción of 392 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 303 MPa Show Material materials with Resistencia a la tracción of 303 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
149 °C | 165 MPa Show Material materials with Resistencia a la tracción of 165 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
204 °C | 97 MPa Show Material materials with Resistencia a la tracción of 97 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 221.0 MPa Show Material materials with Resistencia al cizallamiento of 221.0 MPa | T53 |
Aplicaciones térmicas
| Property | Value | Condition | Comment |
|---|---|---|---|
Calor específico | 880.0 J/(kg·K) Show Material materials with Calor específico of 880.0 J/(kg·K) | T53 | |
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T53 | |
Conductividad térmica | 121.0 - 170.0 W/(m·K) Show Material materials with Conductividad térmica of 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium | |
Temperatura de fusión | 610.0 °C Show Material materials with Temperatura de fusión of 610.0 °C | T53 |
Eléctrico
| Property | Value | Condition | Comment |
|---|---|---|---|
Conductividad eléctrica | 22000000 S/m Show Material materials with Conductividad eléctrica of 22000000 S/m | T53 | Typical/derived value |
Resistividad eléctrica | 4.54e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.54e-08 Ω·m | T53 | Typical value |
Specific Electrical conductivity | 38.0 % IACS Show Material materials with Specific Electrical conductivity of 38.0 % IACS | T53 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 91.0 - 94.7 % Show Material materials with Aluminio of 91.0 - 94.7 % | T53 | |
Circonio | 0.08 - 0.2 % Show Material materials with Circonio of 0.08 - 0.2 % | T53 | AA Standards, ASTM B221 |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | T53 | AA Standards, ASTM B221 |
Cromo | 0.06 - 0.2 % Show Material materials with Cromo of 0.06 - 0.2 % | T53 | AA Standards, ASTM B221 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | T53 | AA Standards, ASTM B221 |
0.4 % Show Material materials with Hierro of 0.4 % | T53 | ||
Magnesio | 1.0 - 1.8 % Show Material materials with Magnesio of 1.0 - 1.8 % | T53 | AA Standards, ASTM B221 |
Manganeso | 0.2 - 0.7 % Show Material materials with Manganeso of 0.2 - 0.7 % | T53 | AA Standards, ASTM B221 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T53 | |
Silicona | 0.35 % Show Material materials with Silicona of 0.35 % | T53 | AA Standards, ASTM B221 |
Titanio | 0.01 - 0.06 % Show Material materials with Titanio of 0.01 - 0.06 % | T53 | AA Standards, ASTM B221 |
Zinc | 4.0 - 5.0 % Show Material materials with Zinc of 4.0 - 5.0 % | T53 | AA Standards, ASTM B221 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |