EN 573-3 Grade 3.2315 T4

Want to keep this datasheet? Save it now in your required format

Description

From the type of alloy AlMgSi is the alloy AlMgSi1 that, which used longest. This cold and/or hot hardenable material reaches strength values of 200 to 315 MPa with A5-elongation at break of approx. 6 to 18 %. In hot and cold-hardened condition is this alloy only limited formable, in the soft material condition however well. Weldability, corrosion resistance and anodising of this material are good. Although this alloy achieves the highest mechanical strength of all alloys of this type, it is used with priority due to its good corrosion resistance. Furthermore it, although the weldability is good, is used more for screwing and/or rivet joints, because within the welding seam range there is the danger of destabilizations. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperature hot ageing: 4 to 16 h at 155 to 190 °C Application: For bearing constructions (loadedstatically according to DIN 4113), in the apparatus and tank construction for heat exchangers, for compressed gas bottles, technical flow pressed parts, in the automobile engineering for tank and silo trucks, for dump truck hollows, buses, body parts, for safety-related parts, wheels and superstructures. In mechanical engineering for devices, tools (baseplates, head and stamp retaining plates as well as guide plates), machine tables, hydraulic/pneumatics, shaft couplings (forging), roller pipes, brake disks and brake drums (with squirted wear course), liaison vehicles (screws according to DIN 267 T18, rivets), in food industry (including commercial devices), in the building of rail-mounted vehicles for railroad car doors, stroke sun roofs, wheel-center disks, axle box case, car boxes, in shipbuilding for the trunk, for superstructures, sail masts, equipment for radar, in the mining industry, in the building industry for rolling shutter, roll gates, for camping furniture and for metal goods (building fittings, table-ware, reflectors etc.).

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
	20.0 °C	2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging, Wire

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending Fatigue Strength		100.0 MPa Show Material materials with Bending Fatigue Strength of 100.0 MPa	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Dureza Brinell		58.0 [-] Show Material materials with Dureza Brinell of 58.0 [-]	T4	EN 573-3, EN 485
	20.0 °C	60.0 [-] Show Material materials with Dureza Brinell of 60.0 [-]	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging, Wire
	20.0 °C	65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-]	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging
Elongación		6.0 % Show Material materials with Elongación of 6.0 %	T4	EN 573-3, EN 1386		A50
		8.0 % Show Material materials with Elongación of 8.0 %	T4	EN 573-3, EN 1386		A50
		10.0 % Show Material materials with Elongación of 10.0 %	T4	EN 573-3, EN 1386		A50
		12.0 % Show Material materials with Elongación of 12.0 %	T4	EN 573-3, EN 1386		A100
		12.0 % Show Material materials with Elongación of 12.0 %	T4	EN 573-3, EN 1386, EN 485, EN 754, EN 755		A50
		13.0 % Show Material materials with Elongación of 13.0 %	T4	EN 573-3, EN 1301
		14.0 % Show Material materials with Elongación of 14.0 %	T4	EN 573-3, EN 754, EN 755		A100
		14.0 % Show Material materials with Elongación of 14.0 %	T4	EN 573-3, EN 485		A50
		15.0 % Show Material materials with Elongación of 15.0 %	T4	EN 573-3, EN 485		A50
	20.0 °C	7.0 % Show Material materials with Elongación of 7.0 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Wire	A100
	20.0 °C	11.0 % Show Material materials with Elongación of 11.0 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Wire	A10
	20.0 °C	12.0 % Show Material materials with Elongación of 12.0 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging
Módulo de cizallamiento		26.4 GPa Show Material materials with Módulo de cizallamiento of 26.4 GPa	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
	20.0 °C	26.0 - 27.0 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.0 GPa	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging, Wire
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
	20.0 °C	68.0 - 73.0 GPa Show Material materials with Módulo elástico of 68.0 - 73.0 GPa	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging, Wire
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Resistencia a la tracción		205.0 MPa Show Material materials with Resistencia a la tracción of 205.0 MPa	T4	EN 573-3, EN 1301, EN 1386, EN 485, EN 754, EN 755
		260.0 - 290.0 MPa Show Material materials with Resistencia a la tracción of 260.0 - 290.0 MPa	T4	EN 573-3, EN 1715-3
	20.0 °C	200.0 MPa Show Material materials with Resistencia a la tracción of 200.0 MPa	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging, Wire
Ángulo de flexión a 180°		3.0 °/t Show Material materials with Ángulo de flexión a 180° of 3.0 °/t	T4	EN 573-3, EN 485
Ángulo de flexión a 90°		1.5 °/t Show Material materials with Ángulo de flexión a 90° of 1.5 °/t	T4	EN 573-3, EN 485
		2.0 °/t Show Material materials with Ángulo de flexión a 90° of 2.0 °/t	T4	EN 573-3, EN 485
		3.0 °/t Show Material materials with Ángulo de flexión a 90° of 3.0 °/t	T4	EN 573-3, EN 485
		4.0 °/t Show Material materials with Ángulo de flexión a 90° of 4.0 °/t	T4	EN 573-3, EN 1386, EN 485

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape
Calor específico		896.0 J/(kg·K) Show Material materials with Calor específico of 896.0 J/(kg·K)	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
Coeficiente de dilatación térmica	20 °C	2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
	100 °C	2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
Conductividad térmica	20.0 °C	170.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 220.0 W/(m·K)	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Temperatura de fusión		585.0 - 650.0 °C Show Material materials with Temperatura de fusión of 585.0 - 650.0 °C	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica	20.0 °C	24000000.0 - 32000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 - 32000000.0 S/m	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Resistividad eléctrica		3.13e-08 - 4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.13e-08 - 4.17e-08 Ω·m	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.1 % Show Material materials with Cobre of 0.1 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Cromo	0.25 % Show Material materials with Cromo of 0.25 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Hierro	0.5 % Show Material materials with Hierro of 0.5 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Forging, Wire
	0.50 % Show Material materials with Hierro of 0.50 %	T4	EN 573-3, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755
Magnesio	0.6 - 1.2 % Show Material materials with Magnesio of 0.6 - 1.2 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Manganeso	0.4 - 1.0 % Show Material materials with Manganeso of 0.4 - 1.0 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Silicona	0.7 - 1.3 % Show Material materials with Silicona of 0.7 - 1.3 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Titanio	0.1 % Show Material materials with Titanio of 0.1 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire
Zinc	0.2 % Show Material materials with Zinc of 0.2 %	T4	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493, EN 1301, EN 1386, EN 1715-3, EN 485, EN 754, EN 755	Forging, Wire

Technological properties

Property
Anodizing	decorative: acceptable, Protective: very good
Brazing	hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O)

Looking for suppliers of this material? Click to see 10 supplier of EN 573-3 Grade 3.2315 T4 on Matmatch