Propiedades
General
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Elongación | 14.0 % Show Material materials with Elongación of 14.0 % | T3 | AA Standards, ASTM B209 | A50 |
14.0 % Show Material materials with Elongación of 14.0 % | T3 | |||
Límite elástico | 240.0 MPa Show Material materials with Límite elástico of 240.0 MPa | T3 | AA Standards, ASTM B209 | RP02 |
250.0 MPa Show Material materials with Límite elástico of 250.0 MPa | T3 | AA Standards, ASTM B209 | RP02 | |
290.0 MPa Show Material materials with Límite elástico of 290.0 MPa | T3 | |||
Módulo de cizallamiento | 26.0 - 27.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Módulo elástico | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T3 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | 405.0 MPa Show Material materials with Resistencia a la tracción of 405.0 MPa | T3 | AA Standards, ASTM B209 | |
450.0 MPa Show Material materials with Resistencia a la tracción of 450.0 MPa | T3 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 870.0 J/(kg·K) Show Material materials with Calor específico of 870.0 J/(kg·K) | T3 | ||
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T3 | ||
20 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T3 | AA Standards, ASTM B209 | |
100 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T3 | AA Standards, ASTM B209 | |
Conductividad térmica | 134.0 - 193.0 W/(m·K) Show Material materials with Conductividad térmica of 134.0 - 193.0 W/(m·K) | T3 | AA Standards, ASTM B209 | |
150.0 W/(m·K) Show Material materials with Conductividad térmica of 150.0 W/(m·K) | T3 | |||
Temperatura de fusión | 505.0 - 635.0 °C Show Material materials with Temperatura de fusión of 505.0 - 635.0 °C | T3 | AA Standards, ASTM B209 | |
510.0 °C Show Material materials with Temperatura de fusión of 510.0 °C | T3 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 19700000 S/m Show Material materials with Conductividad eléctrica of 19700000 S/m | T3 | Typical/derived value | |
20000000.0 - 29000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 - 29000000.0 S/m | T3 | AA Standards, ASTM B209 | ||
Resistividad eléctrica | 3.45e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.45e-08 - 5e-08 Ω·m | T3 | AA Standards, ASTM B209 | |
5.0999999999999993e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.0999999999999993e-08 Ω·m | T3 | Typical value | ||
Specific Electrical conductivity | 34.0 % IACS Show Material materials with Specific Electrical conductivity of 34.0 % IACS | T3 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 90.4 - 95.0 % Show Material materials with Aluminio of 90.4 - 95.0 % | T3 | |
Circonio | 0.2 % Show Material materials with Circonio of 0.2 % | T3 | |
Cobre | 3.9 - 5.0 % Show Material materials with Cobre of 3.9 - 5.0 % | T3 | AA Standards, ASTM B209 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T3 | AA Standards, ASTM B209 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T3 | AA Standards, ASTM B209 |
0.7 % Show Material materials with Hierro of 0.7 % | T3 | ||
Magnesio | 0.2 - 0.8 % Show Material materials with Magnesio of 0.2 - 0.8 % | T3 | AA Standards, ASTM B209 |
Manganeso | 0.4 - 1.2 % Show Material materials with Manganeso of 0.4 - 1.2 % | T3 | AA Standards, ASTM B209 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T3 | |
Silicona | 0.5 - 1.2 % Show Material materials with Silicona of 0.5 - 1.2 % | T3 | AA Standards, ASTM B209 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T3 | AA Standards, ASTM B209 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T3 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511) | |