General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Supplier Material materials with Absorción de agua of 0.2 % | ISO 62 |
Densidad | 23.0 °C | 1.55 g/cm³ Show Supplier Material materials with Densidad of 1.55 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2 % Show Supplier Material materials with Elongación of 2 % | ISO 527 |
Módulo de flexión | 23.0 °C | 12 GPa Show Supplier Material materials with Módulo de flexión of 12 GPa | ISO 178 |
Resistencia a la flexión | 23.0 °C | 270 MPa Show Supplier Material materials with Resistencia a la flexión of 270 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 190 MPa Show Supplier Material materials with Resistencia a la tracción of 190 MPa | ISO 527 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179 |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75 | |
Temperatura de fusión | 280 °C Show Supplier Material materials with Temperatura de fusión of 280 °C | ISO 11357 (10°C/min) | |
Temperatura máx. de funcionamiento | 250 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 250 °C | ||
Inflamabilidad | HB, UL-94 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 4 [-] Show Supplier Material materials with Constante dieléctrica of 4 [-] | IEC 60250 |
Factor de disipación | 23.0 °C | 3E-3 [-] Show Supplier Material materials with Factor de disipación of 3E-3 [-] | IEC 60250 |
Rigidez dieléctrica | 23.0 °C | 22 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 22 kV/mm | IEC 60243 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Índice de seguimiento comparativo | 23.0 °C | 270 V Show Supplier Material materials with Índice de seguimiento comparativo of 270 V | IEC 60112 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in the production of Aluminum Alloy fixture, mixing warter valve, water heater set of water treatment equipment, and other products in the field of high toughness | |
Fillers | Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |