Propiedades
General
| Property | Value | Condition | Shape |
|---|---|---|---|
Densidad | 2.81 g/cm³ Show Material materials with Densidad of 2.81 g/cm³ | T651 | |
2.81 g/cm³ Show Material materials with Densidad of 2.81 g/cm³ | T651 | Bar | |
3.1 g/cm³ Show Material materials with Densidad of 3.1 g/cm³ | T651 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 160.0 MPa Show Material materials with Bending Fatigue Strength of 160.0 MPa | T651 | AA Standards | |||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | T651 | ||||
Dureza Brinell | 150.0 [-] Show Material materials with Dureza Brinell of 150.0 [-] | T651 | AA Standards | |||
150.0 [-] Show Material materials with Dureza Brinell of 150.0 [-] | T651 | 500 kg load, 10 mm ball | ||||
Elongación | -195 °C | 9 % Show Material materials with Elongación of 9 % | T651 | Elongation in 50 mm | ||
-80 °C | 11 % Show Material materials with Elongación of 11 % | T651 | Elongation in 50 mm | |||
2.0 % Show Material materials with Elongación of 2.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
4.0 % Show Material materials with Elongación of 4.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
5.0 % Show Material materials with Elongación of 5.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
6.0 % Show Material materials with Elongación of 6.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
7.0 % Show Material materials with Elongación of 7.0 % | T651 | AA Standards, ASTM B211 | Bar | A50 | ||
7.4 % Show Material materials with Elongación of 7.4 % | T651 | |||||
9.0 % Show Material materials with Elongación of 9.0 % | T651 | AA Standards, ASTM B209 | A50 | |||
9.0 % Show Material materials with Elongación of 9.0 % | T651 | AA Standards | A100 | |||
11.0 % Show Material materials with Elongación of 11.0 % | T651 | AA Standards | A50 | |||
11.0 % Show Material materials with Elongación of 11.0 % | T651 | |||||
0 °C | 11 % Show Material materials with Elongación of 11 % | T651 | Elongation in 50 mm | |||
24 °C | 11 % Show Material materials with Elongación of 11 % | T651 | Elongation in 50 mm | |||
100 °C | 14 % Show Material materials with Elongación of 14 % | T651 | Elongation in 50 mm | |||
150 °C | 30 % Show Material materials with Elongación of 30 % | T651 | Elongation in 50 mm | |||
205 °C | 55 % Show Material materials with Elongación of 55 % | T651 | Elongation in 50 mm | |||
260 °C | 65 % Show Material materials with Elongación of 65 % | T651 | Elongation in 50 mm | |||
315 °C | 70 % Show Material materials with Elongación of 70 % | T651 | Elongation in 50 mm | |||
370 °C | 70 % Show Material materials with Elongación of 70 % | T651 | Elongation in 50 mm | |||
Límite elástico | -196 °C | 634 MPa Show Material materials with Límite elástico of 634 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 545 MPa Show Material materials with Límite elástico of 545 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-28 °C | 517 MPa Show Material materials with Límite elástico of 517 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
370.0 MPa Show Material materials with Límite elástico of 370.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
400.0 MPa Show Material materials with Límite elástico of 400.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
420.0 MPa Show Material materials with Límite elástico of 420.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
425.0 MPa Show Material materials with Límite elástico of 425.0 MPa | T651 | AA Standards, ASTM B211 | RP02 | |||
440.0 MPa Show Material materials with Límite elástico of 440.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211 | RP02 | |||
455.0 MPa Show Material materials with Límite elástico of 455.0 MPa | T651 | AA Standards, ASTM B211 | Bar | RP02 | ||
460.0 MPa Show Material materials with Límite elástico of 460.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
470.0 MPa Show Material materials with Límite elástico of 470.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
470.0 MPa Show Material materials with Límite elástico of 470.0 MPa | T651 | |||||
505.0 MPa Show Material materials with Límite elástico of 505.0 MPa | T651 | AA Standards | RP02 | |||
505.0 MPa Show Material materials with Límite elástico of 505.0 MPa | T651 | |||||
24 °C | 503 MPa Show Material materials with Límite elástico of 503 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 448 MPa Show Material materials with Límite elástico of 448 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
149 °C | 186 MPa Show Material materials with Límite elástico of 186 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
204 °C | 87 MPa Show Material materials with Límite elástico of 87 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
316 °C | 45 MPa Show Material materials with Límite elástico of 45 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
371 °C | 32 MPa Show Material materials with Límite elástico of 32 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
Módulo de cizallamiento | 26.9 GPa Show Material materials with Módulo de cizallamiento of 26.9 GPa | T651 | ||||
Módulo de compresión | 72.4 MPa Show Material materials with Módulo de compresión of 72.4 MPa | T651 | ||||
Módulo elástico | 72.0 GPa Show Material materials with Módulo elástico of 72.0 GPa | T651 | Bar | |||
Plane-Strain Fracture Toughnes | -196 °C | 33.5 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 33.5 MPa·√m | T651 | For plate in T-L direction | ||
24.2 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.2 MPa·√m | T651 | |||||
24 °C | 32.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 32.3 MPa·√m | T651 | For plate in T-L direction | |||
Resistencia a la fatiga | 159 MPa Show Material materials with Resistencia a la fatiga of 159 MPa | T651 | for 5x10⁸ cycles | |||
Resistencia a la tracción | -195 °C | 703 MPa Show Material materials with Resistencia a la tracción of 703 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 620 MPa Show Material materials with Resistencia a la tracción of 620 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
460.0 MPa Show Material materials with Resistencia a la tracción of 460.0 MPa | T651 | AA Standards, ASTM B209 | ||||
490.0 MPa Show Material materials with Resistencia a la tracción of 490.0 MPa | T651 | AA Standards, ASTM B209 | ||||
495.0 MPa Show Material materials with Resistencia a la tracción of 495.0 MPa | T651 | AA Standards, ASTM B209 | ||||
505.0 MPa Show Material materials with Resistencia a la tracción of 505.0 MPa | T651 | AA Standards, ASTM B211 | ||||
515.0 MPa Show Material materials with Resistencia a la tracción of 515.0 MPa | T651 | AA Standards, ASTM B211 | ||||
525.0 MPa Show Material materials with Resistencia a la tracción of 525.0 MPa | T651 | AA Standards, ASTM B209 | ||||
530.0 MPa Show Material materials with Resistencia a la tracción of 530.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211 | ||||
531.0 MPa Show Material materials with Resistencia a la tracción of 531.0 MPa | T651 | Bar | ||||
540.0 MPa Show Material materials with Resistencia a la tracción of 540.0 MPa | T651 | AA Standards, ASTM B209 | ||||
560.0 MPa Show Material materials with Resistencia a la tracción of 560.0 MPa | T651 | |||||
570.0 MPa Show Material materials with Resistencia a la tracción of 570.0 MPa | T651 | AA Standards | ||||
0 °C | 593 MPa Show Material materials with Resistencia a la tracción of 593 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
24 °C | 572 MPa Show Material materials with Resistencia a la tracción of 572 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 483 MPa Show Material materials with Resistencia a la tracción of 483 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 215 MPa Show Material materials with Resistencia a la tracción of 215 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 75 MPa Show Material materials with Resistencia a la tracción of 75 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 55 MPa Show Material materials with Resistencia a la tracción of 55 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
Resistencia al cizallamiento | 331.0 MPa Show Material materials with Resistencia al cizallamiento of 331.0 MPa | T651 |
Aplicaciones térmicas
| Property | Value | Condition | Shape |
|---|---|---|---|
Calor específico | 910.0 J/(kg·K) Show Material materials with Calor específico of 910.0 J/(kg·K) | T651 | |
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T651 | |
2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K | T651 | Bar | |
Conductividad térmica | 130.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 W/(m·K) | T651 | |
134.0 - 160.0 W/(m·K) Show Material materials with Conductividad térmica of 134.0 - 160.0 W/(m·K) | T651 | Bar | |
Temperatura de fusión | 477.0 °C Show Material materials with Temperatura de fusión of 477.0 °C | T651 | |
480.0 °C Show Material materials with Temperatura de fusión of 480.0 °C | T651 | ||
635.0 °C Show Material materials with Temperatura de fusión of 635.0 °C | T651 | Bar |
Eléctrico
| Property | Value | Condition | Shape | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 19000000 S/m Show Material materials with Conductividad eléctrica of 19000000 S/m | T651 | Typical/derived value | |
Resistividad eléctrica | 4.31e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.31e-08 Ω·m | T651 | Bar | |
5.22e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.22e-08 Ω·m | T651 | Typical value | ||
Specific Electrical conductivity | 33.0 % IACS Show Material materials with Specific Electrical conductivity of 33.0 % IACS | T651 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Aluminio | 86.9 - 91.4 % Show Material materials with Aluminio of 86.9 - 91.4 % | T651 | |||
Circonio | 0.25 % Show Material materials with Circonio of 0.25 % | T651 | |||
Cobre | 1.2 - 2.0 % Show Material materials with Cobre of 1.2 - 2.0 % | T651 | AA Standards, ASTM B209, ASTM B211 | Bar | |
Cromo | 0.18 - 0.28 % Show Material materials with Cromo of 0.18 - 0.28 % | T651 | AA Standards, ASTM B209, ASTM B211 | Bar | |
Hierro | 0.50 % Show Material materials with Hierro of 0.50 % | T651 | AA Standards, ASTM B209, ASTM B211 | ||
0.5 % Show Material materials with Hierro of 0.5 % | T651 | Bar | |||
Magnesio | 2.1 - 2.9 % Show Material materials with Magnesio of 2.1 - 2.9 % | T651 | AA Standards, ASTM B209, ASTM B211 | Bar | |
Manganeso | 0.3 % Show Material materials with Manganeso of 0.3 % | T651 | AA Standards, ASTM B209, ASTM B211 | Bar | |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T651 | Bar | Total | |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | T651 | AA Standards, ASTM B209, ASTM B211 | Bar | |
Titanio | 0.2 % Show Material materials with Titanio of 0.2 % | T651 | AA Standards, ASTM B209, ASTM B211 | Bar | |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T651 | AA Standards, ASTM B209, ASTM B211 | Bar |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): not suitable | |