Propiedades
General
| Property | Temperature | Value | Condition | Testing Standard | Thickness |
|---|---|---|---|---|---|
Densidad | 1.39 g/cm³ Show Supplier Material materials with Densidad of 1.39 g/cm³ | dry | ISO 1183 | ||
Moisture absorption | 23 °C | 1.2 % Show Supplier Material materials with Moisture absorption of 1.2 % | 50%RH | ISO 62 | 2 mm |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 3.1 % Show Supplier Material materials with Elongación of 3.1 % | dry | ISO 527-2/1A | 5mm/min | |
Módulo de flexión | 10 GPa Show Supplier Material materials with Módulo de flexión of 10 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 12.1 GPa Show Supplier Material materials with Módulo elástico of 12.1 GPa | dry | ISO 527-2/1A | 1mm/min | |
Resistencia a la flexión | 300 MPa Show Supplier Material materials with Resistencia a la flexión of 300 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 194 MPa Show Supplier Material materials with Resistencia a la tracción of 194 MPa | dry | ISO 527-2/1A | 5mm/min | |
Resistencia al choque, ensayo Charpy entallado | -30 °C | 12.5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 12.5 kJ/m² | dry | ISO 179/1eA | |
23 °C | 15 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 15 kJ/m² | dry | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | 70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | dry | ISO 179/1eU | -30°C | |
101 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 101 kJ/m² | dry | ISO 179/1eU | 23°C |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Temperatura de flexión bajo carga | 252 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 252 °C | ISO 75/2Bf | 0.45 MPa | ||
Temperatura de fusión | 295 °C Show Supplier Material materials with Temperatura de fusión of 295 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Eléctrico
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 35% Glass Fiber | |
| Processing methods | Injection Molding | |