Propiedades
General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 2.2 % Show Supplier Material materials with Absorción de agua of 2.2 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.26 g/cm³ Show Supplier Material materials with Densidad of 1.26 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 1 % Show Supplier Material materials with Moisture absorption of 1 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 5 % Show Supplier Material materials with Elongación of 5 % | dry | ISO 527-2/1A | 5mm/min | |
8 % Show Supplier Material materials with Elongación of 8 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 4.5 GPa Show Supplier Material materials with Módulo de flexión of 4.5 GPa | 50%RH | ISO 178 | 2mm/min | |
6.2 GPa Show Supplier Material materials with Módulo de flexión of 6.2 GPa | dry | ISO 178 | 2mm/min | ||
Módulo elástico | 5.1 GPa Show Supplier Material materials with Módulo elástico of 5.1 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
7 GPa Show Supplier Material materials with Módulo elástico of 7 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 140 MPa Show Supplier Material materials with Resistencia a la flexión of 140 MPa | 50%RH | ISO 178 | 2mm/min | |
180 MPa Show Supplier Material materials with Resistencia a la flexión of 180 MPa | dry | ISO 178 | 2mm/min | ||
Resistencia a la tracción | 90 MPa Show Supplier Material materials with Resistencia a la tracción of 90 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
115 MPa Show Supplier Material materials with Resistencia a la tracción of 115 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | dry | ISO 179/1eA | |
23 °C | 30 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 30 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 40 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 85 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 85 kJ/m² | dry | ISO 179/1eU | |
23 °C | 100 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 105 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 105 kJ/m² | 50%RH | ISO 179/1eU |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Temperatura de flexión bajo carga | 195 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 195 °C | ISO 75/2Af | 1.80 MPa | ||
Temperatura de fusión | 220 °C Show Supplier Material materials with Temperatura de fusión of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | ||||
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Impact Modified, Heat Stabilized | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Injection Molding | |