General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8 g/cm³ Show Supplier Material materials with Densidad of 8 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 30 % Show Supplier Material materials with Elongación of 30 % | Typical mechanical properties |
Límite elástico Rp 0,2 | 20.0 °C | 210 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 210 MPa | Typical mechanical properties |
100.0 °C | 185 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 185 MPa | Typical mechanical properties | |
200.0 °C | 160 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 160 MPa | Typical mechanical properties | |
300.0 °C | 145 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 145 MPa | Typical mechanical properties | |
400.0 °C | 130 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 130 MPa | Typical mechanical properties | |
500.0 °C | 125 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 125 MPa | Typical mechanical properties | |
550.0 °C | 115 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 115 MPa | Typical mechanical properties | |
Límite elástico Rp 1,0 | 20.0 °C | 240 MPa Show Supplier Material materials with Límite elástico Rp 1,0 of 240 MPa | Typical mechanical properties |
100.0 °C | 205 MPa Show Supplier Material materials with Límite elástico Rp 1,0 of 205 MPa | Typical mechanical properties | |
200.0 °C | 180 MPa Show Supplier Material materials with Límite elástico Rp 1,0 of 180 MPa | Typical mechanical properties | |
300.0 °C | 165 MPa Show Supplier Material materials with Límite elástico Rp 1,0 of 165 MPa | Typical mechanical properties | |
400.0 °C | 150 MPa Show Supplier Material materials with Límite elástico Rp 1,0 of 150 MPa | Typical mechanical properties | |
500.0 °C | 145 MPa Show Supplier Material materials with Límite elástico Rp 1,0 of 145 MPa | Typical mechanical properties | |
550.0 °C | 135 MPa Show Supplier Material materials with Límite elástico Rp 1,0 of 135 MPa | Typical mechanical properties | |
Módulo elástico | 20.0 °C | 194 GPa Show Supplier Material materials with Módulo elástico of 194 GPa | |
100.0 °C | 189 GPa Show Supplier Material materials with Módulo elástico of 189 GPa | ||
200.0 °C | 183 GPa Show Supplier Material materials with Módulo elástico of 183 GPa | ||
300.0 °C | 177 GPa Show Supplier Material materials with Módulo elástico of 177 GPa | ||
400.0 °C | 170 GPa Show Supplier Material materials with Módulo elástico of 170 GPa | ||
500.0 °C | 163 GPa Show Supplier Material materials with Módulo elástico of 163 GPa | ||
600.0 °C | 156 GPa Show Supplier Material materials with Módulo elástico of 156 GPa | ||
700.0 °C | 149 GPa Show Supplier Material materials with Módulo elástico of 149 GPa | ||
800.0 °C | 141 GPa Show Supplier Material materials with Módulo elástico of 141 GPa | ||
900.0 °C | 134 GPa Show Supplier Material materials with Módulo elástico of 134 GPa | ||
1000.0 °C | 127 GPa Show Supplier Material materials with Módulo elástico of 127 GPa | ||
1100.0 °C | 120 GPa Show Supplier Material materials with Módulo elástico of 120 GPa | ||
1200.0 °C | 113 GPa Show Supplier Material materials with Módulo elástico of 113 GPa | ||
Resistencia a la tracción | 20.0 °C | 500 MPa Show Supplier Material materials with Resistencia a la tracción of 500 MPa | Typical mechanical properties |
100.0 °C | 425 MPa Show Supplier Material materials with Resistencia a la tracción of 425 MPa | Typical mechanical properties | |
200.0 °C | 400 MPa Show Supplier Material materials with Resistencia a la tracción of 400 MPa | Typical mechanical properties | |
300.0 °C | 390 MPa Show Supplier Material materials with Resistencia a la tracción of 390 MPa | Typical mechanical properties | |
400.0 °C | 380 MPa Show Supplier Material materials with Resistencia a la tracción of 380 MPa | Typical mechanical properties | |
500.0 °C | 360 MPa Show Supplier Material materials with Resistencia a la tracción of 360 MPa | Typical mechanical properties | |
550.0 °C | 300 MPa Show Supplier Material materials with Resistencia a la tracción of 300 MPa | Typical mechanical properties | |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 2000 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 2000 kJ/m² | |
impactTransVNotch | 23.0 °C | 1000 kJ/m² Show Supplier Material materials with impactTransVNotch of 1000 kJ/m² |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 20.0 °C | 443 J/(kg·K) Show Supplier Material materials with Calor específico of 443 J/(kg·K) |
100.0 °C | 457 J/(kg·K) Show Supplier Material materials with Calor específico of 457 J/(kg·K) | |
200.0 °C | 474 J/(kg·K) Show Supplier Material materials with Calor específico of 474 J/(kg·K) | |
300.0 °C | 492 J/(kg·K) Show Supplier Material materials with Calor específico of 492 J/(kg·K) | |
400.0 °C | 512 J/(kg·K) Show Supplier Material materials with Calor específico of 512 J/(kg·K) | |
500.0 °C | 548 J/(kg·K) Show Supplier Material materials with Calor específico of 548 J/(kg·K) | |
600.0 °C | 578 J/(kg·K) Show Supplier Material materials with Calor específico of 578 J/(kg·K) | |
700.0 °C | 588 J/(kg·K) Show Supplier Material materials with Calor específico of 588 J/(kg·K) | |
800.0 °C | 598 J/(kg·K) Show Supplier Material materials with Calor específico of 598 J/(kg·K) | |
900.0 °C | 602 J/(kg·K) Show Supplier Material materials with Calor específico of 602 J/(kg·K) | |
1000.0 °C | 613 J/(kg·K) Show Supplier Material materials with Calor específico of 613 J/(kg·K) | |
1100.0 °C | 628 J/(kg·K) Show Supplier Material materials with Calor específico of 628 J/(kg·K) | |
1200.0 °C | 634 J/(kg·K) Show Supplier Material materials with Calor específico of 634 J/(kg·K) | |
Coeficiente de dilatación térmica | 100.0 °C | 1.41E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.41E-5 1/K |
200.0 °C | 1.46E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.46E-5 1/K | |
300.0 °C | 1.49E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.49E-5 1/K | |
400.0 °C | 1.52E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.52E-5 1/K | |
500.0 °C | 1.55E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.55E-5 1/K | |
600.0 °C | 1.59E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.59E-5 1/K | |
700.0 °C | 1.64E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.64E-5 1/K | |
800.0 °C | 1.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.7E-5 1/K | |
900.0 °C | 1.74E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.74E-5 1/K | |
1000.0 °C | 1.78E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.78E-5 1/K | |
1100.0 °C | 1.83E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.83E-5 1/K | |
1200.0 °C | 1.87E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.87E-5 1/K | |
Conductividad térmica | 20.0 °C | 12.4 W/(m·K) Show Supplier Material materials with Conductividad térmica of 12.4 W/(m·K) |
100.0 °C | 13.7 W/(m·K) Show Supplier Material materials with Conductividad térmica of 13.7 W/(m·K) | |
200.0 °C | 15.3 W/(m·K) Show Supplier Material materials with Conductividad térmica of 15.3 W/(m·K) | |
300.0 °C | 17 W/(m·K) Show Supplier Material materials with Conductividad térmica of 17 W/(m·K) | |
400.0 °C | 18.9 W/(m·K) Show Supplier Material materials with Conductividad térmica of 18.9 W/(m·K) | |
500.0 °C | 21.4 W/(m·K) Show Supplier Material materials with Conductividad térmica of 21.4 W/(m·K) | |
600.0 °C | 23.6 W/(m·K) Show Supplier Material materials with Conductividad térmica of 23.6 W/(m·K) | |
700.0 °C | 24.7 W/(m·K) Show Supplier Material materials with Conductividad térmica of 24.7 W/(m·K) | |
800.0 °C | 25.8 W/(m·K) Show Supplier Material materials with Conductividad térmica of 25.8 W/(m·K) | |
900.0 °C | 26.7 W/(m·K) Show Supplier Material materials with Conductividad térmica of 26.7 W/(m·K) | |
1000.0 °C | 28 W/(m·K) Show Supplier Material materials with Conductividad térmica of 28 W/(m·K) | |
1100.0 °C | 29.6 W/(m·K) Show Supplier Material materials with Conductividad térmica of 29.6 W/(m·K) | |
1200.0 °C | 30.6 W/(m·K) Show Supplier Material materials with Conductividad térmica of 30.6 W/(m·K) | |
Temperatura de fusión | 1350 - 1400 °C Show Supplier Material materials with Temperatura de fusión of 1350 - 1400 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 20.0 °C | 1.01E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.01E-6 Ω·m |
100.0 °C | 1.04E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.04E-6 Ω·m | |
200.0 °C | 1.08E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.08E-6 Ω·m | |
300.0 °C | 1.12E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.12E-6 Ω·m | |
400.0 °C | 1.15E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.15E-6 Ω·m | |
500.0 °C | 1.18E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.18E-6 Ω·m | |
600.0 °C | 1.2E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.2E-6 Ω·m | |
700.0 °C | 1.22E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.22E-6 Ω·m | |
800.0 °C | 1.24E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.24E-6 Ω·m | |
900.0 °C | 1.26E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.26E-6 Ω·m | |
1000.0 °C | 1.27E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.27E-6 Ω·m | |
1100.0 °C | 1.28E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.28E-6 Ω·m | |
1200.0 °C | 1.29E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.29E-6 Ω·m | |
Magnético
Property | Temperature | Value |
---|---|---|
Permeabilidad magnética relativa | 23.0 °C | 1.01 [-] Show Supplier Material materials with Permeabilidad magnética relativa of 1.01 [-] |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminio | 0.2 - 0.4 % Show Supplier Material materials with Aluminio of 0.2 - 0.4 % | |
Azufre | 0.01 % Show Supplier Material materials with Azufre of 0.01 % | max. |
Carbono | 0.1 % Show Supplier Material materials with Carbono of 0.1 % | max. |
Cobre | 0.5 % Show Supplier Material materials with Cobre of 0.5 % | max. |
Cromo | 19 - 21.5 % Show Supplier Material materials with Cromo of 19 - 21.5 % | |
Fósforo | 0.02 % Show Supplier Material materials with Fósforo of 0.02 % | max. |
Hierro | 41 - 47 % Show Supplier Material materials with Hierro of 41 - 47 % | |
Manganeso | 0.5 - 1 % Show Supplier Material materials with Manganeso of 0.5 - 1 % | |
Níquel | 30 - 32 % Show Supplier Material materials with Níquel of 30 - 32 % | |
Silicona | 0.2 - 0.6 % Show Supplier Material materials with Silicona of 0.2 - 0.6 % | |
Titanio | 0.2 - 0.5 % Show Supplier Material materials with Titanio of 0.2 - 0.5 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical fields of application for VDM® Alloy 800 are: Heating element sheaths, acetic anhydride cracking furnaces VDM® Alloy 800 shall be used in the soft-annealed condition up to 600 °C. The solution annealed version VDM® Alloy 800 H shall be considered for application temperatures above 600 °C. | |
Cold Forming | VDM® Alloy 800 is easily cold-shaped. However, it has a slightly higher work-hardening than carbon steel. This must be taken into account during the design and selection of forming tools and equipment and during the planning of forming processes. Intermediate annealing is necessary during cold working. | |
Corrosion properties | VDM® Alloy 800 is resistant to many corrosive media. For wet corrosion, the increased nickel content of this alloy results in good resistance to stress cracking corrosion. The elevated chromium content increases the resistance to pitting and crevice corrosion. The alloy shows good resistance in nitric acid and organic acids, but only limited resistance to sulfuric and hydrochloric acid. Pitting corrosion may occur in halogen-containing acids. The material shows good resistance in oxidizing and reducing saline solutions. It is also resistant in fresh water and steam as well as mixtures of steam, air and carbon dioxide. At elevated temperatures, VDM® Alloy 800 exhibits excellent resistance in oxidizing and carburizing atmospheres as well as in alternating oxidizing and carburizing atmospheres. The resistance to hydrogen, nitrogen and sulfuric gases is good, whereby it is better under oxidizing conditions than under reducing conditions. | |
General machinability | Machining of VDM® Alloy 800 should take place in an annealed condition. Because of the elevated tendency toward work hardening in comparison with low-alloy austenitic stainless steels, a low cutting speed and a feed level that is not too high should be selected and the cutting tool should be engaged at all times. An adequate depth of cut is important in order to cut below the previously formed strain-hardened zone. Optimum heat dissipation through the use of large quantities of suitable preferably aqueous lubricants has considerable influence on a stable machining process. | |
Heat Treatment | VDM® Alloy 800 is used in the soft-annealed condition in applications whose operating temperatures are below approximately 600°C (1,112°F). The annealing should be performed at temperatures of 920 to 980°C (1688-1796°F), preferably at about 950°C (1,742°F). The retention time commences with material temperature equalization; longer times are generally considerably less critical than retention times that are too short. Cooling should be accelerated with water to achieve optimum corrosion properties. Fast air cooling can also be carried out at thicknesses below approx. 3 mm. The material must be placed in a furnace that has been heated up to the maximum annealing temperature before any heat treatment. For strip products, the heat treatment can be performed in a continuous furnace at a speed and temperature that is adapted to the strip thickness. The cleanliness requirements listed under "Heating" must be observed. | |
Hot forming | VDM® Alloy 800 can be hot-formed at a temperature range of between 1,200 and 900°C (2,192-1,652°F) with subsequent rapid cooling down in water or in air, whereby the temperature range from 760 to 540 °C (1,400-1,004°F) must be passed through quickly. Hot bending is performed between 1,150 and 1,000°C (2,102-1,832°F). For preheating, the workpieces may be placed in the furnace which has already been preheated to the maximum hot forming temperature. The workpieces should be retained in the furnace for around 60 minutes per 100 mm of thickness once the furnace has reached its temperature again. After this, the workpiece should be removed from the furnace immediately and formed within the temperature interval stated above, whereby reheating is necessary once the temperature reaches 900 °C (1,652°F). Heat treatment after hot-working is recommended for the achievement of optimal corrosion properties and microstructure. | |
Other | VDM® Alloy 800 is an austenitic solid solution alloy which precipitates carbides and γ’ phase during high-temperature ageing. | |
Welding | Care should be taken that the work is performed with a deliberately chosen, low heat input. The stringer bead technique is recommended. The interpass temperature should not exceed 120°C (248 °F). The welding parameters should be monitored as a matter of principle. |