General
Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
---|---|---|---|---|---|---|
Absorción de agua | 7.6 % Show Supplier Material materials with Absorción de agua of 7.6 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.34 g/cm³ Show Supplier Material materials with Densidad of 1.34 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | 2 mm | ISO 62 | 50%RH |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elongación | 20 % Show Supplier Material materials with Elongación of 20 % | dry | ISO 527-2/1A | 5mm/min | |
Módulo de flexión | 3.9 GPa Show Supplier Material materials with Módulo de flexión of 3.9 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 3.8 GPa Show Supplier Material materials with Módulo elástico of 3.8 GPa | dry | ISO 527-2/1A | 1mm/min | |
Resistencia a la flexión | 122 MPa Show Supplier Material materials with Resistencia a la flexión of 122 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 72 MPa Show Supplier Material materials with Resistencia a la tracción of 72 MPa | dry | ISO 527-2/1A | 5mm/min | |
Resistencia al choque, ensayo Charpy entallado | 23 °C | 4 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | dry, 50%RH | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23 °C | 25 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 25 kJ/m² | dry | ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Testing Standard | Thickness | Comment | |||
---|---|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 7.5e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 7.5e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||||
7.5e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 7.5e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||||
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 2 mm | ||||
Temperatura de flexión bajo carga | 70 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 70 °C | ISO 75/2Af | 1.80 MPa | ||||
200 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 200 °C | ISO 75/2Bf | 0.45 MPa | |||||
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Temperatura de reblandecimiento Vicat | 225 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 225 °C | ISO 306 | 50°C/h 50N | ||||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Eléctrico
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Contracción | 1.1 % Show Supplier Material materials with Contracción of 1.1 % | 290/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1.2 % Show Supplier Material materials with Contracción of 1.2 % | 290/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Deep black | |
Fillers | 30% Glass Bead | |
Processing methods | Injection Molding |