General
Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
---|---|---|---|---|---|---|
Absorción de agua | 1.5 % Show Supplier Material materials with Absorción de agua of 1.5 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.13 g/cm³ Show Supplier Material materials with Densidad of 1.13 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 0.7 % Show Supplier Material materials with Moisture absorption of 0.7 % | 2 mm | ISO 62 | 50%RH |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elongación | 70 % Show Supplier Material materials with Elongación of 70 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
100 % Show Supplier Material materials with Elongación of 100 % | 50%RH | ISO 527-2/1A | min. | 50mm/min | nominal | ||
Elongation at yield | 40 % Show Supplier Material materials with Elongation at yield of 40 % | dry | ISO 527-2/1A | 50mm/min | |
Límite elástico | 28 MPa Show Supplier Material materials with Límite elástico of 28 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
38 MPa Show Supplier Material materials with Límite elástico of 38 MPa | dry | ISO 527-2/1A | 50mm/min | ||
Módulo de flexión | 1.1 GPa Show Supplier Material materials with Módulo de flexión of 1.1 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 0.68 GPa Show Supplier Material materials with Módulo elástico of 0.68 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
1.1 GPa Show Supplier Material materials with Módulo elástico of 1.1 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 34 MPa Show Supplier Material materials with Resistencia a la flexión of 34 MPa | dry | ISO 178 | 2mm/min | |
Resistencia al choque, ensayo Charpy entallado | 23 °C | 70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 70 kJ/m² | dry | ISO 179/1eA |
Aplicaciones térmicas
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 0.000168 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.000168 1/K | ISO 11359-1/-2 | 23°C-55°C | ||
0.000169 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.000169 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||
Temperatura de flexión bajo carga | 50 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 50 °C | ISO 75/2Af | 1.80 MPa | ||
Temperatura de fusión | 217 °C Show Supplier Material materials with Temperatura de fusión of 217 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 |
Eléctrico
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 100000 Ω/sq Show Supplier Material materials with Surface resistivity of 100000 Ω/sq | dry, 50%RH | IEC 60093 | 500V |
Volume resistivity | 1e+07 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+07 Ω·cm | dry, 50%RH | IEC 60093 | 500V |
Technological properties
Property | ||
---|---|---|
Additives | Plasticizer | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | Eletrically Dissipative, Increased Electrical Conductivity, Anti-Static Modified, Impact Modified, Heat Stabilized | |
Processing methods | Injection Molding,Profile Extrusion |