General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Densidad | 20.0 °C | 2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Dureza Brinell | 20.0 °C | 130.0 [-] Show Material materials with Dureza Brinell of 130.0 [-] | T7351 | WL 3.4364-1, DIN 1725-1 | Rod, Plate | Transverse |
20.0 °C | 130.0 [-] Show Material materials with Dureza Brinell of 130.0 [-] | T7351 | WL 3.4364-1, DIN 1725-1 | Rod, Plate | ||
Elongación | 20.0 °C | 4.0 % Show Material materials with Elongación of 4.0 % | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse |
20.0 °C | 6.0 % Show Material materials with Elongación of 6.0 % | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 6.0 % Show Material materials with Elongación of 6.0 % | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | ||
20.0 °C | 7.0 % Show Material materials with Elongación of 7.0 % | T7351 | WL 3.4364-1, DIN 1725-1 | Rod, Plate | Transverse | |
20.0 °C | 7.0 % Show Material materials with Elongación of 7.0 % | T7351 | WL 3.4364-1, DIN 1725-1 | Rod, Plate | ||
Módulo de cizallamiento | 26.4 - 27.1 GPa Show Material materials with Módulo de cizallamiento of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||||
Módulo de compresibilidad | 20.0 °C | 72.5 GPa Show Material materials with Módulo de compresibilidad of 72.5 GPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod | |
Módulo elástico | 20.0 °C | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||||
Resistencia a la tracción | 20.0 °C | 410.0 MPa Show Material materials with Resistencia a la tracción of 410.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse |
20.0 °C | 420.0 MPa Show Material materials with Resistencia a la tracción of 420.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 420.0 MPa Show Material materials with Resistencia a la tracción of 420.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | ||
20.0 °C | 430.0 MPa Show Material materials with Resistencia a la tracción of 430.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 440.0 MPa Show Material materials with Resistencia a la tracción of 440.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 440.0 MPa Show Material materials with Resistencia a la tracción of 440.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | ||
20.0 °C | 460.0 MPa Show Material materials with Resistencia a la tracción of 460.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 460.0 MPa Show Material materials with Resistencia a la tracción of 460.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | ||
20.0 °C | 470.0 MPa Show Material materials with Resistencia a la tracción of 470.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 470.0 MPa Show Material materials with Resistencia a la tracción of 470.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Plate | ||
20.0 °C | 480.0 MPa Show Material materials with Resistencia a la tracción of 480.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Rod, Plate | Transverse | |
20.0 °C | 480.0 MPa Show Material materials with Resistencia a la tracción of 480.0 MPa | T7351 | WL 3.4364-1, DIN 1725-1 | Rod, Plate |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Calor específico | 795.0 - 1050.0 J/(kg·K) Show Material materials with Calor específico of 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Coeficiente de dilatación térmica | 2.1e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Conductividad térmica | 121.0 - 170.0 W/(m·K) Show Material materials with Conductividad térmica of 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Temperatura de fusión | 465.0 - 655.0 °C Show Material materials with Temperatura de fusión of 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Eléctrico
Property | Value | Comment |
---|---|---|
Conductividad eléctrica | 18000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Resistividad eléctrica | 2.9e-08 - 5.6e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Cobre | 1.2 - 2.0 % Show Material materials with Cobre of 1.2 - 2.0 % | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Cromo | 0.18 - 0.28 % Show Material materials with Cromo of 0.18 - 0.28 % | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Hierro | 0.5 Show Material materials with Hierro of 0.5 | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Magnesio | 2.1 - 2.9 % Show Material materials with Magnesio of 2.1 - 2.9 % | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Manganeso | 0.3 Show Material materials with Manganeso of 0.3 | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Silicona | 0.4 Show Material materials with Silicona of 0.4 | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Titanio | 0.2 Show Material materials with Titanio of 0.2 | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T7351 | WL 3.4364-1, DIN 1725-1 | Plate, Rod |
Technological properties
Property | ||
---|---|---|
Brazing | Excellent |