General
Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
---|---|---|---|---|---|---|
Absorción de agua | 5.5 % Show Supplier Material materials with Absorción de agua of 5.5 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.06 g/cm³ Show Supplier Material materials with Densidad of 1.06 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 1.6 % Show Supplier Material materials with Moisture absorption of 1.6 % | 2 mm | ISO 62 | 50%RH |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elongación | 100 % Show Supplier Material materials with Elongación of 100 % | dry, 50%RH | ISO 527-2/1A | min. | 50mm/min | nominal | |
Elongation at yield | 4.5 % Show Supplier Material materials with Elongation at yield of 4.5 % | dry | ISO 527-2/1A | 50mm/min | |
Límite elástico | 35 MPa Show Supplier Material materials with Límite elástico of 35 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
42 MPa Show Supplier Material materials with Límite elástico of 42 MPa | dry | ISO 527-2/1A | 50mm/min | ||
Módulo de flexión | 0.75 GPa Show Supplier Material materials with Módulo de flexión of 0.75 GPa | 50%RH | ISO 178 | 2mm/min | |
1.6 GPa Show Supplier Material materials with Módulo de flexión of 1.6 GPa | dry | ISO 178 | 2mm/min | ||
Módulo elástico | 0.85 GPa Show Supplier Material materials with Módulo elástico of 0.85 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
1.7 GPa Show Supplier Material materials with Módulo elástico of 1.7 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 40 MPa Show Supplier Material materials with Resistencia a la flexión of 40 MPa | 50%RH | ISO 178 | 2mm/min | |
60 MPa Show Supplier Material materials with Resistencia a la flexión of 60 MPa | dry | ISO 178 | 2mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 25 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 25 kJ/m² | dry | ISO 179/1eA | |
23 °C | 105 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 105 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 120 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 120 kJ/m² | 50%RH | ISO 179/1eA |
Aplicaciones térmicas
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Temperatura de flexión bajo carga | 55 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 55 °C | ISO 75/2Af | 1.80 MPa | ||
Temperatura de fusión | 220 °C Show Supplier Material materials with Temperatura de fusión of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 1.6, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 |
Eléctrico
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Contracción | 1.1 % Show Supplier Material materials with Contracción of 1.1 % | 280/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
1.4 % Show Supplier Material materials with Contracción of 1.4 % | 280/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] | |
Velocidad de flujo de la masa derretida | 2 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 2 g/10min | ISO 1133 | 275°C/5Kg |
Technological properties
Property | ||
---|---|---|
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | Impact Modified, Heat Stabilized | |
Processing methods | Injection Molding,Blow Molding |