Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³ | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³ | H18 | ||
2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | H18 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 MPa | H18 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | |||
Dureza Brinell | 44.0 [-] Show Material materials with Dureza Brinell of 44.0 [-] | H18 | AA Standards | ||
44.0 [-] Show Material materials with Dureza Brinell of 44.0 [-] | H18 | 500 kg load, 10 mm ball | |||
Elongación | -195 °C | 30 % Show Material materials with Elongación of 30 % | H18 | Elongation in 50 mm | |
-80 °C | 16 % Show Material materials with Elongación of 16 % | H18 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongación of 1.0 % | H18 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Elongación of 2.0 % | H18 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
4.0 % Show Material materials with Elongación of 4.0 % | H18 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
5.0 % Show Material materials with Elongación of 5.0 % | H18 | AA Standards | A50 | ||
6.5 % Show Material materials with Elongación of 6.5 % | H18 | ||||
13.0 % Show Material materials with Elongación of 13.0 % | H18 | AA Standards | A100 | ||
0 °C | 15 % Show Material materials with Elongación of 15 % | H18 | Elongation in 50 mm | ||
24 °C | 15 % Show Material materials with Elongación of 15 % | H18 | Elongation in 50 mm | ||
100 °C | 15 % Show Material materials with Elongación of 15 % | H18 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Elongación of 20 % | H18 | Elongation in 50 mm | ||
205 °C | 65 % Show Material materials with Elongación of 65 % | H18 | Elongation in 50 mm | ||
260 °C | 75 % Show Material materials with Elongación of 75 % | H18 | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongación of 80 % | H18 | Elongation in 50 mm | ||
370 °C | 85 % Show Material materials with Elongación of 85 % | H18 | Elongation in 50 mm | ||
Límite elástico | -196 °C | 180 MPa Show Material materials with Límite elástico of 180 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 160 MPa Show Material materials with Límite elástico of 160 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 160 MPa Show Material materials with Límite elástico of 160 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
140.0 MPa Show Material materials with Límite elástico of 140.0 MPa | H18 | AA Standards, ASTM B210, ASTM B483 | RP02 | ||
150.0 MPa Show Material materials with Límite elástico of 150.0 MPa | H18 | AA Standards | RP02 | ||
150.0 MPa Show Material materials with Límite elástico of 150.0 MPa | H18 | ||||
24 °C | 150 MPa Show Material materials with Límite elástico of 150 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 130 MPa Show Material materials with Límite elástico of 130 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 97 MPa Show Material materials with Límite elástico of 97 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 24 MPa Show Material materials with Límite elástico of 24 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 18 MPa Show Material materials with Límite elástico of 18 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 14 MPa Show Material materials with Límite elástico of 14 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 11 MPa Show Material materials with Límite elástico of 11 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 25.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 GPa | H18 | |||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
69 GPa Show Material materials with Módulo elástico of 69 GPa | H18 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |||
Resistencia a la fatiga | 62 MPa Show Material materials with Resistencia a la fatiga of 62 MPa | H18 | for 5x10⁸ cycles | ||
Resistencia a la tracción | -195 °C | 235 MPa Show Material materials with Resistencia a la tracción of 235 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |||
165.0 MPa Show Material materials with Resistencia a la tracción of 165.0 MPa | H18 | AA Standards | |||
170.0 MPa Show Material materials with Resistencia a la tracción of 170.0 MPa | H18 | ||||
0 °C | 172 MPa Show Material materials with Resistencia a la tracción of 172 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 165 MPa Show Material materials with Resistencia a la tracción of 165 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 145 MPa Show Material materials with Resistencia a la tracción of 145 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 125 MPa Show Material materials with Resistencia a la tracción of 125 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 28 MPa Show Material materials with Resistencia a la tracción of 28 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 20 MPa Show Material materials with Resistencia a la tracción of 20 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 14 MPa Show Material materials with Resistencia a la tracción of 14 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 85.0 MPa Show Material materials with Resistencia al cizallamiento of 85.0 MPa | H18 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H18 | ||
Coeficiente de dilatación térmica | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | H18 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
100 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
Conductividad térmica | 218.0 - 222.0 W/(m·K) Show Material materials with Conductividad térmica of 218.0 - 222.0 W/(m·K) | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
220.0 W/(m·K) Show Material materials with Conductividad térmica of 220.0 W/(m·K) | H18 | |||
Temperatura de fusión | 640.0 - 655.0 °C Show Material materials with Temperatura de fusión of 640.0 - 655.0 °C | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
640.0 °C Show Material materials with Temperatura de fusión of 640.0 °C | H18 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 33000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 33000000.0 - 34000000.0 S/m | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
33000000 S/m Show Material materials with Conductividad eléctrica of 33000000 S/m | H18 | Typical value | ||
Resistividad eléctrica | 2.94e-08 - 3.03e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.94e-08 - 3.03e-08 Ω·m | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
3.02e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.02e-08 Ω·m | H18 | Typical value | ||
Specific Electrical conductivity | 57.0 % IACS Show Material materials with Specific Electrical conductivity of 57.0 % IACS | H18 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 99.0 % Show Material materials with Aluminio of 99.0 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
99.0 - 100.0 % Show Material materials with Aluminio of 99.0 - 100.0 % | H18 | ||
Cobre | 0.05 - 0.2 % Show Material materials with Cobre of 0.05 - 0.2 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Hierro | 1.0 % Show Material materials with Hierro of 1.0 % | H18 | |
Manganeso | 0.05 % Show Material materials with Manganeso of 0.05 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H18 | |
Silicona | 1.0 % Show Material materials with Silicona of 1.0 % | H18 | |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16), poor(H18) | |