Propiedades
General
| Property | Temperature | Value | Thickness | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|---|
Absorción de agua | 7 % Show Supplier Material materials with Absorción de agua of 7 % | 2 mm | ISO 62 | immersion at 23°C | ||
Densidad | 1.37 g/cm³ Show Supplier Material materials with Densidad of 1.37 g/cm³ | ISO 1183 | dry | |||
Moisture absorption | 23 °C | 2 % Show Supplier Material materials with Moisture absorption of 2 % | 2 mm | ISO 62 | 50%RH |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elongación | 2.6 % Show Supplier Material materials with Elongación of 2.6 % | dry | ISO 527-2/1A | 5mm/min | |
3.6 % Show Supplier Material materials with Elongación of 3.6 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Módulo de flexión | 4.7 GPa Show Supplier Material materials with Módulo de flexión of 4.7 GPa | 50%RH | ISO 178 | 2mm/min | |
8.4 GPa Show Supplier Material materials with Módulo de flexión of 8.4 GPa | dry | ISO 178 | 2mm/min | ||
Módulo elástico | 5.4 GPa Show Supplier Material materials with Módulo elástico of 5.4 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
9.3 GPa Show Supplier Material materials with Módulo elástico of 9.3 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Resistencia a la flexión | 135 MPa Show Supplier Material materials with Resistencia a la flexión of 135 MPa | 50%RH | ISO 178 | 2mm/min | |
210 MPa Show Supplier Material materials with Resistencia a la flexión of 210 MPa | dry | ISO 178 | 2mm/min | ||
Resistencia a la tracción | 85 MPa Show Supplier Material materials with Resistencia a la tracción of 85 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
135 MPa Show Supplier Material materials with Resistencia a la tracción of 135 MPa | dry | ISO 527-2/1A | 5mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | dry | ISO 179/1eA | |
23 °C | 12 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | 50%RH | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | 55 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 55 kJ/m² | dry | ISO 179/1eU | 23°C | |
70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 70 kJ/m² | 50%RH | ISO 179/1eU | 23°C |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Temperatura de flexión bajo carga | 190 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 190 °C | ISO 75/2Af | 1.80 MPa | ||
215 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 215 °C | ISO 75/2Bf | 0.45 MPa | |||
Temperatura de fusión | 220 °C Show Supplier Material materials with Temperatura de fusión of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Inflamabilidad | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | ||||
Eléctrico
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Injection Molding | |