General
Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
---|---|---|---|---|---|---|
Absorción de agua | 3.7 % Show Supplier Material materials with Absorción de agua of 3.7 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.68 g/cm³ Show Supplier Material materials with Densidad of 1.68 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 0.9 % Show Supplier Material materials with Moisture absorption of 0.9 % | 2 mm | ISO 62 | 50%RH |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elongación | 2 % Show Supplier Material materials with Elongación of 2 % | dry | ISO 527-2/1A | 5mm/min | |
2.2 % Show Supplier Material materials with Elongación of 2.2 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 8 GPa Show Supplier Material materials with Módulo de flexión of 8 GPa | 50%RH | ISO 178 | 2mm/min | |
11 GPa Show Supplier Material materials with Módulo de flexión of 11 GPa | dry | ISO 178 | 2mm/min | ||
Módulo elástico | 9.5 GPa Show Supplier Material materials with Módulo elástico of 9.5 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
12.2 GPa Show Supplier Material materials with Módulo elástico of 12.2 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 160 MPa Show Supplier Material materials with Resistencia a la flexión of 160 MPa | 50%RH | ISO 178 | 2mm/min | |
220 MPa Show Supplier Material materials with Resistencia a la flexión of 220 MPa | dry | ISO 178 | 2mm/min | ||
Resistencia a la tracción | 100 MPa Show Supplier Material materials with Resistencia a la tracción of 100 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
150 MPa Show Supplier Material materials with Resistencia a la tracción of 150 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | dry | ISO 179/1eA | |
23 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 11 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 42 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 42 kJ/m² | dry | ISO 179/1eU | |
23 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 45 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 52 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 52 kJ/m² | 50%RH | ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Temperatura de flexión bajo carga | 220 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 220 °C | ISO 75/2Af | 1.80 MPa | ||||
240 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 240 °C | ISO 75/2Bf | 0.45 MPa | |||||
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Temperatura de reblandecimiento Vicat | 240 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 240 °C | ISO 306 | 50°C/h 50N | ||||
Inflamabilidad | Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Eléctrico
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Contracción | 0.3 % Show Supplier Material materials with Contracción of 0.3 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.8 % Show Supplier Material materials with Contracción of 0.8 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent, Flame retarding agent | |
Certifications | Yellow Card, RoHS 2011/65/UE | |
Color | Natural | |
Features | Flame Retardant, Heat Stabilized | |
Fillers | 30% Glass Fiber | |
Processing methods | Injection Molding |