DIN 1725-1 Grade 3.3316 H24

Want to keep this datasheet? Save it now in your required format

Description

The alloys are characterised by a good corrosion resistance. It is sea water steady and resistant to saline atmosphere. The Mg content increases the strength, but the cold forming capacity decreases. The material is nature hard, i.e. only by a cold forming and not by a purposeful heat treatment a strength increase can be attained. It is well polishable and anodisable. The splinter-giving machinability becomes better with increasing Mg content, just as the weldability. From the AlMg alloys the mark AlMg1,5 has to exhibit only relatively small mechanical properties. Standardised semi-finished material only for sheet metal and strips with thickness: > 0.35 mm in accordance to DIN 1745. Application: The main application lies in the building industry. In the building industry for lamella net curtains, rolling shutter, roll gates, in food industry (including table-ware) and for transport containers.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³	H24	EN 573-3, EN 485
		2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³	H24	EN 573-3, EN 485
	20.0 °C	2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Dureza Brinell		54.0 [-] Show Material materials with Dureza Brinell of 54.0 [-]	H24	EN 573-3, EN 485
	20.0 °C	55.0 [-] Show Material materials with Dureza Brinell of 55.0 [-]	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Elongación		3.0 % Show Material materials with Elongación of 3.0 %	H24	EN 573-3, EN 485		A50
		4.0 % Show Material materials with Elongación of 4.0 %	H24	EN 573-3, EN 485		A50
		5.0 % Show Material materials with Elongación of 5.0 %	H24	EN 573-3, EN 485		A50
		8.0 % Show Material materials with Elongación of 8.0 %	H24	EN 573-3, EN 485		A50
	20.0 °C	8.0 % Show Material materials with Elongación of 8.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	10.0 % Show Material materials with Elongación of 10.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Módulo de cizallamiento	20.0 °C	26.5 Show Material materials with Módulo de cizallamiento of 26.5	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Módulo elástico		69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa	H24	EN 573-3, EN 485
		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	H24	EN 573-3, EN 485
	20.0 °C	70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Resistencia a la tracción	20.0 °C	175.0 - 215.0 MPa Show Material materials with Resistencia a la tracción of 175.0 - 215.0 MPa	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Ángulo de flexión a 180°		1.5 °/t Show Material materials with Ángulo de flexión a 180° of 1.5 °/t	H24	EN 573-3, EN 485
		2.0 °/t Show Material materials with Ángulo de flexión a 180° of 2.0 °/t	H24	EN 573-3, EN 485
Ángulo de flexión a 90°		0.5 °/t Show Material materials with Ángulo de flexión a 90° of 0.5 °/t	H24	EN 573-3, EN 485
		1.0 °/t Show Material materials with Ángulo de flexión a 90° of 1.0 °/t	H24	EN 573-3, EN 485
		1.5 °/t Show Material materials with Ángulo de flexión a 90° of 1.5 °/t	H24	EN 573-3, EN 485
		2.0 °/t Show Material materials with Ángulo de flexión a 90° of 2.0 °/t	H24	EN 573-3, EN 485

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico		879.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 879.0 - 963.0 J/(kg·K)				Typical for Wrought 5000 Series Aluminium
Coeficiente de dilatación térmica	20 °C	2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K	H24	EN 573-3, EN 485
	100 °C	2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K	H24	EN 573-3, EN 485
Conductividad térmica		170.0 - 190.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 190.0 W/(m·K)	H24	EN 573-3, EN 485
		193 W/(m·K) Show Material materials with Conductividad térmica of 193 W/(m·K)	H24	EN 573-3, EN 485
	20.0 °C	160.0 - 200.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 - 200.0 W/(m·K)	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Temperatura de fusión		620.0 - 650.0 °C Show Material materials with Temperatura de fusión of 620.0 - 650.0 °C	H24	EN 573-3, EN 485
		625.0 - 650.0 °C Show Material materials with Temperatura de fusión of 625.0 - 650.0 °C	H24	EN 573-3, EN 485
Temperatura máx. de funcionamiento		150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C				Typical for Wrought 5000 Series Aluminium

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica		23000000.0 - 26000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 26000000.0 S/m	H24	EN 573-3, EN 485
		29000000.0 S/m Show Material materials with Conductividad eléctrica of 29000000.0 S/m	H24	EN 573-3, EN 485
	20.0 °C	28000000.0 - 30000000.0 S/m Show Material materials with Conductividad eléctrica of 28000000.0 - 30000000.0 S/m	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Resistividad eléctrica		3.45e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.45e-08 Ω·m	H24	EN 573-3, EN 485
		3.85e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.85e-08 - 4.35e-08 Ω·m	H24	EN 573-3, EN 485

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.05 % Show Material materials with Cobre of 0.05 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Cromo	0.1 % Show Material materials with Cromo of 0.1 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Hierro	0.45 % Show Material materials with Hierro of 0.45 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
	0.45 % Show Material materials with Hierro of 0.45 %	H24	EN 573-3, EN 485
Magnesio	1.1 - 1.7 % Show Material materials with Magnesio of 1.1 - 1.7 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Manganeso	0.15 % Show Material materials with Manganeso of 0.15 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Silicona	0.4 % Show Material materials with Silicona of 0.4 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Zinc	0.2 % Show Material materials with Zinc of 0.2 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat

Technological properties

Property

Workability

Good workability.