Propiedades
General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 0.2 % Show Supplier Material materials with Absorción de agua of 0.2 % | 2 mm | ISO 62 | 24h immersion at 23°C | ||
Densidad | 1.44 g/cm³ Show Supplier Material materials with Densidad of 1.44 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 1.5 % Show Supplier Material materials with Moisture absorption of 1.5 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 1.6 % Show Supplier Material materials with Elongación of 1.6 % | dry | ISO 527-2/1A | 5mm/min | |
1.7 % Show Supplier Material materials with Elongación of 1.7 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 10.2 GPa Show Supplier Material materials with Módulo de flexión of 10.2 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 11.6 GPa Show Supplier Material materials with Módulo elástico of 11.6 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
11.7 GPa Show Supplier Material materials with Módulo elástico of 11.7 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 250 MPa Show Supplier Material materials with Resistencia a la flexión of 250 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 145 MPa Show Supplier Material materials with Resistencia a la tracción of 145 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
160 MPa Show Supplier Material materials with Resistencia a la tracción of 160 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | dry | ISO 179/1eA | |
23 °C | 7.5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7.5 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 45 kJ/m² | dry | ISO 179/1eU | |
23 °C | 50 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | dry | ISO 179/1eU |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Temperatura de flexión bajo carga | 290 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 290 °C | ISO 75/2Af | 1.80 MPa | ||
Temperatura de fusión | 325 °C Show Supplier Material materials with Temperatura de fusión of 325 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | ||||
Eléctrico
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Contracción | 0.3 % Show Supplier Material materials with Contracción of 0.3 % | 330/140/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.8 % Show Supplier Material materials with Contracción of 0.8 % | 330/140/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE, Food and Water Contact (please get in touch with Radici Group): KTW guidlines and DVGW-standard W270 (11/2007), ACS positive lists include the circular DGC/VS4 n°2000/232 dated 27 april 2000 | |
| Color | Black | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Injection Molding | |