General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Densidad | 2.73 g/cm³ Show Material materials with Densidad of 2.73 g/cm³ | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
20.0 °C | 2.73 g/cm³ Show Material materials with Densidad of 2.73 g/cm³ | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending Fatigue Strength | 75.0 MPa Show Material materials with Bending Fatigue Strength of 75.0 MPa | H18 | EN 573-3, EN 1301, EN 485, EN 683, EN 754 | |||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||||
Dureza Brinell | 58.0 [-] Show Material materials with Dureza Brinell of 58.0 [-] | H18 | EN 573-3, EN 485 | |||
20.0 °C | 45.0 [-] Show Material materials with Dureza Brinell of 45.0 [-] | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Wire | ||
20.0 °C | 50.0 [-] Show Material materials with Dureza Brinell of 50.0 [-] | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat | ||
Elongación | -196.0 °C | 30.0 % Show Material materials with Elongación of 30.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | ||
-80.0 °C | 18.0 % Show Material materials with Elongación of 18.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
-20.0 °C | 16.0 % Show Material materials with Elongación of 16.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
1.0 % Show Material materials with Elongación of 1.0 % | H18 | EN 573-3, EN 485, EN 546, EN 683 | A50 | |||
2.0 % Show Material materials with Elongación of 2.0 % | H18 | EN 573-3, EN 1592 | A100 | |||
2.0 % Show Material materials with Elongación of 2.0 % | H18 | EN 573-3, EN 485, EN 754 | A50 | |||
3.0 % Show Material materials with Elongación of 3.0 % | H18 | EN 573-3, EN 1301 | ||||
3.0 % Show Material materials with Elongación of 3.0 % | H18 | EN 573-3, EN 754 | A100 | |||
20.0 °C | 1.0 % Show Material materials with Elongación of 1.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Wire | A100 | |
20.0 °C | 3.0 % Show Material materials with Elongación of 3.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | A10 | |
20.0 °C | 4.0 % Show Material materials with Elongación of 4.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat | ||
20.0 °C | 10.0 % Show Material materials with Elongación of 10.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
100.0 °C | 10.0 % Show Material materials with Elongación of 10.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
150.0 °C | 11.0 % Show Material materials with Elongación of 11.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
200.0 °C | 18.0 % Show Material materials with Elongación of 18.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
260.0 °C | 60.0 % Show Material materials with Elongación of 60.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
320.0 °C | 70.0 % Show Material materials with Elongación of 70.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
370.0 °C | 70.0 % Show Material materials with Elongación of 70.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
Módulo de cizallamiento | 26.1 GPa Show Material materials with Módulo de cizallamiento of 26.1 GPa | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | |||
20.0 °C | 24.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 24.0 - 26.5 GPa | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | ||
Módulo elástico | 69.5 GPa Show Material materials with Módulo elástico of 69.5 GPa | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | |||
20.0 °C | 60.0 - 65.0 GPa Show Material materials with Módulo elástico of 60.0 - 65.0 GPa | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||||
Resistencia a la tracción | -196.0 °C | 298.0 MPa Show Material materials with Resistencia a la tracción of 298.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | ||
-80.0 °C | 225.0 MPa Show Material materials with Resistencia a la tracción of 225.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
-20.0 °C | 214.0 MPa Show Material materials with Resistencia a la tracción of 214.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
170.0 MPa Show Material materials with Resistencia a la tracción of 170.0 MPa | H18 | EN 573-3, EN 1301 | ||||
180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | H18 | EN 573-3, EN 754 | ||||
185.0 MPa Show Material materials with Resistencia a la tracción of 185.0 MPa | H18 | EN 573-3, EN 485, EN 683 | ||||
185.0 - 230.0 MPa Show Material materials with Resistencia a la tracción of 185.0 - 230.0 MPa | H18 | EN 573-3, EN 546 | ||||
190.0 MPa Show Material materials with Resistencia a la tracción of 190.0 MPa | H18 | EN 573-3, EN 1592 | ||||
20.0 °C | 100.0 MPa Show Material materials with Resistencia a la tracción of 100.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513 | Tube | ||
20.0 °C | 160.0 MPa Show Material materials with Resistencia a la tracción of 160.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Wire | ||
20.0 °C | 165.0 - 205.0 MPa Show Material materials with Resistencia a la tracción of 165.0 - 205.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Flat | ||
20.0 °C | 204.0 MPa Show Material materials with Resistencia a la tracción of 204.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
100.0 °C | 183.0 MPa Show Material materials with Resistencia a la tracción of 183.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
150.0 °C | 163.0 MPa Show Material materials with Resistencia a la tracción of 163.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
200.0 °C | 98.0 MPa Show Material materials with Resistencia a la tracción of 98.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
260.0 °C | 53.0 MPa Show Material materials with Resistencia a la tracción of 53.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
320.0 °C | 28.0 MPa Show Material materials with Resistencia a la tracción of 28.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
370.0 °C | 21.0 MPa Show Material materials with Resistencia a la tracción of 21.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
Ángulo de flexión a 90° | 1.5 °/t Show Material materials with Ángulo de flexión a 90° of 1.5 °/t | H18 | EN 573-3, EN 485 | |||
2.5 °/t Show Material materials with Ángulo de flexión a 90° of 2.5 °/t | H18 | EN 573-3, EN 485 | ||||
3.0 °/t Show Material materials with Ángulo de flexión a 90° of 3.0 °/t | H18 | EN 573-3, EN 485 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Calor específico | 893.0 J/(kg·K) Show Material materials with Calor específico of 893.0 J/(kg·K) | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
20.0 °C | 893.0 J/(kg·K) Show Material materials with Calor específico of 893.0 J/(kg·K) | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | |
Coeficiente de dilatación térmica | 20 °C | 2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | |
100 °C | 2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
Conductividad térmica | 20.0 °C | 160.0 - 200.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 - 200.0 W/(m·K) | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Flat, Wire |
Temperatura de fusión | 645.0 - 655.0 °C Show Material materials with Temperatura de fusión of 645.0 - 655.0 °C | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 |
Eléctrico
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 22000000.0 - 28000000.0 S/m Show Material materials with Conductividad eléctrica of 22000000.0 - 28000000.0 S/m | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Flat, Wire |
Resistividad eléctrica | 3.57e-08 - 4.55e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.57e-08 - 4.55e-08 Ω·m | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Hierro | 0.7 % Show Material materials with Hierro of 0.7 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Tube, Flat, Wire |
0.70 % Show Material materials with Hierro of 0.70 % | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
Magnesio | 0.3 % Show Material materials with Magnesio of 0.3 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Manganeso | 0.9 - 1.5 % Show Material materials with Manganeso of 0.9 - 1.5 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Silicona | 0.5 % Show Material materials with Silicona of 0.5 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Titanio | 0.1 Show Material materials with Titanio of 0.1 | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Tube, Flat, Wire |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Technological properties
Property | ||
---|---|---|
Workability | Good workability. |