General
Property | Value |
---|---|
Densidad | 8.9 g/cm³ Show Supplier Material materials with Densidad of 8.9 g/cm³ |
Medidas
Property | Value |
---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Hot-dip tinned and electroplated strip available. |
Mecánica
Property | Value | Testing Standard | Comment |
---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.33 [-] | ||
Dureza Vickers | 115 - 135 [-] Show Supplier Material materials with Dureza Vickers of 115 - 135 [-] | R360(3/4H) | For reference only | |
120 - 140 [-] Show Supplier Material materials with Dureza Vickers of 120 - 140 [-] | R385(H) | For reference only. | ||
125 - 145 [-] Show Supplier Material materials with Dureza Vickers of 125 - 145 [-] | R415(EH) | For reference only | ||
130 - 150 [-] Show Supplier Material materials with Dureza Vickers of 130 - 150 [-] | R440(SH) | For reference only | ||
Elongación | 1 % Show Supplier Material materials with Elongación of 1 % | min. | R440(SH), A50 | |
2 % Show Supplier Material materials with Elongación of 2 % | min. | R415(EH), A50 | ||
3 % Show Supplier Material materials with Elongación of 3 % | min. | R385(H), A50 | ||
4 % Show Supplier Material materials with Elongación of 4 % | min. | R360(3/4H), A50 | ||
Límite elástico | 345 MPa Show Supplier Material materials with Límite elástico of 345 MPa | min. | R360(3/4H) | |
355 MPa Show Supplier Material materials with Límite elástico of 355 MPa | min. | R385(H) | ||
400 MPa Show Supplier Material materials with Límite elástico of 400 MPa | min. | R415(EH) | ||
425 MPa Show Supplier Material materials with Límite elástico of 425 MPa | min. | R440(SH) | ||
Módulo elástico | 125 GPa Show Supplier Material materials with Módulo elástico of 125 GPa | ||
Plegabilidad 180 ° bidireccional | 1.5 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 1.5 [-] | ASTM B820 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 1.5 [-] | ASTM B820 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 2 [-] | ASTM B820 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 2 [-] | ASTM B820 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Plegabilidad 180 ° en peso bruto | 1 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 1 [-] | ASTM B820 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 1.5 [-] | ASTM B820 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 1.5 [-] | ASTM B820 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 2 [-] | ASTM B820 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Plegabilidad 90 ° bidireccional | 1 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1 [-] | EN ISO 7438 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1 [-] | EN ISO 7438 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1.5 [-] | EN ISO 7438 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 2 [-] | EN ISO 7438 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Plegabilidad 90 ° en peso bruto | 0.5 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0.5 [-] | EN ISO 7438 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1 [-] | EN ISO 7438 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1.5 [-] | EN ISO 7438 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1.5 [-] | EN ISO 7438 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Resistencia a la tracción | 360 - 425 MPa Show Supplier Material materials with Resistencia a la tracción of 360 - 425 MPa | R360(3/4H) | |
385 - 455 MPa Show Supplier Material materials with Resistencia a la tracción of 385 - 455 MPa | R385(H) | ||
415 - 480 MPa Show Supplier Material materials with Resistencia a la tracción of 415 - 480 MPa | R415(EH) | ||
440 - 510 MPa Show Supplier Material materials with Resistencia a la tracción of 440 - 510 MPa | R440(SH) |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 385 J/(kg·K) Show Supplier Material materials with Calor específico of 385 J/(kg·K) | ||
Coeficiente de dilatación térmica | 1.7e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.7e-05 1/K | average value between 20-300°C | |
Conductividad térmica | 20 °C | 350 W/(m·K) Show Supplier Material materials with Conductividad térmica of 350 W/(m·K) |
Eléctrico
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | Application target: Ideal for semiconductor. | |
Chemical composition | The chemical composition is the nominal composition of the alloy | |
Coating | Electroplating: Good Hot dip tinning: Very good | |
Cold Forming | Good | |
Machining | Fair | |
Packaging size | Standard coils with outside diameters up to 1300 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons. | |
Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
Welding | Laser welding: Average Resistance welding: Good |