Propiedades
General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 0.3 % Show Supplier Material materials with Absorción de agua of 0.3 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.53 g/cm³ Show Supplier Material materials with Densidad of 1.53 g/cm³ | ISO 1183 | ||||
Moisture absorption | 23 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elongación | 2.5 % Show Supplier Material materials with Elongación of 2.5 % | ISO 527-2/1A | 5mm/min | |
Módulo de flexión | 9.2 GPa Show Supplier Material materials with Módulo de flexión of 9.2 GPa | ISO 178 | 2mm/min | |
Módulo elástico | 10 GPa Show Supplier Material materials with Módulo elástico of 10 GPa | ISO 527-2/1A | 1mm/min | |
Resistencia a la flexión | 220 MPa Show Supplier Material materials with Resistencia a la flexión of 220 MPa | ISO 178 | 2mm/min | |
Resistencia a la tracción | 145 MPa Show Supplier Material materials with Resistencia a la tracción of 145 MPa | ISO 527-2/1A | 5mm/min | |
Resistencia al choque, ensayo Charpy entallado | 23 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23 °C | 55 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 55 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 2.5e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.5e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||
9e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||
Temperatura de flexión bajo carga | 205 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 205 °C | ISO 75/2Af | 1.80 MPa | ||
220 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 220 °C | ISO 75/2Bf | 0.45 MPa | |||
Temperatura de fusión | 225 °C Show Supplier Material materials with Temperatura de fusión of 225 °C | ISO 11357-1/-3 | 10°C/min | ||
Temperatura de reblandecimiento Vicat | 210 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 210 °C | ISO 306 | 50°C/h 50N | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | ||||
Eléctrico
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Contracción | 0.3 % Show Supplier Material materials with Contracción of 0.3 % | 280/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1 % Show Supplier Material materials with Contracción of 1 % | 280/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | DPPD Free | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Injection Molding | |