Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.09 % Show Supplier Material materials with Absorción de agua of 0.09 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.54 g/cm³ Show Supplier Material materials with Densidad of 1.54 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.54 [-] Show Supplier Material materials with Densidad relativa of 1.54 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.6 % Show Supplier Material materials with Elongación of 1.6 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 83 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 83 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 770 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 770 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 9.1 GPa Show Supplier Material materials with Módulo de flexión of 9.1 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 10.7 GPa Show Supplier Material materials with Módulo elástico of 10.7 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 210 MPa Show Supplier Material materials with Resistencia a la flexión of 210 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 139 MPa Show Supplier Material materials with Resistencia a la tracción of 139 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Ball pressure temperature | 200 °C Show Supplier Material materials with Ball pressure temperature of 200 °C | IEC 60695-10-2 | approximate maximum | |
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 8.9E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 217 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 217 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 203 - 217 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 203 - 217 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
High Volt Arc Track Rate | 23.0 °C | 2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code | UL 746A | (PLC) |
Rigidez dieléctrica | 23.0 °C | 23 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 23 kV/mm | ASTM D 149 | in air, 3.2 mm |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, ASTM D 257 |
Índice de seguimiento comparativo | 23.0 °C | 2 V Show Supplier Material materials with Índice de seguimiento comparativo of 2 V | UL 746A | (UL) {PLC} |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.8 % Show Supplier Material materials with Contracción transversal of 0.8 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 52 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 52 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 38 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 38 cm³/10min | ISO 1133 | MVR at 250°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Small Appliance, Personal Care | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |