Propiedades
General
| Property | Value |
|---|---|
Densidad | 8.78 g/cm³ Show Supplier Material materials with Densidad of 8.78 g/cm³ |
Medidas
| Property | Value |
|---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Electroplated and Hot-dip tinned strip available. |
Mecánica
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.33 [-] | ||
Dureza Vickers | 200 - 240 [-] Show Supplier Material materials with Dureza Vickers of 200 - 240 [-] | R650(H) | For reference only | |
230 - 270 [-] Show Supplier Material materials with Dureza Vickers of 230 - 270 [-] | R750(EH) | For reference only | ||
250 - 300 [-] Show Supplier Material materials with Dureza Vickers of 250 - 300 [-] | R850(SH) | For reference only | ||
270 [-] Show Supplier Material materials with Dureza Vickers of 270 [-] | min. | R950(ESH) | For reference only | ||
290 [-] Show Supplier Material materials with Dureza Vickers of 290 [-] | min. | R1000(XSH) | For reference only | ||
Elongación | 1 % Show Supplier Material materials with Elongación of 1 % | min. | R950(ESH), A50 | |
5 % Show Supplier Material materials with Elongación of 5 % | min. | R850(SH), A50 | ||
9 % Show Supplier Material materials with Elongación of 9 % | min. | R750(EH), A50 | ||
11 % Show Supplier Material materials with Elongación of 11 % | min. | R650(H), A50 | ||
Límite elástico | 550 MPa Show Supplier Material materials with Límite elástico of 550 MPa | min. | R650(H) | |
650 MPa Show Supplier Material materials with Límite elástico of 650 MPa | min. | R750(EH) | ||
750 MPa Show Supplier Material materials with Límite elástico of 750 MPa | min. | R850(SH) | ||
870 MPa Show Supplier Material materials with Límite elástico of 870 MPa | min. | R950(ESH) | ||
930 MPa Show Supplier Material materials with Límite elástico of 930 MPa | min. | R1000(XSH) | ||
Módulo elástico | 110 GPa Show Supplier Material materials with Módulo elástico of 110 GPa | ||
Plegabilidad 180 ° bidireccional | 1.5 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 1.5 [-] | ASTM B820 | R650(H) | bending thickness: 0.06-0.5 mm & bending width: 10 mm |
2.5 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 2.5 [-] | ASTM B820 | R750(EH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
4 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 4 [-] | ASTM B820 | R850(SH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
Plegabilidad 180 ° en peso bruto | 1.5 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 1.5 [-] | ASTM B820 | R650(H) | bending thickness: 0.06-0.5 mm & bending width: 10 mm |
2 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 2 [-] | ASTM B820 | R750(EH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
3 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 3 [-] | ASTM B820 | R850(SH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
Plegabilidad 90 ° bidireccional | 1 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1 [-] | EN ISO 7438 | R650(H) | bending thickness: 0.06-0.5 mm & bending width: 10 mm |
2 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 2 [-] | EN ISO 7438 | R750(EH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
2.5 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 2.5 [-] | EN ISO 7438 | R850(SH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
Plegabilidad 90 ° en peso bruto | 1 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1 [-] | EN ISO 7438 | R650(H) | bending thickness: 0.06-0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1.5 [-] | EN ISO 7438 | R750(EH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 2 [-] | EN ISO 7438 | R850(SH) | bending thickness: 0.06-0.5 mm & bending width: 10 mm | |
Resistencia a la tracción | 650 - 750 MPa Show Supplier Material materials with Resistencia a la tracción of 650 - 750 MPa | R650(H) | |
750 - 850 MPa Show Supplier Material materials with Resistencia a la tracción of 750 - 850 MPa | R750(EH) | ||
850 - 950 MPa Show Supplier Material materials with Resistencia a la tracción of 850 - 950 MPa | R850(SH) |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 375 J/(kg·K) Show Supplier Material materials with Calor específico of 375 J/(kg·K) | ||
Coeficiente de dilatación térmica | 1.84e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.84e-05 1/K | average value between 20-300°C | |
Conductividad térmica | 20 °C | 50 W/(m·K) Show Supplier Material materials with Conductividad térmica of 50 W/(m·K) |
Eléctrico
Chemical properties
| Property | Value |
|---|---|
Cobre | Balance |
Estaño | 10 % Show Supplier Material materials with Estaño of 10 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Application target: Ideal for BTB connector, audio jack and other miniaturized connectors | |
| Chemical composition | The chemical composition is the nominal composition of the alloy | |
| Coating | Electroplating: Very good Hot dip tinning: Very good | |
| Cold Forming | Very good | |
| Machining | Not suitable | |
| Packaging size | Standard coils with outside diameters up to 1300 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons. | |
| Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
| Welding | Good | |