Propiedades
General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 1.1 % Show Supplier Material materials with Absorción de agua of 1.1 % | 2 mm | ISO 62 | 24h immersion at 23°C | ||
2 % Show Supplier Material materials with Absorción de agua of 2 % | ISO 62 | 1mm | ||||
Densidad | 1.42 g/cm³ Show Supplier Material materials with Densidad of 1.42 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 3 % Show Supplier Material materials with Elongación of 3 % | dry | ISO 527-2/1A | 5mm/min | |
Módulo de flexión | 11 GPa Show Supplier Material materials with Módulo de flexión of 11 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 11.5 GPa Show Supplier Material materials with Módulo elástico of 11.5 GPa | dry | ISO 527-2/1A | 1mm/min | |
Resistencia a la flexión | 310 MPa Show Supplier Material materials with Resistencia a la flexión of 310 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 210 MPa Show Supplier Material materials with Resistencia a la tracción of 210 MPa | dry | ISO 527-2/1A | 5mm/min | |
Resistencia al choque, ensayo Charpy entallado | 23 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | dry | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 79 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 79 kJ/m² | dry | ISO 179/1eU | 23°C | |
Resistencia al choque, ensayo Izod no entallado | 23 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 14 kJ/m² | dry | ISO 180/1U |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Temperatura de flexión bajo carga | 250 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 250 °C | ISO 75/2Af | 1.80 MPa | ||
260 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 260 °C | ISO 75/2Bf | 0.45 MPa | |||
Temperatura de fusión | 261 °C Show Supplier Material materials with Temperatura de fusión of 261 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <100,method: ISO 3795 and thickness tested (mm): 2 | ||||
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 35% Glass Fiber | |
| Processing methods | Injection Molding | |