General
Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
---|---|---|---|---|---|---|
Absorción de agua | 7.9 % Show Supplier Material materials with Absorción de agua of 7.9 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.23 g/cm³ Show Supplier Material materials with Densidad of 1.23 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 2.3 % Show Supplier Material materials with Moisture absorption of 2.3 % | 2 mm | ISO 62 | 50%RH |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elongación | 4.2 % Show Supplier Material materials with Elongación of 4.2 % | dry | ISO 527-2/1A | 5mm/min | |
Módulo de flexión | 5 GPa Show Supplier Material materials with Módulo de flexión of 5 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 5.6 GPa Show Supplier Material materials with Módulo elástico of 5.6 GPa | dry | ISO 527-2/1A | 1mm/min | |
Resistencia a la flexión | 185 MPa Show Supplier Material materials with Resistencia a la flexión of 185 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 120 MPa Show Supplier Material materials with Resistencia a la tracción of 120 MPa | dry | ISO 527-2/1A | 5mm/min | |
Resistencia al choque, ensayo Charpy entallado | 23 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | dry | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 45 kJ/m² | dry | ISO 179/1eU | |
23 °C | 70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | dry | ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Testing Standard | Comment |
---|---|---|---|
Temperatura de flexión bajo carga | 226 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 226 °C | ISO 75/2Af | 1.80 MPa |
240 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 240 °C | ISO 75/2Bf | 0.45 MPa | |
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | 10°C/min |
Temperatura de reblandecimiento Vicat | 245 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 245 °C | ISO 306 | 3mm |
Eléctrico
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Contracción | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.8 % Show Supplier Material materials with Contracción of 0.8 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse | |
Velocidad de flujo de la masa derretida | 27 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 27 g/10min | ISO 1133 | 275°C/3.25Kg | |
Viscosity number | 140 cm³/gr Show Supplier Material materials with Viscosity number of 140 cm³/gr | ISO 307 | Sulfuric acid |
Technological properties
Property | ||
---|---|---|
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Fillers | 15% Glass Fiber | |
Processing methods | Injection Molding |