DIN 1725-1 Grade 3.3525 H24

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlMg2Mn0,3 has similar characteristics as the alloy AlMg1,8. The additive of Mn causes an increase of the heat resistance of the material apart from a strength increase with the products of extruding. The material is characterised by a good corrosion resistance. It is sea water steady and steady against saline atmosphere. With the Mg content the strength increases, the cold forming capacity decreases. The alloy is nature hard, i.e. that only by a cold forming shaping however by a purposeful heat treatment a strength increase cannot be attained. The splinter-giving workability and the weldability are improved with increasing Mg content. Application: For metal goods (including table-ware), in food industry (including commercial devices). For transport containers e.g. rolling barrels, in the packaging industry as cans as well as for describe (e.g. road signs).

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³	H24	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending Fatigue Strength		115.0 MPa Show Material materials with Bending Fatigue Strength of 115.0 MPa	H24	EN 573-3, EN 1592, EN 485, EN 754
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Dureza Brinell		62.0 [-] Show Material materials with Dureza Brinell of 62.0 [-]	H24	EN 573-3, EN 485
	20.0 °C	65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-]	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Elongación		3.0 % Show Material materials with Elongación of 3.0 %	H24	EN 573-3, EN 485, EN 754		A50
		4.0 % Show Material materials with Elongación of 4.0 %	H24	EN 573-3, EN 754		A100
		4.0 % Show Material materials with Elongación of 4.0 %	H24	EN 573-3, EN 754		A50
		5.0 % Show Material materials with Elongación of 5.0 %	H24	EN 573-3, EN 754		A100
		5.0 % Show Material materials with Elongación of 5.0 %	H24	EN 573-3, EN 485		A50
		6.0 % Show Material materials with Elongación of 6.0 %	H24	EN 573-3, EN 1592		A100
		6.0 % Show Material materials with Elongación of 6.0 %	H24	EN 573-3, EN 485		A50
		8.0 % Show Material materials with Elongación of 8.0 %	H24	EN 573-3, EN 485		A50
		10.0 % Show Material materials with Elongación of 10.0 %	H24	EN 573-3, EN 485		A50
	20.0 °C	8.0 % Show Material materials with Elongación of 8.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	10.0 % Show Material materials with Elongación of 10.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Módulo de cizallamiento		26.3 GPa Show Material materials with Módulo de cizallamiento of 26.3 GPa	H24	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	26.5 GPa Show Material materials with Módulo de cizallamiento of 26.5 GPa	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	H24	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Resistencia a la tracción		200.0 - 240.0 MPa Show Material materials with Resistencia a la tracción of 200.0 - 240.0 MPa	H24	EN 573-3, EN 754
		210.0 - 250.0 MPa Show Material materials with Resistencia a la tracción of 210.0 - 250.0 MPa	H24	EN 573-3, EN 485
		230.0 MPa Show Material materials with Resistencia a la tracción of 230.0 MPa	H24	EN 573-3, EN 1592
	20.0 °C	205.0 - 245.0 MPa Show Material materials with Resistencia a la tracción of 205.0 - 245.0 MPa	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Ángulo de flexión a 180°		2.0 °/t Show Material materials with Ángulo de flexión a 180° of 2.0 °/t	H24	EN 573-3, EN 485
Ángulo de flexión a 90°		0.5 °/t Show Material materials with Ángulo de flexión a 90° of 0.5 °/t	H24	EN 573-3, EN 485
		1.5 °/t Show Material materials with Ángulo de flexión a 90° of 1.5 °/t	H24	EN 573-3, EN 485
		2.5 °/t Show Material materials with Ángulo de flexión a 90° of 2.5 °/t	H24	EN 573-3, EN 485
		3.0 °/t Show Material materials with Ángulo de flexión a 90° of 3.0 °/t	H24	EN 573-3, EN 485

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico	20.0 °C	921.0 J/(kg·K) Show Material materials with Calor específico of 921.0 J/(kg·K)	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Coeficiente de dilatación térmica	20 °C	2.3699999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3699999999999997e-05 1/K	H24	EN 573-3, EN 1592, EN 485, EN 754
	100 °C	2.3699999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3699999999999997e-05 1/K	H24	EN 573-3, EN 1592, EN 485, EN 754
Conductividad térmica		140.0 - 160.0 W/(m·K) Show Material materials with Conductividad térmica of 140.0 - 160.0 W/(m·K)	H24	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	167.0 W/(m·K) Show Material materials with Conductividad térmica of 167.0 W/(m·K)	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Temperatura de fusión		610.0 - 650.0 °C Show Material materials with Temperatura de fusión of 610.0 - 650.0 °C	H24	EN 573-3, EN 1592, EN 485, EN 754
Temperatura máx. de funcionamiento		150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C				Typical for Wrought 5000 Series Aluminium

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica		25000000.0 - 30000000.0 S/m Show Material materials with Conductividad eléctrica of 25000000.0 - 30000000.0 S/m	H24	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	26000000.0 S/m Show Material materials with Conductividad eléctrica of 26000000.0 S/m	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Resistividad eléctrica		3.33e-08 - 4e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.33e-08 - 4e-08 Ω·m	H24	EN 573-3, EN 1592, EN 485, EN 754

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.15 % Show Material materials with Cobre of 0.15 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat
Cromo	0.15 % Show Material materials with Cromo of 0.15 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat
Hierro	0.5 % Show Material materials with Hierro of 0.5 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
	0.50 % Show Material materials with Hierro of 0.50 %	H24	EN 573-3, EN 1592, EN 485, EN 754
Magnesio	1.7 - 2.4 % Show Material materials with Magnesio of 1.7 - 2.4 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat
Manganeso	0.1 - 0.5 % Show Material materials with Manganeso of 0.1 - 0.5 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat
Silicona	0.4 % Show Material materials with Silicona of 0.4 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat
Titanio	0.15 % Show Material materials with Titanio of 0.15 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat
Zinc	0.15 % Show Material materials with Zinc of 0.15 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat

Technological properties

Property
Anodizing	decorative: sufficient, Protective: very good
Brazing	hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / acceptable (H12)

Looking for suppliers of this material? Click to see 2 supplier of DIN 1725-1 Grade 3.3525 H24 on Matmatch