Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.83 g/cm³ Show Material materials with Densidad of 2.83 g/cm³ | T3 | AA Standards, ASTM B210, ASTM B211 |
2.83 g/cm³ Show Material materials with Densidad of 2.83 g/cm³ | T3 | ||
3.1 g/cm³ Show Material materials with Densidad of 3.1 g/cm³ | T3 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | T3 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Dureza Brinell | 95.0 [-] Show Material materials with Dureza Brinell of 95.0 [-] | T3 | AA Standards | ||
95.0 [-] Show Material materials with Dureza Brinell of 95.0 [-] | T3 | 500 kg load, 10 mm ball | |||
Elongación | 7.0 % Show Material materials with Elongación of 7.0 % | T3 | AA Standards, ASTM B210 | A100 | |
8.0 % Show Material materials with Elongación of 8.0 % | T3 | AA Standards, ASTM B210 | A50 | ||
9.0 % Show Material materials with Elongación of 9.0 % | T3 | AA Standards, ASTM B211 | A100 | ||
10.0 % Show Material materials with Elongación of 10.0 % | T3 | AA Standards, ASTM B211 | A100 | ||
10.0 % Show Material materials with Elongación of 10.0 % | T3 | AA Standards, ASTM B211 | A50 | ||
12.0 % Show Material materials with Elongación of 12.0 % | T3 | AA Standards, ASTM B211 | A100 | ||
12.0 % Show Material materials with Elongación of 12.0 % | T3 | ||||
13.0 % Show Material materials with Elongación of 13.0 % | T3 | AA Standards | A100 | ||
24 °C | 15 % Show Material materials with Elongación of 15 % | T3 | |||
100 °C | 16 % Show Material materials with Elongación of 16 % | T3 | |||
150 °C | 25 % Show Material materials with Elongación of 25 % | T3 | |||
205 °C | 35 % Show Material materials with Elongación of 35 % | T3 | |||
260 °C | 45 % Show Material materials with Elongación of 45 % | T3 | |||
315 °C | 90 % Show Material materials with Elongación of 90 % | T3 | |||
370 °C | 125 % Show Material materials with Elongación of 125 % | T3 | |||
Límite elástico | 205.0 MPa Show Material materials with Límite elástico of 205.0 MPa | T3 | AA Standards, ASTM B211 | RP02 | |
235.0 MPa Show Material materials with Límite elástico of 235.0 MPa | T3 | AA Standards, ASTM B211 | RP02 | ||
260.0 MPa Show Material materials with Límite elástico of 260.0 MPa | T3 | AA Standards, ASTM B211 | RP02 | ||
275.0 MPa Show Material materials with Límite elástico of 275.0 MPa | T3 | AA Standards, ASTM B210 | RP02 | ||
280.0 MPa Show Material materials with Límite elástico of 280.0 MPa | T3 | ||||
295.0 MPa Show Material materials with Límite elástico of 295.0 MPa | T3 | AA Standards | RP02 | ||
Módulo de cizallamiento | 26.0 GPa Show Material materials with Módulo de cizallamiento of 26.0 GPa | T3 | |||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | T3 | AA Standards, ASTM B210, ASTM B211 | ||
70 GPa Show Material materials with Módulo elástico of 70 GPa | T3 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Resistencia a la fatiga | 124 MPa Show Material materials with Resistencia a la fatiga of 124 MPa | T3 | for 5x10⁸ cycles | ||
Resistencia a la tracción | 290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | T3 | AA Standards, ASTM B211 | ||
295.0 MPa Show Material materials with Resistencia a la tracción of 295.0 MPa | T3 | AA Standards, ASTM B211 | |||
310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T3 | AA Standards, ASTM B211 | |||
325.0 MPa Show Material materials with Resistencia a la tracción of 325.0 MPa | T3 | AA Standards, ASTM B210 | |||
360.0 MPa Show Material materials with Resistencia a la tracción of 360.0 MPa | T3 | ||||
380.0 MPa Show Material materials with Resistencia a la tracción of 380.0 MPa | T3 | AA Standards | |||
24 °C | 380 MPa Show Material materials with Resistencia a la tracción of 380 MPa | T3 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 325 MPa Show Material materials with Resistencia a la tracción of 325 MPa | T3 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 193 MPa Show Material materials with Resistencia a la tracción of 193 MPa | T3 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | T3 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 45 MPa Show Material materials with Resistencia a la tracción of 45 MPa | T3 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 21 MPa Show Material materials with Resistencia a la tracción of 21 MPa | T3 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 16 MPa Show Material materials with Resistencia a la tracción of 16 MPa | T3 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Resistencia al cizallamiento | 221.0 MPa Show Material materials with Resistencia al cizallamiento of 221.0 MPa | T3 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 860.0 J/(kg·K) Show Material materials with Calor específico of 860.0 J/(kg·K) | T3 | ||
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T3 | ||
20 °C | 2.2899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2899999999999998e-05 1/K | T3 | AA Standards, ASTM B210, ASTM B211 | |
100 °C | 2.2899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2899999999999998e-05 1/K | T3 | AA Standards, ASTM B210, ASTM B211 | |
Conductividad térmica | 150.0 W/(m·K) Show Material materials with Conductividad térmica of 150.0 W/(m·K) | T3 | ||
151.0 - 172.0 W/(m·K) Show Material materials with Conductividad térmica of 151.0 - 172.0 W/(m·K) | T3 | AA Standards, ASTM B210, ASTM B211 | ||
Temperatura de fusión | 540.0 - 645.0 °C Show Material materials with Temperatura de fusión of 540.0 - 645.0 °C | T3 | AA Standards, ASTM B210, ASTM B211 | |
540.0 °C Show Material materials with Temperatura de fusión of 540.0 °C | T3 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 23000000.0 - 26000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 26000000.0 S/m | T3 | AA Standards, ASTM B210, ASTM B211 | |
23000000 S/m Show Material materials with Conductividad eléctrica of 23000000 S/m | T3 | Typical/derived value | ||
Resistividad eléctrica | 3.85e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.85e-08 - 4.35e-08 Ω·m | T3 | AA Standards, ASTM B210, ASTM B211 | |
4.4e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.4e-08 Ω·m | T3 | Typical value | ||
Specific Electrical conductivity | 39.0 % IACS Show Material materials with Specific Electrical conductivity of 39.0 % IACS | T3 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 91.3 - 94.6 % Show Material materials with Aluminio of 91.3 - 94.6 % | T3 | |
Bismuto | 0.2 - 0.6 % Show Material materials with Bismuto of 0.2 - 0.6 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Cobre | 5.0 - 6.0 % Show Material materials with Cobre of 5.0 - 6.0 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T3 | AA Standards, ASTM B210, ASTM B211 |
0.7 % Show Material materials with Hierro of 0.7 % | T3 | ||
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T3 | |
Plomo | 0.2 - 0.6 % Show Material materials with Plomo of 0.2 - 0.6 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Zinc | 0.3 % Show Material materials with Zinc of 0.3 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Limited operational damage(T3, T4, T451), no damage during operation, limited damage during laboratory tests (T8), general: sufficient, in principle it should be protected | |
| General machinability | General: very good | |
| Workability | general (condition): poor(T3), acceptable (T4, T451), d (T8) | |