General
Property | Value | Condition |
---|---|---|
Densidad | 3.1 g/cm³ Show Material materials with Densidad of 3.1 g/cm³ | T6510 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||
Elongación | 5.0 % Show Material materials with Elongación of 5.0 % | T6510 | AA Standards, ASTM B221 | A100 |
5.8 % Show Material materials with Elongación of 5.8 % | T6510 | |||
6.0 % Show Material materials with Elongación of 6.0 % | T6510 | AA Standards, ASTM B221, ASTM B241 | A100 | |
7.0 % Show Material materials with Elongación of 7.0 % | T6510 | AA Standards, ASTM B221, ASTM B241 | A50 | |
Límite elástico | 470.0 MPa Show Material materials with Límite elástico of 470.0 MPa | T6510 | AA Standards, ASTM B221 | RP02 |
485.0 MPa Show Material materials with Límite elástico of 485.0 MPa | T6510 | AA Standards, ASTM B221, ASTM B241 | RP02 | |
490.0 MPa Show Material materials with Límite elástico of 490.0 MPa | T6510 | AA Standards, ASTM B221 | RP02 | |
495.0 MPa Show Material materials with Límite elástico of 495.0 MPa | T6510 | AA Standards, ASTM B221, ASTM B241 | RP02 | |
505.0 MPa Show Material materials with Límite elástico of 505.0 MPa | T6510 | AA Standards, ASTM B221, ASTM B241 | RP02 | |
520.0 MPa Show Material materials with Límite elástico of 520.0 MPa | T6510 | |||
Módulo de cizallamiento | 26.4 - 27.1 GPa Show Material materials with Módulo de cizallamiento of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||
Módulo elástico | 72.0 GPa Show Material materials with Módulo elástico of 72.0 GPa | T6510 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||
Resistencia a la tracción | 540.0 MPa Show Material materials with Resistencia a la tracción of 540.0 MPa | T6510 | AA Standards, ASTM B221, ASTM B241 | |
560.0 MPa Show Material materials with Resistencia a la tracción of 560.0 MPa | T6510 | AA Standards, ASTM B221, ASTM B241 | ||
590.0 MPa Show Material materials with Resistencia a la tracción of 590.0 MPa | T6510 |
Aplicaciones térmicas
Property | Value | Condition |
---|---|---|
Calor específico | 910.0 J/(kg·K) Show Material materials with Calor específico of 910.0 J/(kg·K) | T6510 |
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T6510 |
Conductividad térmica | 130.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 W/(m·K) | T6510 |
Temperatura de fusión | 480.0 °C Show Material materials with Temperatura de fusión of 480.0 °C | T6510 |
Eléctrico
Property | Value | Comment |
---|---|---|
Conductividad eléctrica | 18000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Resistividad eléctrica | 2.9e-08 - 5.6e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 86.9 - 91.4 % Show Material materials with Aluminio of 86.9 - 91.4 % | T6510 | |
Circonio | 0.25 % Show Material materials with Circonio of 0.25 % | T6510 | |
Cobre | 1.2 - 2.0 % Show Material materials with Cobre of 1.2 - 2.0 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
Cromo | 0.18 - 0.28 % Show Material materials with Cromo of 0.18 - 0.28 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
Hierro | 0.50 % Show Material materials with Hierro of 0.50 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
0.5 % Show Material materials with Hierro of 0.5 % | T6510 | ||
Magnesio | 2.1 - 2.9 % Show Material materials with Magnesio of 2.1 - 2.9 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
Manganeso | 0.3 % Show Material materials with Manganeso of 0.3 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T6510 | |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
Titanio | 0.2 % Show Material materials with Titanio of 0.2 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T6510 | AA Standards, ASTM B221, ASTM B241 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O), good to acceptable | |
Workability | general (condition): not suitable |