Propiedades
General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 8.5 % Show Supplier Material materials with Absorción de agua of 8.5 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.23 g/cm³ Show Supplier Material materials with Densidad of 1.23 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 2.5 % Show Supplier Material materials with Moisture absorption of 2.5 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 4.5 % Show Supplier Material materials with Elongación of 4.5 % | dry | ISO 527-2/1A | 5mm/min | |
12 % Show Supplier Material materials with Elongación of 12 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 4.9 GPa Show Supplier Material materials with Módulo de flexión of 4.9 GPa | dry | ISO 178 | 2mm/min | |
Módulo elástico | 3.8 GPa Show Supplier Material materials with Módulo elástico of 3.8 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
5.7 GPa Show Supplier Material materials with Módulo elástico of 5.7 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 190 MPa Show Supplier Material materials with Resistencia a la flexión of 190 MPa | dry | ISO 178 | 2mm/min | |
Resistencia a la tracción | 80 MPa Show Supplier Material materials with Resistencia a la tracción of 80 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
130 MPa Show Supplier Material materials with Resistencia a la tracción of 130 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 5.5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 5.5 kJ/m² | dry | ISO 179/1eA | |
23 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 40 kJ/m² | dry | ISO 179/1eU | -30°C | |
50 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | dry | ISO 179/1eU | 23°C | ||
70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | 50%RH | ISO 179/1eU | 23°C |
Aplicaciones térmicas
| Property | Value | Testing Standard | Thickness | Comment | |||
|---|---|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 3e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||||
7e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 7e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||||
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 2 mm | ||||
Temperatura de flexión bajo carga | 190 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 190 °C | ISO 75/2Af | 1.80 MPa | ||||
Temperatura de fusión | 220 °C Show Supplier Material materials with Temperatura de fusión of 220 °C | ISO 11357-1/-3 | 10°C/min | ||||
Temperatura de reblandecimiento Vicat | 205 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 205 °C | ISO 306 | 50°C/h 50N | ||||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Eléctrico
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V | |
Índice de seguimiento comparativo | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | dry | IEC 60112 | Sol.A |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Contracción | 0.4 % Show Supplier Material materials with Contracción of 0.4 % | 280/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1.1 % Show Supplier Material materials with Contracción of 1.1 % | 280/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Natural | |
| Fillers | 15% Glass Fiber | |
| Processing methods | Injection Molding | |