Propiedades
General
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | T651 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Dureza Brinell | 135.0 [-] Show Material materials with Dureza Brinell of 135.0 [-] | T651 | AA Standards | ||
Elongación | -195 °C | 14 % Show Material materials with Elongación of 14 % | T651 | Elongation in 50 mm | |
-80 °C | 13 % Show Material materials with Elongación of 13 % | T651 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongación of 1.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
3.0 % Show Material materials with Elongación of 3.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
5.0 % Show Material materials with Elongación of 5.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Elongación of 7.0 % | T651 | AA Standards, ASTM B211 | A100 | ||
7.0 % Show Material materials with Elongación of 7.0 % | T651 | AA Standards, ASTM B209 | A50 | ||
7.1 % Show Material materials with Elongación of 7.1 % | T651 | ||||
8.0 % Show Material materials with Elongación of 8.0 % | T651 | AA Standards, ASTM B211 | A50 | ||
11.0 % Show Material materials with Elongación of 11.0 % | T651 | AA Standards | A100 | ||
0 °C | 13 % Show Material materials with Elongación of 13 % | T651 | Elongation in 50 mm | ||
24 °C | 13 % Show Material materials with Elongación of 13 % | T651 | Elongation in 50 mm | ||
100 °C | 15 % Show Material materials with Elongación of 15 % | T651 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Elongación of 20 % | T651 | Elongation in 50 mm | ||
205 °C | 38 % Show Material materials with Elongación of 38 % | T651 | Elongation in 50 mm | ||
260 °C | 52 % Show Material materials with Elongación of 52 % | T651 | Elongation in 50 mm | ||
315 °C | 65 % Show Material materials with Elongación of 65 % | T651 | Elongation in 50 mm | ||
370 °C | 72 % Show Material materials with Elongación of 72 % | T651 | Elongation in 50 mm | ||
Límite elástico | 380.0 MPa Show Material materials with Límite elástico of 380.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211 | RP02 | |
395.0 MPa Show Material materials with Límite elástico of 395.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | ||
400.0 MPa Show Material materials with Límite elástico of 400.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | ||
405.0 MPa Show Material materials with Límite elástico of 405.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | ||
415.0 MPa Show Material materials with Límite elástico of 415.0 MPa | T651 | AA Standards | RP02 | ||
430.0 MPa Show Material materials with Límite elástico of 430.0 MPa | T651 | ||||
Módulo de cizallamiento | 28.0 GPa Show Material materials with Módulo de cizallamiento of 28.0 GPa | T651 | |||
Módulo elástico | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T651 | AA Standards, ASTM B209, ASTM B211 | ||
73 GPa Show Material materials with Módulo elástico of 73 GPa | T651 | ||||
Plane-Strain Fracture Toughnes | -196 °C | 28.5 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 28.5 MPa·√m | T651 | For plate in T-L direction | |
24 °C | 23.2 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 23.2 MPa·√m | T651 | For plate in T-L direction | ||
Resistencia a la tracción | -195 °C | 580 MPa Show Material materials with Resistencia a la tracción of 580 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 510 MPa Show Material materials with Resistencia a la tracción of 510 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
405.0 MPa Show Material materials with Resistencia a la tracción of 405.0 MPa | T651 | AA Standards, ASTM B209 | |||
435.0 MPa Show Material materials with Resistencia a la tracción of 435.0 MPa | T651 | AA Standards, ASTM B209 | |||
450.0 MPa Show Material materials with Resistencia a la tracción of 450.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211 | |||
460.0 MPa Show Material materials with Resistencia a la tracción of 460.0 MPa | T651 | AA Standards, ASTM B209 | |||
485.0 MPa Show Material materials with Resistencia a la tracción of 485.0 MPa | T651 | AA Standards | |||
490.0 MPa Show Material materials with Resistencia a la tracción of 490.0 MPa | T651 | ||||
0 °C | 495 MPa Show Material materials with Resistencia a la tracción of 495 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 483 MPa Show Material materials with Resistencia a la tracción of 483 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 435 MPa Show Material materials with Resistencia a la tracción of 435 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 275 MPa Show Material materials with Resistencia a la tracción of 275 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 66 MPa Show Material materials with Resistencia a la tracción of 66 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 45 MPa Show Material materials with Resistencia a la tracción of 45 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Resistencia a la tracción of 30 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 870.0 J/(kg·K) Show Material materials with Calor específico of 870.0 J/(kg·K) | T651 | ||
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T651 | ||
20 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211 | |
100 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211 | |
Conductividad térmica | 134.0 - 193.0 W/(m·K) Show Material materials with Conductividad térmica of 134.0 - 193.0 W/(m·K) | T651 | AA Standards, ASTM B209, ASTM B211 | |
150.0 W/(m·K) Show Material materials with Conductividad térmica of 150.0 W/(m·K) | T651 | |||
Temperatura de fusión | 505.0 - 635.0 °C Show Material materials with Temperatura de fusión of 505.0 - 635.0 °C | T651 | AA Standards, ASTM B209, ASTM B211 | |
510.0 °C Show Material materials with Temperatura de fusión of 510.0 °C | T651 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 20000000.0 - 29000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 - 29000000.0 S/m | T651 | AA Standards, ASTM B209, ASTM B211 | |
23000000 S/m Show Material materials with Conductividad eléctrica of 23000000 S/m | T651 | Typical/derived value | ||
Resistividad eléctrica | 3.45e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.45e-08 - 5e-08 Ω·m | T651 | AA Standards, ASTM B209, ASTM B211 | |
4.3e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.3e-08 Ω·m | T651 | Typical value | ||
Specific Electrical conductivity | 40.0 % IACS Show Material materials with Specific Electrical conductivity of 40.0 % IACS | T651 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 90.4 - 95.0 % Show Material materials with Aluminio of 90.4 - 95.0 % | T651 | |
Circonio | 0.2 % Show Material materials with Circonio of 0.2 % | T651 | |
Cobre | 3.9 - 5.0 % Show Material materials with Cobre of 3.9 - 5.0 % | T651 | AA Standards, ASTM B209, ASTM B211 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T651 | AA Standards, ASTM B209, ASTM B211 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T651 | AA Standards, ASTM B209, ASTM B211 |
0.7 % Show Material materials with Hierro of 0.7 % | T651 | ||
Magnesio | 0.2 - 0.8 % Show Material materials with Magnesio of 0.2 - 0.8 % | T651 | AA Standards, ASTM B209, ASTM B211 |
Manganeso | 0.4 - 1.2 % Show Material materials with Manganeso of 0.4 - 1.2 % | T651 | AA Standards, ASTM B209, ASTM B211 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T651 | |
Silicona | 0.5 - 1.2 % Show Material materials with Silicona of 0.5 - 1.2 % | T651 | AA Standards, ASTM B209, ASTM B211 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T651 | AA Standards, ASTM B209, ASTM B211 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T651 | AA Standards, ASTM B209, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511) | |