Propiedades
General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 4 % Show Supplier Material materials with Absorción de agua of 4 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.58 g/cm³ Show Supplier Material materials with Densidad of 1.58 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 1.1 % Show Supplier Material materials with Moisture absorption of 1.1 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 3 % Show Supplier Material materials with Elongación of 3 % | dry | ISO 527-2/1A | 5mm/min | |
3.1 % Show Supplier Material materials with Elongación of 3.1 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 15.4 GPa Show Supplier Material materials with Módulo de flexión of 15.4 GPa | 50%RH | ISO 178 | 2mm/min | |
15.5 GPa Show Supplier Material materials with Módulo de flexión of 15.5 GPa | dry | ISO 178 | 2mm/min | ||
Módulo elástico | 14.2 GPa Show Supplier Material materials with Módulo elástico of 14.2 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
17 GPa Show Supplier Material materials with Módulo elástico of 17 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 305 MPa Show Supplier Material materials with Resistencia a la flexión of 305 MPa | 50%RH | ISO 178 | 2mm/min | |
375 MPa Show Supplier Material materials with Resistencia a la flexión of 375 MPa | dry | ISO 178 | 2mm/min | ||
Resistencia a la tracción | 190 MPa Show Supplier Material materials with Resistencia a la tracción of 190 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
245 MPa Show Supplier Material materials with Resistencia a la tracción of 245 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 16 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 16 kJ/m² | dry | ISO 179/1eA | |
23 °C | 18 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 18 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 25 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 25 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 102 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 102 kJ/m² | dry | ISO 179/1eU | |
23 °C | 100 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 112 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 112 kJ/m² | 50%RH | ISO 179/1eU |
Aplicaciones térmicas
| Property | Temperature | Value | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 1.5e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.5e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||
8.5e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.5e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||
Conductividad térmica | 23 °C | 0.37 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.37 W/(m·K) | |||
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 1 mm, 2 mm | ||
Glow Wire Ignition Temperature | 725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | IEC 60695-2-13 | 1 mm, 2 mm | ||
Temperatura de flexión bajo carga | 215 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 215 °C | ISO 75/2Af | 8.00 MPa | ||
250 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 250 °C | ISO 75/2Af | 1.80 MPa | |||
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 10°C/min | ||
Temperatura de reblandecimiento Vicat | 255 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 255 °C | ISO 306 | 50°C/h 50N |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Contracción | 0.2 % Show Supplier Material materials with Contracción of 0.2 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.7 % Show Supplier Material materials with Contracción of 0.7 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse | |
Velocidad de flujo de la masa derretida | 8.2 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 8.2 g/10min | ISO 1133 | 275°C/5Kg | |
Viscosity number | 152 cm³/gr Show Supplier Material materials with Viscosity number of 152 cm³/gr | ISO 307 | Sulfuric acid |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Deep black | |
| Features | Heat Stabilized | |
| Fillers | 50% Glass Fiber | |
| Processing methods | Injection Molding | |