WL 3.3354 Grade 3.3354 O

Want to keep this datasheet? Save it now in your required format

Description

The alloy is characterised by a good corrosion resistance. It is sea water steady and resistant to saline atmosphere. The Mg content increases the strength, but the cold forming capacity decreases. The material is nature hard, i.e. only by a cold forming and not by a purposeful heat treatment a strength increase can be attained. It is well polishable and anodisable. The splinter-giving machinability becomes better with increasing Mg content, just as the weldability. AlMg5 has the highest Mg content of the standardized AlMg alloys, so it is badly cold formable, but the strength is the highest, so that the employment is possible for statically more highly loaded constructions. The alloy is suitable for a splinter-giving machinig on automats. It possesses sensitivity to intergranular corrosion. By a purposeful heat treatment and/or by additive of Mn or Cr the inclination to the intergranular corrosion can be reduced. Application: In the optics, in the automobile engineering for body parts, in mechanical engineering (turned parts). For joining elements (solid rivets, blind rivets, riveting nuts and screws). In the building industry for carrying constructions as well as in shipbuilding considering the sensitivity to corrosion.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.64 g/cm³ Show Material materials with Densidad of 2.64 g/cm³	O	WL 3.3354	Wire
	20.0 °C	2.64 g/cm³ Show Material materials with Densidad of 2.64 g/cm³	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Dureza Brinell	20.0 °C	55.0 [-] Show Material materials with Dureza Brinell of 55.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire
	20.0 °C	60.0 [-] Show Material materials with Dureza Brinell of 60.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod
	20.0 °C	65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Tube
Elongación	20.0 °C	5.0 % Show Material materials with Elongación of 5.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire	A100
	20.0 °C	10.0 % Show Material materials with Elongación of 10.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire	A10
	20.0 °C	12.0 % Show Material materials with Elongación of 12.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod	A10
	20.0 °C	14.0 % Show Material materials with Elongación of 14.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod
	20.0 °C	14.0 % Show Material materials with Elongación of 14.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Tube	A10
	20.0 °C	16.0 % Show Material materials with Elongación of 16.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Tube
	20.0 °C	28.0 % Show Material materials with Elongación of 28.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	60.0 °C	28.0 % Show Material materials with Elongación of 28.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	100.0 °C	32.0 % Show Material materials with Elongación of 32.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	140.0 °C	40.0 % Show Material materials with Elongación of 40.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	180.0 °C	52.0 % Show Material materials with Elongación of 52.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	240.0 °C	64.0 % Show Material materials with Elongación of 64.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	300.0 °C	100.0 % Show Material materials with Elongación of 100.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	360.0 °C	104.0 % Show Material materials with Elongación of 104.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
Módulo de cizallamiento	20.0 °C	27.0 GPa Show Material materials with Módulo de cizallamiento of 27.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Módulo elástico		71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa	O	WL 3.3354	Wire
	20.0 °C	67.0 - 72.0 GPa Show Material materials with Módulo elástico of 67.0 - 72.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Resistencia a la tracción	20.0 °C	250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube
	20.0 °C	270.0 MPa Show Material materials with Resistencia a la tracción of 270.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire
	20.0 °C	280.0 MPa Show Material materials with Resistencia a la tracción of 280.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	100.0 °C	275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	140.0 °C	235.0 MPa Show Material materials with Resistencia a la tracción of 235.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	180.0 °C	200.0 MPa Show Material materials with Resistencia a la tracción of 200.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	240.0 °C	140.0 MPa Show Material materials with Resistencia a la tracción of 140.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	300.0 °C	100.0 MPa Show Material materials with Resistencia a la tracción of 100.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	360.0 °C	55.0 MPa Show Material materials with Resistencia a la tracción of 55.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
Resistencia al cizallamiento	20.0 °C	150.0 MPa Show Material materials with Resistencia al cizallamiento of 150.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico		904.0 J/(kg·K) Show Material materials with Calor específico of 904.0 J/(kg·K)	O	WL 3.3354	Wire
	20.0 °C	904.0 J/(kg·K) Show Material materials with Calor específico of 904.0 J/(kg·K)	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Coeficiente de dilatación térmica	-50.0 °C	2.25e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.25e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	20 °C	2.31e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.31e-05 1/K	O	WL 3.3354	Wire
	100 °C	2.31e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.31e-05 1/K	O	WL 3.3354	Wire
	100.0 °C	2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	200.0 °C	2.51e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.51e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	300.0 °C	2.61e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.61e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Conductividad térmica	20.0 °C	110.0 - 140.0 W/(m·K) Show Material materials with Conductividad térmica of 110.0 - 140.0 W/(m·K)	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Temperatura de fusión		565.0 - 640.0 °C Show Material materials with Temperatura de fusión of 565.0 - 640.0 °C	O	WL 3.3354	Wire
Temperatura máx. de funcionamiento		150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C				Typical for Wrought 5000 Series Aluminium

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica	20.0 °C	15000000.0 - 19000000.0 S/m Show Material materials with Conductividad eléctrica of 15000000.0 - 19000000.0 S/m	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Resistividad eléctrica		5.26e-08 - 6.67e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.26e-08 - 6.67e-08 Ω·m	O	WL 3.3354	Wire

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.1 % Show Material materials with Cobre of 0.1 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Cromo	0.2 % Show Material materials with Cromo of 0.2 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Hierro	0.5 % Show Material materials with Hierro of 0.5 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	0.50 % Show Material materials with Hierro of 0.50 %	O	WL 3.3354	Wire
Magnesio	4.5 - 5.6 % Show Material materials with Magnesio of 4.5 - 5.6 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Manganeso	0.1 - 0.6 % Show Material materials with Manganeso of 0.1 - 0.6 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Silicona	0.4 % Show Material materials with Silicona of 0.4 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Titanio	0.2 Show Material materials with Titanio of 0.2	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Zinc	0.2 % Show Material materials with Zinc of 0.2 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Technological properties

Property

Workability

Good workability.